Viewer

194_6_263337070 Dupes Run TOTOPOL

Structure Data

Name

194_6_263337070

Type Code

n/a

Spacegroup

194

P 63/m m c

Energy (eV/TO₂)

0.19

FD (T/1000 Å³)

21.525

UC volume (Å³)

5574.971

avg. TD₁₀

1003

Lattice Parameters

18.529

18.751

90.000

120.000

Topological Data

CS and VS

CS T1	1 4 9 21 40 64 93 129 181 227 278 343 425 486 554 659
VS T1	3.4.8_{2}.8_{2}.8_{3}.12
CS T2	1 4 8 13 23 43 76 119 165 211 256 309 374 442 522 619
VS T2	4.4.4.6.4.8
CS T3	1 4 7 12 24 46 82 131 181 227 275 348 433 483 546 654
VS T3	3.4.4.8.4.8
CS T4	1 4 9 19 36 59 90 125 166 216 271 334 403 472 554 651
VS T4	4.8.4.8_{2}.4.8_{4}
CS T5	1 4 9 18 34 60 98 134 173 227 291 344 403 501 578 633
VS T5	3.4.8.8.8.8
CS T6	1 4 10 22 40 62 91 127 170 223 279 334 406 492 568 634
VS T6	4.8.4.8_{4}.8.8_{2}

Topological Spheres data

D_i	D_f	D_sf
7.06	0.99	0.99

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.017

data_194_6_263337070_bgbmin.cif
# energy = 0.188908
#FD = 21.52 T-atoms/1000 Angstroms^3

_cell_length_a           18.5287
_cell_length_b           18.5287
_cell_length_c           18.7509
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        120.0000
_symmetry_space_group_name_H-M  'P 63/m m c'
_symmetry_Int_Tables_number 194

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.43332 0.40846 0.07983
O O_11_1 0.43353 0.43353 0.00000
O O_11_2 0.52003 0.47997 0.11732
O O_12_1 0.43497 0.32612 0.05654
O O_13_1 0.34468 0.39146 0.12209
Si Si2 0.34209 0.25108 0.04215
O O_22_1 0.28287 0.28287 0.00000
O O_22_2 0.34211 0.17106 0.00372
O O_25_1 0.32323 0.22896 0.12591
Si Si3 0.25070 0.34323 0.16375
O O_33_1 0.26500 0.34174 0.25000
O O_33_2 0.19402 0.38805 0.14977
O O_34_1 0.19493 0.24667 0.13351
Si Si4 0.15597 0.15405 0.17041
O O_44_1 0.19330 0.16796 0.25000
O O_44_2 0.05641 0.11282 0.17551
O O_44_3 0.17429 0.08714 0.12854
Si Si5 0.36880 0.18440 0.16459
O O_55_1 0.35387 0.17694 0.25000
O O_56_1 0.46872 0.23436 0.14389
Si Si6 0.56663 0.28332 0.16521
O O_66_1 0.61904 0.38096 0.13909
O O_66_2 0.56776 0.28388 0.25000

_iza_sc_Energy_eV_TO2 = 0.188908

_iza_sc_FrameworkDensity = 21.524765

_iza_sc_avgTD10 = 1002.100

loop_
_iza_sc_CoordinationSequence
1 4 10 22 40 62 91 127 170 223 279 334 406 492 568 634 
1 4 9 21 40 64 93 129 181 227 278 343 425 486 554 659 
1 4 9 19 36 59 90 125 166 216 271 334 403 472 554 651 
1 4 8 13 23 43 76 119 165 211 256 309 374 442 522 619 
1 4 9 18 34 60 98 134 173 227 291 344 403 501 578 633 
1 4 7 12 24 46 82 131 181 227 275 348 433 483 546 654

loop_
_iza_sc_VertexSymbols
4.8.4.8_{4}.8.8_{2}
3.4.8_{2}.8_{2}.8_{3}.12
4.8.4.8_{2}.4.8_{4}
4.4.4.6.4.8
3.4.8.8.8.8
3.4.4.8.4.8

#MMJT_TO_anneal_parms 52 18.528728135 18.750850769 0.433318867 0.408456583 0.079833447 0.342087221 0.251081154 0.042152235 0.250703578 0.343233720 0.163752707 0.155966144 0.154052382 0.170409908 0.184398511 0.164585597 0.283316711 0.165209039 0.433525629 0.479974618 0.117315536 0.434968318 0.326116824 0.056540529 0.344680400 0.391456364 0.122088657 0.282866433 0.171056537 0.003719475 0.323228753 0.228959235 0.125912035 0.264998927 0.341744389 0.388047826 0.149766429 0.194931859 0.246672134 0.133508490 0.193299791 0.167961643 0.112817233 0.175509617 0.087144318 0.128543089 0.176935618 0.234359570 0.143894917 0.380957851 0.139087583 0.283881597 0.188907972
# Graph Descriptor
# 194
# 6
# 0 0 0 0 16 16 
# 17
# 0 7 0
# 0 34 0
# 0 0 1
# 0 0 2
# 1 7 1
# 1 37 1
# 1 0 4
# 2 26 2
# 2 35 2
# 2 0 3
# 3 26 3
# 3 35 3
# 3 37 3
# 4 18 4
# 4 0 5
# 5 2 5
# 5 18 5