Viewer

194_6_100564779 Dupes Run TOTOPOL

Structure Data

Name

194_6_100564779

Type Code

n/a

Spacegroup

194

P 63/m m c

Energy (eV/TO₂)

0.25

FD (T/1000 Å³)

19.380

UC volume (Å³)

7430.384

avg. TD₁₀

735

Lattice Parameters

24.549

14.237

90.000

120.000

Topological Data

CS and VS

CS T1	1 4 10 19 30 45 65 93 126 154 191 241 285 334 398 455
VS T1	4.5.4.8.6.8
CS T2	1 4 9 17 30 47 67 95 127 153 187 234 273 318 385 450
VS T2	4.4.4.5.12.16_{5}
CS T3	1 4 9 16 26 42 63 85 113 151 188 223 268 317 368 433
VS T3	4.5.4.6.4.12
CS T4	1 4 9 17 30 48 69 92 119 154 199 251 302 353 408 470
VS T4	4.4.4.8.6.8
CS T5	1 4 9 18 32 48 66 90 121 157 198 243 291 348 410 464
VS T5	4.4.4.8.6.8
CS T6	1 4 10 19 29 44 68 94 121 158 196 230 280 335 382 453
VS T6	4.5.4.16_{6}.5.8

Topological Spheres data

D_i	D_f	D_sf
9.10	3.44	1.42

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.017

data_194_6_100564779_bgbmin.cif
# energy = 0.254481
#FD = 19.38 T-atoms/1000 Angstroms^3

_cell_length_a           24.5485
_cell_length_b           24.5485
_cell_length_c           14.2374
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        120.0000
_symmetry_space_group_name_H-M  'P 63/m m c'
_symmetry_Int_Tables_number 194

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.47439 0.40940 0.04502
O O_11_1 0.44952 0.44952 0.00000
O O_11_2 0.53720 0.46280 0.10684
O O_12_1 0.40198 0.35281 0.09597
O O_13_1 0.49932 0.38995 -0.04818
Si Si2 0.32614 0.33764 0.13594
O O_22_1 0.32722 0.33654 0.25000
O O_24_1 0.30745 0.38891 0.10244
O O_25_1 0.25884 0.27425 0.09794
Si Si3 0.37269 0.51981 0.14835
O O_33_1 0.38897 0.49685 0.25000
O O_33_2 0.40480 0.59520 0.14984
O O_34_1 0.29982 0.49124 0.14217
Si Si4 0.26305 0.41622 0.14270
O O_44_1 0.25101 0.39680 0.25000
O O_44_2 0.19591 0.39181 0.08925
Si Si5 0.18526 0.25157 0.14490
O O_55_1 0.19543 0.27783 0.25000
O O_55_2 0.13406 0.26812 0.09216
O O_56_1 0.15063 0.17874 0.15768
Si Si6 0.11450 0.11384 0.11015
O O_66_1 0.12512 0.12512 0.00000
O O_66_2 0.04023 0.08046 0.13375
O O_66_3 0.14313 0.07156 0.14636

_iza_sc_Energy_eV_TO2 = 0.254481

_iza_sc_FrameworkDensity = 19.379855

_iza_sc_avgTD10 = 733.833

loop_
_iza_sc_CoordinationSequence
1 4 10 19 29 44 68 94 121 158 196 230 280 335 382 453 
1 4 10 19 30 45 65 93 126 154 191 241 285 334 398 455 
1 4 9 17 30 47 67 95 127 153 187 234 273 318 385 450 
1 4 9 16 26 42 63 85 113 151 188 223 268 317 368 433 
1 4 9 18 32 48 66 90 121 157 198 243 291 348 410 464 
1 4 9 17 30 48 69 92 119 154 199 251 302 353 408 470

loop_
_iza_sc_VertexSymbols
4.5.4.16_{6}.5.8
4.5.4.8.6.8
4.4.4.5.12.16_{5}
4.5.4.6.4.12
4.4.4.8.6.8
4.4.4.8.6.8

#MMJT_TO_anneal_parms 60 24.548541247 14.237375750 0.474390230 0.409395962 0.045020029 0.326136796 0.337637350 0.135939555 0.372694638 0.519807086 0.148345522 0.263047681 0.416220414 0.142701388 0.185255699 0.251574355 0.144897055 0.114500349 0.113838240 0.110151496 0.449521903 0.462795954 0.106839792 0.401977077 0.352809974 0.095974110 0.499323514 0.389951093 -0.048176270 0.327220559 0.336540914 0.307451281 0.388912569 0.102441212 0.258837501 0.274249723 0.097935531 0.388973418 0.496848367 0.595195887 0.149836356 0.299823120 0.491239822 0.142165221 0.251007296 0.396803520 0.391814887 0.089253264 0.195426396 0.277826938 0.268122425 0.092159303 0.150625222 0.178735711 0.157681115 0.125116516 0.080462678 0.133753091 0.071563419 0.146362197 0.254480623
# Graph Descriptor
# 194
# 6
# 0 0 0 0 0 0 
# 18
# 0 7 0
# 0 34 0
# 0 0 1
# 0 7 2
# 1 26 1
# 1 0 3
# 1 0 4
# 2 26 2
# 2 34 2
# 2 0 3
# 3 26 3
# 3 35 3
# 4 26 4
# 4 35 4
# 4 0 5
# 5 7 5
# 5 35 5
# 5 37 5