Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_628944_umHNd_.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 14.52 T-atoms per nm^3
Material density = 1.448 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6257 Angstrom
T1  -- O2  = 1.7070 Angstrom
T1  -- O3  = 1.6484 Angstrom
T1  -- O4  = 1.6062 Angstrom
      mean = 1.6468 Angstrom
        t1 = 0.104473  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076313  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6134 Angstrom
T2  -- O4  = 1.5980 Angstrom
T2  -- O3  = 1.6134 Angstrom
T2  -- O4  = 1.5980 Angstrom
      mean = 1.6057 Angstrom
        t1 = 0.052526  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060250  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5980 A <--> 1.7070 A
          Mean   = 1.6331 A
          StdDev = 0.0369 A

       t1 Range  = 0.0525 <-- 0.0785 --> 0.1045
       t2 Range  = 0.0602 <-- 0.0683 --> 0.0763

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 140.113 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  98.502 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  =  88.966 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 114.530 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 103.626 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 103.316 deg; O3  -- O4  = 3 A
       88.966 deg <-- 108.176 deg --> 140.113 deg

O3  -- T2  -- O4  =  99.292 deg; O3  -- O4  = 2 A
O3  -- T2  -- O3  = 122.285 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 110.006 deg; O3  -- O4  = 3 A
O4  -- T2  -- O3  = 110.006 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 117.106 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  =  99.292 deg; O3  -- O4  = 2 A
       99.292 deg <-- 109.665 deg --> 122.285 deg

        O-T-O SUMMARY
          Range  = 88.9664 deg <--> 140.1131 deg
          Mean   = 107.5639 deg
          StdDev = 11.4380 deg

        O--O SUMMARY
          Range  = 2.2646 A <--> 3.1329 A
          Mean   = 2.6087 A
          StdDev = 0.1951 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 147.086 deg; T1  -- T1  = 5.4680 A
T1  - O1  - T1  - O3  - T2  =  64.876 deg; T1  -- T2  = 3.0117 A
T1  - O1  - T1  - O4  - T2  =  61.643 deg; T1  -- T2  = 2.9273 A
T1  - O2  - T1  - O3  - T2  = 139.134 deg; T1  -- T2  = 5.5800 A
T1  - O2  - T1  - O4  - T2  =  90.576 deg; T1  -- T2  = 4.2916 A
T2  - O3  - T1  - O4  - T2  =  93.107 deg; T2  -- T2  = 4.3122 A

T1  - O3  - T2  - O4  - T1  =  53.480 deg; T1  -- T1  = 2.6733 A
T1  - O3  - T2  - O3  - T1  = 135.619 deg; T1  -- T1  = 5.4992 A
T1  - O3  - T2  - O4  - T1  = 161.381 deg; T1  -- T1  = 5.7774 A
T1  - O4  - T2  - O3  - T1  = 136.610 deg; T1  -- T1  = 5.5967 A
T1  - O4  - T2  - O4  - T1  = 135.619 deg; T1  -- T1  = 5.4992 A
T1  - O3  - T2  - O4  - T1  =  53.480 deg; T1  -- T1  = 2.6733 A

        T-T-T SUMMARY
          Range  = 53.4803 deg <--> 161.3808 deg
          Mean   = 104.2667 deg
          StdDev = 38.8302 deg

        T--T SUMMARY
          Range  = 2.6733 A <--> 5.7774 A
          Mean   = 4.3979 A
          StdDev = 1.2471 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 137.211 deg ; T1  -- T1   3.0273 A

T1  -- O2  -- T1  = 103.080 deg ; T1  -- T1   2.6733 A

T1  -- O3  -- T2  = 127.647 deg ; T1  -- T2   2.9273 A

T1  -- O4  -- T2  = 140.079 deg ; T1  -- T2   3.0117 A


        T-O-T SUMMARY
          Range  = 103.0804° <--> 140.0786 deg
          Mean   = 127.0041 deg
          StdDev = 14.6742 deg

        T--T SUMMARY
          Range  = 2.6733 A <--> 3.0273 A
          Mean   = 2.9099 A
          StdDev = 0.1429 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2646 A
O1  -- O4  = 2.2646 A
T1  -- T1  = 2.6733 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 23 38 65 82 107 135 174 203 242 290 336 380 432
TD10 = 650
Circuit symbol = 3.6.3.8.4.7
Weight = 8
Vertex symbol  = 3.6.3.13_{12}.13_{3}.13_{6}
Weight = 66

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 6 15 20 38 64 79 104 139 172 202 238 287 348 367 422
TD10 = 642
Circuit symbol = 3.3.6.8.7.7
Weight = 8
Vertex symbol  = 3.3.6.13_{6}.13_{9}.13_{9}
Weight = 74

<TD10> = 647.333
Average ring size = 9.8985