Viewer

194_6_145611513 Dupes Run TOTOPOL

Structure Data

Name

194_6_145611513

Type Code

n/a

Spacegroup

194

P 63/m m c

Energy (eV/TO₂)

0.00

FD (T/1000 Å³)

15.339

UC volume (Å³)

9387.811

avg. TD₁₀

695

Lattice Parameters

17.212

36.589

90.000

120.000

Topological Data

CS and VS

CS T1	1 4 9 16 26 43 69 100 130 155 177 201 233 279 340 411
VS T1	4.4.4.6.6.12
CS T2	1 4 10 19 31 47 64 83 109 141 177 217 262 309 352 392
VS T2	4.4.6.6.6.12_{2}
CS T3	1 4 9 16 26 41 61 86 118 153 184 211 244 294 357 421
VS T3	4.4.4.6.6.8
CS T4	1 4 9 18 30 43 62 86 111 142 181 223 263 302 346 399
VS T4	4.4.4.6_{2}.8.10
CS T5	1 4 9 17 28 42 63 90 116 143 175 213 255 297 344 397
VS T5	4.4.4.8.6.6
CS T6	1 4 10 19 31 47 65 84 105 134 176 226 275 314 346 384
VS T6	4.4.6.6.6.6

Topological Spheres data

D_i	D_f	D_sf
11.60	7.32	1.71

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.017

data_194_6_145611513_bgbmin.cif
# energy = 0.002094
#FD = 15.34 T-atoms/1000 Angstroms^3

_cell_length_a           17.2125
_cell_length_b           17.2125
_cell_length_c           36.5886
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        120.0000
_symmetry_space_group_name_H-M  'P 63/m m c'
_symmetry_Int_Tables_number 194

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.17853 0.17977 0.20809
O O_11_1 0.20687 0.21159 0.25000
O O_11_2 0.07271 0.14541 0.20257
O O_11_3 0.19777 0.09889 0.19867
O O_12_1 0.23733 0.26394 0.18105
Si Si2 0.23572 0.29420 0.13920
O O_22_1 0.16490 0.32980 0.13561
O O_23_1 0.33482 0.37388 0.12777
O O_24_1 0.20576 0.20891 0.11250
Si Si3 0.39498 0.42616 0.09235
O O_33_1 0.48756 0.51244 0.10589
O O_35_1 0.41803 0.35942 0.06936
O O_36_1 0.34025 0.45934 0.06673
Si Si4 0.17706 0.17703 0.07068
O O_44_1 0.09867 0.19733 0.05839
O O_44_2 0.14087 0.07043 0.06731
O O_45_1 0.26249 0.23134 0.04423
Si Si5 0.36966 0.27197 0.04312
O O_55_1 0.39322 0.19661 0.05703
O O_56_1 0.40396 0.30003 0.00151
Si Si6 0.33355 0.48941 0.02541
O O_66_1 0.43133 0.56867 0.01229
O O_66_2 0.26271 0.52541 0.02414

_iza_sc_Energy_eV_TO2 = 0.002094

_iza_sc_FrameworkDensity = 15.339007

_iza_sc_avgTD10 = 694.333

loop_
_iza_sc_CoordinationSequence
1 4 9 16 26 43 69 100 130 155 177 201 233 279 340 411 
1 4 9 17 28 42 63 90 116 143 175 213 255 297 344 397 
1 4 10 19 31 47 64 83 109 141 177 217 262 309 352 392 
1 4 9 16 26 41 61 86 118 153 184 211 244 294 357 421 
1 4 9 18 30 43 62 86 111 142 181 223 263 302 346 399 
1 4 10 19 31 47 65 84 105 134 176 226 275 314 346 384

loop_
_iza_sc_VertexSymbols
4.4.4.6.6.12
4.4.4.8.6.6
4.4.6.6.6.12_{2}
4.4.4.6.6.8
4.4.4.6_{2}.8.10
4.4.6.6.6.6

#MMJT_TO_anneal_parms 61 17.212510857 36.588630176 0.178532224 0.179770552 0.208094061 0.235721742 0.294195242 0.139202454 0.394978239 0.426159903 0.092346108 0.177058179 0.177027333 0.070676139 0.369658388 0.271965882 0.043124737 0.333546291 0.489406590 0.025408257 0.206873290 0.211588899 0.145413397 0.202573955 0.098886629 0.198671500 0.237333168 0.263941147 0.181052514 0.329800158 0.135613961 0.334823452 0.373882000 0.127769132 0.205755209 0.208908744 0.112495822 0.512441780 0.105892235 0.418029414 0.359424272 0.069360648 0.340245351 0.459339206 0.066729625 0.197333476 0.058392975 0.070434241 0.067306155 0.262494634 0.231344311 0.044225849 0.196608577 0.057026303 0.403957804 0.300033631 0.001513463 0.568665758 0.012290399 0.525410839 0.024135437 0.002094017
# Graph Descriptor
# 194
# 6
# 0 0 0 0 0 0 
# 17
# 0 26 0
# 0 35 0
# 0 37 0
# 0 0 1
# 1 35 1
# 1 0 2
# 1 0 3
# 2 34 2
# 2 0 4
# 2 0 5
# 3 35 3
# 3 37 3
# 3 0 4
# 4 37 4
# 4 7 5
# 5 34 5
# 5 35 5