Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_615403_pMI0BI.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 17.01 T-atoms per nm^3
Material density = 1.697 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6522 Angstrom
T1  -- O3  = 1.4827 Angstrom
T1  -- O4  = 1.6603 Angstrom
T1  -- O1  = 1.6155 Angstrom
      mean = 1.6027 Angstrom
        t1 = 0.108358  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.126238  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6303 Angstrom
T2  -- O3  = 1.6303 Angstrom
T2  -- O4  = 1.6236 Angstrom
T2  -- O4  = 1.6236 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.092681  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.071658  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4827 A <--> 1.6603 A
          Mean   = 1.6108 A
          StdDev = 0.0597 A

       t1 Range  = 0.0927 <-- 0.1005 --> 0.1084
       t2 Range  = 0.0717 <-- 0.0989 --> 0.1262

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  =  93.107 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 131.722 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  = 106.406 deg; O2  -- O1  = 3 A
O3  -- T1  -- O4  =  88.311 deg; O3  -- O4  = 2 A
O3  -- T1  -- O1  = 118.525 deg; O3  -- O1  = 3 A
O4  -- T1  -- O1  = 115.005 deg; O4  -- O1  = 3 A
       88.311 deg <-- 108.846 deg --> 131.722 deg

O3  -- T2  -- O3  = 118.091 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 120.194 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  =  90.052 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  =  90.052 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 120.194 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 121.346 deg; O4  -- O4  = 3 A
       90.052 deg <-- 109.989 deg --> 121.346 deg

        O-T-O SUMMARY
          Range  = 88.3112 deg <--> 131.7218 deg
          Mean   = 109.5482 deg
          StdDev = 14.8650 deg

        O--O SUMMARY
          Range  = 2.1932 A <--> 3.0229 A
          Mean   = 2.6176 A
          StdDev = 0.2713 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  53.615 deg; T1  -- T2  = 2.6534 A
T1  - O2  - T1  - O4  - T2  = 106.490 deg; T1  -- T2  = 5.0235 A
T1  - O2  - T1  - O1  - T1  = 128.334 deg; T1  -- T1  = 5.6901 A
T2  - O3  - T1  - O4  - T2  =  78.819 deg; T2  -- T2  = 3.6843 A
T2  - O3  - T1  - O1  - T1  = 157.204 deg; T2  -- T1  = 5.7132 A
T2  - O4  - T1  - O1  - T1  = 116.901 deg; T2  -- T1  = 5.3652 A

T1  - O3  - T2  - O3  - T1  = 101.443 deg; T1  -- T1  = 4.4804 A
T1  - O3  - T2  - O4  - T1  =  72.771 deg; T1  -- T1  = 3.1480 A
T1  - O3  - T2  - O4  - T1  =  96.802 deg; T1  -- T1  = 4.3300 A
T1  - O3  - T2  - O4  - T1  =  96.802 deg; T1  -- T1  = 4.3300 A
T1  - O3  - T2  - O4  - T1  = 157.302 deg; T1  -- T1  = 6.1218 A
T1  - O4  - T2  - O4  - T1  = 101.443 deg; T1  -- T1  = 4.4804 A

        T-T-T SUMMARY
          Range  = 53.6145 deg <--> 157.3022 deg
          Mean   = 104.6748 deg
          StdDev = 30.1544 deg

        T--T SUMMARY
          Range  = 2.6534 A <--> 6.1218 A
          Mean   = 4.5370 A
          StdDev = 1.0148 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.421 deg ; T1  -- T1   3.1738 A

T1  -- O2  -- T1  = 144.610 deg ; T1  -- T1   3.1480 A

T1  -- O3  -- T2  = 116.855 deg ; T1  -- T2   2.6534 A

T1  -- O4  -- T2  = 143.854 deg ; T1  -- T2   3.1219 A


        T-O-T SUMMARY
          Range  = 116.8546° <--> 158.4207 deg
          Mean   = 140.9348 deg
          StdDev = 15.1826 deg

        T--T SUMMARY
          Range  = 2.6534 A <--> 3.1738 A
          Mean   = 3.0243 A
          StdDev = 0.2166 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.2790 A
O2  -- O3  = 2.2790 A
O3  -- O4  = 2.1932 A
T1  -- T2  = 2.6534 Angstrom
T2  -- T1  = 2.6534 Angstrom
T2  -- T1  = 2.6534 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 17 33 59 77 107 148 187 224 275 329 391 445 510 588
TD10 = 866
Circuit symbol = 3.10_{6}.4.8_{2}.5.8_{2}
Weight = 23
Vertex symbol  = 3.10_{4}.4.8_{2}.8_{2}.8_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 18 32 56 78 108 146 178 234 278 318 384 460 510 576
TD10 = 863
Circuit symbol = 3.7.4.4.5.5
Weight = 7
Vertex symbol  = 3.10_{4}.4.4.8_{2}.8_{2}
Weight = 35

<TD10> = 865.000
Average ring size = 6.7308