Viewer

225_6_238261 Dupes Run TOTOPOL

Structure Data

Name

225_6_238261

Type Code

n/a

Spacegroup

225

F m -3 m

Energy (eV/TO₂)

0.06

FD (T/1000 Å³)

15.309

UC volume (Å³)

56435.747

avg. TD₁₀

679

Lattice Parameters

38.358

90.000

Topological Data

CS and VS

CS T1	1 4 11 24 40 58 77 97 122 152 187 226 273 333 403 475
VS T1	4.6.6.8_{2}.6.8_{2}
CS T2	1 4 8 18 31 52 70 91 117 140 171 218 271 321 367 428
VS T2	3.8_{2}.3.8_{2}.6.10_{2}
CS T3	1 4 8 13 25 43 61 85 110 131 161 209 271 328 368 403
VS T3	3.6.3.6.6.10_{2}
CS T4	1 4 7 16 27 42 61 85 111 134 171 217 260 312 367 415
VS T4	3.3.6.8.8.10_{2}
CS T5	1 4 9 16 25 37 54 77 104 137 175 218 261 303 353 416
VS T5	3.6.4.6.8.8
CS T6	1 4 9 17 28 42 59 82 114 151 186 219 258 308 368 429
VS T6	3.6.4.10_{4}.8.8

Topological Spheres data

D_i	D_f	D_sf
n/a	n/a	n/a

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.014

data_225_6_238261_bgbmin.cif
# energy = 0.064796
#FD = 15.31 T-atoms/1000 Angstroms^3

_cell_length_a           38.3576
_cell_length_b           38.3576
_cell_length_c           38.3576
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        90.0000
_symmetry_space_group_name_H-M  'F m -3 m'
_symmetry_Int_Tables_number 225

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.29747 0.14981 0.09725
O O_11_1 0.32689 0.17311 0.07727
O O_11_2 0.31553 0.12953 0.12953
O O_12_1 0.26721 0.17551 0.11249
O O_13_1 0.27944 0.12072 0.07131
Si Si2 0.22556 0.16890 0.11654
O O_22_1 0.20445 0.20445 0.10799
O O_22_2 0.21703 0.15584 0.15584
O O_23_1 0.21451 0.13856 0.08924
Si Si3 0.23995 0.12725 0.05760
O O_34_1 0.24318 0.16060 0.03374
O O_35_1 0.22261 0.09432 0.03475
Si Si4 0.21958 0.16743 0.00000
O O_44_1 0.20704 0.20704 0.00000
O O_45_1 0.18754 0.13955 0.00000
Si Si5 0.19834 0.09907 0.00000
O O_56_1 0.16198 0.07437 0.00000
Si Si6 0.12063 0.05921 0.00000
O O_66_1 0.09206 0.09206 0.00000
O O_66_2 0.11483 0.03483 0.03483

_iza_sc_Energy_eV_TO2 = 0.064796

_iza_sc_FrameworkDensity = 15.309494

_iza_sc_avgTD10 = 677.778

loop_
_iza_sc_CoordinationSequence
1 4 9 17 28 42 59 82 114 151 186 219 258 308 368 429 
1 4 9 16 25 37 54 77 104 137 175 218 261 303 353 416 
1 4 7 16 27 42 61 85 111 134 171 217 260 312 367 415 
1 4 8 13 25 43 61 85 110 131 161 209 271 328 368 403 
1 4 8 18 31 52 70 91 117 140 171 218 271 321 367 428 
1 4 11 24 40 58 77 97 122 152 187 226 273 333 403 475

loop_
_iza_sc_VertexSymbols
3.6.4.10_{4}.8.8
3.6.4.6.8.8
3.3.6.8.8.10_{2}
3.6.3.6.6.10_{2}
3.8_{2}.3.8_{2}.6.10_{2}
4.6.6.8_{2}.6.8_{2}

#MMJT_TO_anneal_parms 47 38.357559297 0.297474978 0.149813453 0.097254710 0.225557205 0.168902706 0.116539999 0.239949311 0.127249328 0.057604017 0.219578432 0.167434321 0.198338011 0.099073618 0.120628069 0.059208241 0.173106855 0.077269945 0.315525008 0.129534458 0.267206538 0.175506830 0.112487067 0.279441837 0.120723148 0.071307588 0.204445143 0.107988794 0.217027612 0.155841021 0.214507673 0.138555192 0.089236481 0.243183440 0.160597203 0.033744553 0.222608863 0.094319755 0.034747303 0.207036221 0.187541276 0.139545535 0.161979241 0.074372525 0.092056080 0.114833361 0.034831955 0.064796440
# Graph Descriptor
# 225
# 6
# 0 0 0 10 10 10 
# 14
# 0 75 0
# 0 89 0
# 0 0 1
# 0 0 2
# 1 76 1
# 1 89 1
# 1 0 2
# 2 0 3
# 2 0 4
# 3 29 3
# 3 0 4
# 4 0 5
# 5 29 5
# 5 37 5