Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_632205_lc588X.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 16.72 T-atoms per nm^3
Material density = 1.668 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6220 Angstrom
T1  -- O3  = 1.5636 Angstrom
T1  -- O4  = 1.6290 Angstrom
T1  -- O1  = 1.6340 Angstrom
      mean = 1.6122 Angstrom
        t1 = 0.042402  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030084  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6312 Angstrom
T2  -- O5  = 1.6512 Angstrom
T2  -- O4  = 1.6312 Angstrom
T2  -- O5  = 1.6512 Angstrom
      mean = 1.6412 Angstrom
        t1 = 0.175108  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.187761  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5636 A <--> 1.6512 A
          Mean   = 1.6218 A
          StdDev = 0.0276 A

       t1 Range  = 0.0424 <-- 0.1088 --> 0.1751
       t2 Range  = 0.0301 <-- 0.1089 --> 0.1878

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 100.313 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 111.297 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  = 116.670 deg; O2  -- O1  = 3 A
O3  -- T1  -- O4  = 109.762 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  = 104.710 deg; O3  -- O1  = 3 A
O4  -- T1  -- O1  = 112.914 deg; O4  -- O1  = 3 A
       100.313 deg <-- 109.278 deg --> 116.670 deg

O4  -- T2  -- O5  =  82.009 deg; O4  -- O5  = 2 A
O4  -- T2  -- O4  = 136.071 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  =  80.771 deg; O4  -- O5  = 2 A
O5  -- T2  -- O4  =  80.771 deg; O5  -- O4  = 2 A
O5  -- T2  -- O5  = 132.814 deg; O5  -- O5  = 3 A
O4  -- T2  -- O5  =  82.009 deg; O4  -- O5  = 2 A
       80.771 deg <-- 99.074 deg --> 136.071 deg

        O-T-O SUMMARY
          Range  = 80.7708 deg <--> 136.0706 deg
          Mean   = 102.2855 deg
          StdDev = 19.3319 deg

        O--O SUMMARY
          Range  = 2.1268 A <--> 3.0263 A
          Mean   = 2.4990 A
          StdDev = 0.3276 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  77.847 deg; T1  -- T2  = 3.6990 A
T1  - O2  - T1  - O4  - T1  = 148.452 deg; T1  -- T1  = 5.8003 A
T1  - O2  - T1  - O1  - T1  = 101.306 deg; T1  -- T1  = 4.4366 A
T2  - O3  - T1  - O4  - T1  = 128.355 deg; T2  -- T1  = 5.7440 A
T2  - O3  - T1  - O1  - T1  = 110.024 deg; T2  -- T1  = 4.9896 A
T1  - O4  - T1  - O1  - T1  =  86.588 deg; T1  -- T1  = 4.2870 A

T1  - O4  - T2  - O5  - T2  =  70.636 deg; T1  -- T2  = 3.6990 A
T1  - O4  - T2  - O4  - T1  = 125.039 deg; T1  -- T1  = 5.5237 A
T1  - O4  - T2  - O5  - T2  =  91.976 deg; T1  -- T2  = 4.6000 A
T2  - O5  - T2  - O4  - T1  =  91.976 deg; T2  -- T1  = 4.6000 A
T2  - O5  - T2  - O5  - T2  = 142.443 deg; T2  -- T2  = 6.2125 A
T1  - O4  - T2  - O5  - T2  =  70.636 deg; T1  -- T2  = 3.6990 A

        T-T-T SUMMARY
          Range  = 70.6361 deg <--> 148.4518 deg
          Mean   = 102.9467 deg
          StdDev = 26.3923 deg

        T--T SUMMARY
          Range  = 3.6990 A <--> 6.2125 A
          Mean   = 4.7622 A
          StdDev = 0.8306 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.484 deg ; T1  -- T1   3.2677 A

T1  -- O2  -- T1  = 116.452 deg ; T1  -- T1   2.7579 A

T1  -- O3  -- T1  = 144.261 deg ; T1  -- T1   2.9764 A

T1  -- O4  -- T2  = 145.439 deg ; T1  -- T2   3.1131 A

T2  -- O5  -- T2  = 166.939 deg ; T2  -- T2   3.2809 A


        T-O-T SUMMARY
          Range  = 116.4523° <--> 178.4840 deg
          Mean   = 148.4681 deg
          StdDev = 21.8751 deg

        T--T SUMMARY
          Range  = 2.7579 A <--> 3.2809 A
          Mean   = 3.0568 A
          StdDev = 0.1949 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O5  = 2.1537 A
O4  -- O5  = 2.1268 A
T1  -- T1  = 2.7579 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 18 32 59 88 114 157 203 234 293 363 424 456 552 653
TD10 = 920
Circuit symbol = 4.4.5_{2}.7_{2}.5_{2}.7_{2}
Weight = 9
Vertex symbol  = 4.4.5_{2}.10.5_{2}.12_{8}
Weight = 35

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 16 32 56 84 114 154 194 238 302 346 402 484 560 616
TD10 = 903
Circuit symbol = 4.4.5.5.5.5
Weight = 7
Vertex symbol  = 4.4.5.5.5.5
Weight = 7

<TD10> = 914.333
Average ring size = 6.6258