166_5_22603716 Dupes Run TOTOPOL

Structure Data

Name

166_5_22603716

Type Code

n/a

Spacegroup

166

R -3 m

Energy (eV/TO₂)

0.26

FD (T/1000 Å³)

24.367

UC volume (Å³)

7386.953

avg. TD₁₀

953

Lattice Parameters

25.317

13.307

90.000

120.000

Topological Data

CS and VS

CS T1	1 4 10 21 39 67 100 133 176 232 289 345 409 494 604 704
VS T1	4.6.4.6.6.12_{6}
CS T2	1 4 9 17 30 52 79 110 151 194 242 304 373 452 542 629
VS T2	4.4.4.6.6_{2}.12_{7}
CS T3	1 4 8 12 19 36 65 99 134 176 228 284 341 408 495 595
VS T3	4.4.4.6.4.6_{2}
CS T4	1 4 9 17 31 56 93 136 178 219 273 347 425 490 552 645
VS T4	4.4.4.10.6.6
CS T5	1 4 11 23 39 60 85 122 166 214 275 341 405 471 547 640
VS T5	4.6_{2}.6.6.10.12_{12}

Topological Spheres data

D_i	D_f	D_sf
4.55	1.11	1.03

JAVA version HTML5 version (default)

CIF file

# This CIF file was created by TO_anneal version 1.014

data_166_5_22603716_bgbmin.cif
# energy = 0.260460
#FD = 24.37 T-atoms/1000 Angstroms^3

_cell_length_a           25.3174
_cell_length_b           25.3174
_cell_length_c           13.3075
_cell_angle_alpha        90.0000
_cell_angle_beta         90.0000
_cell_angle_gamma        120.0000
_symmetry_space_group_name_H-M  'R -3 m'
_symmetry_Int_Tables_number 166

loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si Si1 0.28172 0.31600 0.10869
O O_11_1 0.30269 0.30269 0.00000
O O_11_2 0.33333 0.31237 0.16667
O O_12_1 0.21970 0.26576 0.14747
O O_13_1 0.27669 0.37660 0.13920
Si Si2 0.16716 0.21816 0.08578
O O_22_1 0.19876 0.19876 0.00000
O O_22_2 0.12012 0.24024 0.04485
O O_24_1 0.13515 0.16635 0.16301
Si Si3 0.40753 0.46519 0.07924
O O_33_1 0.42123 0.42123 0.00000
O O_33_2 0.47178 0.52822 0.09178
O O_35_1 0.35443 0.48637 0.03607
Si Si4 0.10212 0.10090 0.12182
O O_44_1 0.09985 0.09985 0.00000
O O_44_2 0.03441 0.06883 0.16684
O O_44_3 0.13883 0.06941 0.16300
Si Si5 0.33456 0.54364 0.04826
O O_55_1 0.33333 0.55431 0.16667
O O_55_2 0.39081 0.60919 0.00387
O O_55_3 0.26429 0.52858 0.00877

_iza_sc_Energy_eV_TO2 = 0.260460

_iza_sc_FrameworkDensity = 24.367151

_iza_sc_avgTD10 = 952.000

loop_
_iza_sc_CoordinationSequence
1 4 11 23 39 60 85 122 166 214 275 341 405 471 547 640 
1 4 9 17 30 52 79 110 151 194 242 304 373 452 542 629 
1 4 10 21 39 67 100 133 176 232 289 345 409 494 604 704 
1 4 8 12 19 36 65 99 134 176 228 284 341 408 495 595 
1 4 9 17 31 56 93 136 178 219 273 347 425 490 552 645

loop_
_iza_sc_VertexSymbols
4.6_{2}.6.6.10.12_{12}
4.4.4.6.6_{2}.12_{7}
4.6.4.6.6.12_{6}
4.4.4.6.4.6_{2}
4.4.4.10.6.6

#MMJT_TO_anneal_parms 47 25.317427494 13.307545646 0.281721623 0.315996043 0.108690040 0.167155444 0.218161795 0.085783231 0.407526098 0.465194107 0.079241102 0.102124363 0.100899453 0.121815529 0.334558611 0.543642165 0.048263790 0.302694724 0.312367629 0.219698169 0.265764261 0.147466262 0.276694779 0.376595640 0.139203397 0.198760370 0.240238336 0.044849641 0.135145352 0.166349132 0.163011629 0.421229340 0.528215405 0.091775017 0.354431525 0.486370705 0.036068044 0.099845593 0.068828448 0.166837530 0.069414174 0.162995877 0.554305565 0.609193073 0.003873012 0.528577101 0.008769818 0.260459726
# Graph Descriptor
# 166
# 5
# 0 0 0 0 0 
# 16
# 0 7 0
# 0 20 0
# 0 0 1
# 0 20 2
# 1 7 1
# 1 35 1
# 1 0 3
# 2 7 2
# 2 34 2
# 2 0 4
# 3 7 3
# 3 35 3
# 3 37 3
# 4 20 4
# 4 34 4
# 4 35 4