Viewer

194_6_100067495 Dupes Run TOTOPOL

Structure Data

Name

194_6_100067495

Type Code

n/a

Spacegroup

194

P 63/m m c

Energy (eV/TO₂)

0.27

FD (T/1000 Å³)

21.011

UC volume (Å³)

6853.460

avg. TD₁₀

904

Lattice Parameters

23.358

14.504

90.000

120.000

Topological Data

CS and VS

CS T1	1 4 10 21 38 61 88 121 164 210 254 304 366 434 504 580
VS T1	4.5.4.8_{2}.12.12
CS T2	1 4 9 17 30 52 80 109 143 184 234 293 357 426 499 573
VS T2	4.4.4.12_{2}.6.8
CS T3	1 4 9 17 31 51 78 111 145 190 245 295 351 421 493 568
VS T3	4.5.4.8.4.12
CS T4	1 4 9 16 28 50 78 107 144 191 242 296 353 414 482 560
VS T4	4.4.4.5.12.12
CS T5	1 4 9 17 30 49 76 110 147 189 238 293 351 411 475 547
VS T5	4.4.4.5.8.12
CS T6	1 4 10 21 36 57 87 121 159 206 257 309 363 422 493 576
VS T6	4.5.4.8_{2}.8.8

Topological Spheres data

D_i	D_f	D_sf
8.78	3.52	2.06

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.017

data_194_6_100067495_bgbmin.cif
# energy = 0.266027
#FD = 21.01 T-atoms/1000 Angstroms^3

_cell_length_a           23.3583
_cell_length_b           23.3583
_cell_length_c           14.5043
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        120.0000
_symmetry_space_group_name_H-M  'P 63/m m c'
_symmetry_Int_Tables_number 194

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.40107 0.46856 0.03752
O O_11_1 0.40792 0.40792 0.00000
O O_11_2 0.47048 0.52952 0.08314
O O_12_1 0.33134 0.43899 0.10259
O O_13_1 0.39293 0.49299 -0.06027
Si Si2 0.25601 0.37671 0.13865
O O_22_1 0.25983 0.36198 0.25000
O O_22_2 0.19918 0.39836 0.12642
O O_24_1 0.23334 0.30943 0.07460
Si Si3 0.51132 0.37964 0.15961
O O_33_1 0.48606 0.40352 0.25000
O O_33_2 0.59059 0.40941 0.16108
O O_35_1 0.47336 0.30548 0.16037
Si Si4 0.28822 0.21213 0.03507
O O_44_1 0.28624 0.14312 0.04621
O O_45_1 0.35045 0.27453 0.09083
O O_46_1 0.21154 0.19002 0.08406
Si Si5 0.39673 0.25647 0.15105
O O_55_1 0.36250 0.23506 0.25000
O O_55_2 0.40108 0.20054 0.09809
Si Si6 0.13075 0.12937 0.10196
O O_66_1 0.10690 0.10690 0.00000
O O_66_2 0.07511 0.15022 0.14107
O O_66_3 0.12643 0.06322 0.15160

_iza_sc_Energy_eV_TO2 = 0.266027

_iza_sc_FrameworkDensity = 21.011404

_iza_sc_avgTD10 = 902.667

loop_
_iza_sc_CoordinationSequence
1 4 10 21 36 57 87 121 159 206 257 309 363 422 493 576 
1 4 10 21 38 61 88 121 164 210 254 304 366 434 504 580 
1 4 9 17 30 49 76 110 147 189 238 293 351 411 475 547 
1 4 9 17 31 51 78 111 145 190 245 295 351 421 493 568 
1 4 9 16 28 50 78 107 144 191 242 296 353 414 482 560 
1 4 9 17 30 52 80 109 143 184 234 293 357 426 499 573

loop_
_iza_sc_VertexSymbols
4.5.4.8_{2}.8.8
4.5.4.8_{2}.12.12
4.4.4.5.8.12
4.5.4.8.4.12
4.4.4.5.12.12
4.4.4.12_{2}.6.8

#MMJT_TO_anneal_parms 60 23.358263350 14.504263826 0.401065625 0.468564397 0.037520507 0.256010213 0.376712242 0.138648362 0.511323861 0.379637115 0.159610197 0.288222222 0.212128167 0.035068414 0.396732246 0.256471110 0.151052897 0.130752713 0.129369189 0.101961525 0.407921169 0.529515204 0.083141144 0.331340917 0.438992710 0.102588128 0.392933058 0.492985002 -0.060267543 0.259833179 0.361983438 0.398362421 0.126415435 0.233335743 0.309434099 0.074604236 0.486056692 0.403523749 0.409413224 0.161080708 0.473362338 0.305483517 0.160367477 0.143122378 0.046211665 0.350452712 0.274527086 0.090827687 0.211542698 0.190023157 0.084061733 0.362499819 0.235062872 0.200539537 0.098091153 0.106896648 0.150222520 0.141068854 0.063217156 0.151596407 0.266026530
# Graph Descriptor
# 194
# 6
# 0 0 0 0 0 0 
# 18
# 0 7 0
# 0 34 0
# 0 0 1
# 0 7 2
# 1 26 1
# 1 35 1
# 1 7 3
# 2 26 2
# 2 34 2
# 2 0 4
# 3 37 3
# 3 0 4
# 3 0 5
# 4 26 4
# 4 37 4
# 5 7 5
# 5 35 5
# 5 37 5