Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_649238_6qz1n5.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 26.73 T-atoms per nm^3
Material density = 2.667 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6394 Angstrom
T1  -- O2  = 1.6521 Angstrom
T1  -- O2  = 1.6521 Angstrom
T1  -- O1  = 1.6394 Angstrom
      mean = 1.6457 Angstrom
        t1 = 0.054299  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035529  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6174 Angstrom
T2  -- O2  = 1.6174 Angstrom
T2  -- O2  = 1.6174 Angstrom
T2  -- O2  = 1.6174 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.098229  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.073263  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6174 A <--> 1.6521 A
          Mean   = 1.6363 A
          StdDev = 0.0145 A

       t1 Range  = 0.0543 <-- 0.0763 --> 0.0982
       t2 Range  = 0.0355 <-- 0.0544 --> 0.0733

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 116.100 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 113.814 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  =  97.276 deg; O1  -- O1  = 2 A
O2  -- T1  -- O2  = 100.658 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 113.814 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 116.100 deg; O2  -- O1  = 3 A
       97.276 deg <-- 109.627 deg --> 116.100 deg

O2  -- T2  -- O2  =  97.144 deg; O2  -- O2  = 2 A
O2  -- T2  -- O2  =  99.409 deg; O2  -- O2  = 2 A
O2  -- T2  -- O2  = 135.410 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 135.410 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  =  99.409 deg; O2  -- O2  = 2 A
O2  -- T2  -- O2  =  97.144 deg; O2  -- O2  = 2 A
       97.144 deg <-- 110.655 deg --> 135.410 deg

        O-T-O SUMMARY
          Range  = 97.1438 deg <--> 135.4104 deg
          Mean   = 110.7000 deg
          StdDev = 13.5900 deg

        O--O SUMMARY
          Range  = 2.4254 A <--> 2.9929 A
          Mean   = 2.6648 A
          StdDev = 0.2077 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.745 deg; T1  -- T2  = 4.4095 A
T1  - O1  - T1  - O2  - T1  =  97.276 deg; T1  -- T1  = 4.9217 A
T1  - O1  - T1  - O1  - T2  = 128.233 deg; T1  -- T2  = 5.6174 A
T2  - O2  - T1  - O2  - T1  = 128.233 deg; T2  -- T1  = 5.6174 A
T2  - O2  - T1  - O1  - T2  = 124.594 deg; T2  -- T2  = 5.2469 A
T1  - O2  - T1  - O1  - T2  =  89.745 deg; T1  -- T2  = 4.4095 A

T1  - O2  - T2  - O2  - T1  = 103.024 deg; T1  -- T1  = 4.6387 A
T1  - O2  - T2  - O2  - T1  =  77.121 deg; T1  -- T1  = 3.6941 A
T1  - O2  - T2  - O2  - T1  = 175.976 deg; T1  -- T1  = 5.9226 A
T1  - O2  - T2  - O2  - T1  = 175.976 deg; T1  -- T1  = 5.9226 A
T1  - O2  - T2  - O2  - T1  =  77.121 deg; T1  -- T1  = 3.6941 A
T1  - O2  - T2  - O2  - T1  = 103.024 deg; T1  -- T1  = 4.6387 A

        T-T-T SUMMARY
          Range  = 77.1205 deg <--> 175.9764 deg
          Mean   = 113.5610 deg
          StdDev = 33.0768 deg

        T--T SUMMARY
          Range  = 3.6941 A <--> 5.9226 A
          Mean   = 4.8630 A
          StdDev = 0.7536 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2787 A

T1  -- O2  -- T2  = 129.996 deg ; T1  -- T2   2.9631 A


        T-O-T SUMMARY
          Range  = 129.9958° <--> 180.0000 deg
          Mean   = 154.9979 deg
          StdDev = 25.8221 deg

        T--T SUMMARY
          Range  = 2.9631 A <--> 3.2787 A
          Mean   = 3.1209 A
          StdDev = 0.1630 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 30 54 92 130 178 238 300 374 450 536 628 734 830 966
TD10 = 1413
Circuit symbol = 6.6.6.6.6.6
Weight = 21
Vertex symbol  = 6.6.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 30 56 86 134 176 236 310 368 454 538 628 734 846 946
TD10 = 1413
Circuit symbol = 6.6.6_{2}.6_{2}.7_{2}.7_{2}
Weight = 27
Vertex symbol  = 6.6.6_{2}.6_{2}.7_{2}.7_{2}
Weight = 27

<TD10> = 1413.000
Average ring size = 6.1600