Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_9_2_406_SOrzS0.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 18.47 T-atoms per nm^3
Material density = 1.843 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6267 Angstrom
T1  -- O2  = 1.6151 Angstrom
T1  -- O1  = 1.6277 Angstrom
T1  -- O3  = 1.6094 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.010237  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010052  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6106 Angstrom
T2  -- O2  = 1.6160 Angstrom
T2  -- O4  = 1.6120 Angstrom
T2  -- O4  = 1.6013 Angstrom
      mean = 1.6100 Angstrom
        t1 = 0.004346  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002879  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6013 A <--> 1.6277 A
          Mean   = 1.6149 A
          StdDev = 0.0084 A

       t1 Range  = 0.0043 <-- 0.0073 --> 0.0102
       t2 Range  = 0.0029 <-- 0.0065 --> 0.0101

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.178 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 110.921 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 109.832 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 109.905 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 107.957 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 108.995 deg; O1  -- O3  = 3 A
       107.957 deg <-- 109.465 deg --> 110.921 deg

O3  -- T2  -- O2  = 108.836 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 109.549 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 111.267 deg; O3  -- O4  = 3 A
O2  -- T2  -- O4  = 108.676 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.568 deg; O2  -- O4  = 3 A
O4  -- T2  -- O4  = 108.905 deg; O4  -- O4  = 3 A
       108.676 deg <-- 109.467 deg --> 111.267 deg

        O-T-O SUMMARY
          Range  = 107.9573 deg <--> 111.2666 deg
          Mean   = 109.4657 deg
          StdDev = 0.9049 deg

        O--O SUMMARY
          Range  = 2.6080 A <--> 2.6808 A
          Mean   = 2.6369 A
          StdDev = 0.0194 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 121.760 deg; T1  -- T2  = 5.4605 A
T1  - O1  - T1  - O1  - T1  = 117.013 deg; T1  -- T1  = 5.2208 A
T1  - O1  - T1  - O3  - T2  =  90.653 deg; T1  -- T2  = 4.4514 A
T2  - O2  - T1  - O1  - T1  = 113.652 deg; T2  -- T1  = 5.2319 A
T2  - O2  - T1  - O3  - T2  = 116.378 deg; T2  -- T2  = 5.4265 A
T1  - O1  - T1  - O3  - T2  =  89.992 deg; T1  -- T2  = 4.4260 A

T1  - O3  - T2  - O2  - T2  =  89.994 deg; T1  -- T2  = 4.4514 A
T1  - O3  - T2  - O4  - T1  = 117.609 deg; T1  -- T1  = 5.4624 A
T1  - O3  - T2  - O4  - T2  =  89.341 deg; T1  -- T2  = 4.4260 A
T2  - O2  - T2  - O4  - T1  = 122.677 deg; T2  -- T1  = 5.5166 A
T2  - O2  - T2  - O4  - T2  = 114.839 deg; T2  -- T2  = 5.2208 A
T1  - O4  - T2  - O4  - T2  = 114.595 deg; T1  -- T2  = 5.2904 A

        T-T-T SUMMARY
          Range  = 89.3410 deg <--> 122.6770 deg
          Mean   = 108.2086 deg
          StdDev = 13.2658 deg

        T--T SUMMARY
          Range  = 4.4260 A <--> 5.5166 A
          Mean   = 5.0487 A
          StdDev = 0.4465 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.330 deg ; T1  -- T1   3.0613 A

T1  -- O2  -- T2  = 163.297 deg ; T1  -- T2   3.1969 A

T1  -- O3  -- T2  = 164.042 deg ; T1  -- T2   3.1888 A

T2  -- O4  -- T2  = 149.203 deg ; T2  -- T2   3.0979 A


        T-O-T SUMMARY
          Range  = 140.3296° <--> 164.0422 deg
          Mean   = 154.2179 deg
          StdDev = 10.2889 deg

        T--T SUMMARY
          Range  = 3.0613 A <--> 3.1969 A
          Mean   = 3.1362 A
          StdDev = 0.0601 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 413 461 490
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 411 459 491
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000