Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_606966_bmQgPG.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 28.26 T-atoms per nm^3
Material density = 2.820 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6689 Angstrom
T1  -- O2  = 1.6572 Angstrom
T1  -- O3  = 1.6180 Angstrom
T1  -- O4  = 1.6541 Angstrom
      mean = 1.6496 Angstrom
        t1 = 0.034832  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015729  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.4606 Angstrom
T2  -- O4  = 1.6316 Angstrom
T2  -- O4  = 1.6316 Angstrom
T2  -- O5  = 1.4606 Angstrom
      mean = 1.5461 Angstrom
        t1 = 0.206427  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.127314  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4606 A <--> 1.6689 A
          Mean   = 1.6151 A
          StdDev = 0.0715 A

       t1 Range  = 0.0348 <-- 0.1206 --> 0.2064
       t2 Range  = 0.0157 <-- 0.0715 --> 0.1273

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.481 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.536 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.555 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 106.202 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.908 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 104.716 deg; O3  -- O4  = 3 A
       104.716 deg <-- 109.400 deg --> 112.555 deg

O5  -- T2  -- O4  =  79.112 deg; O5  -- O4  = 2 A
O5  -- T2  -- O4  =  78.693 deg; O5  -- O4  = 2 A
O5  -- T2  -- O5  = 137.855 deg; O5  -- O5  = 3 A
O4  -- T2  -- O4  = 115.270 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  =  78.693 deg; O4  -- O5  = 2 A
O4  -- T2  -- O5  =  79.112 deg; O4  -- O5  = 2 A
       78.693 deg <-- 94.789 deg --> 137.855 deg

        O-T-O SUMMARY
          Range  = 78.6935 deg <--> 137.8547 deg
          Mean   = 99.2596 deg
          StdDev = 17.8800 deg

        O--O SUMMARY
          Range  = 1.9649 A <--> 2.7638 A
          Mean   = 2.4121 A
          StdDev = 0.3663 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 115.762 deg; T1  -- T2  = 5.2728 A
T1  - O1  - T1  - O3  - T1  = 116.555 deg; T1  -- T1  = 5.4516 A
T1  - O1  - T1  - O4  - T1  =  87.568 deg; T1  -- T1  = 4.3853 A
T2  - O2  - T1  - O3  - T1  = 112.080 deg; T2  -- T1  = 5.3347 A
T2  - O2  - T1  - O4  - T1  = 121.054 deg; T2  -- T1  = 5.5363 A
T1  - O3  - T1  - O4  - T1  = 101.266 deg; T1  -- T1  = 5.0571 A

T1  - O5  - T2  - O4  - T1  =  79.060 deg; T1  -- T1  = 3.9770 A
T1  - O5  - T2  - O4  - T2  =  72.824 deg; T1  -- T2  = 3.5921 A
T1  - O5  - T2  - O5  - T2  =  74.970 deg; T1  -- T2  = 3.6824 A
T1  - O4  - T2  - O4  - T2  =  74.970 deg; T1  -- T2  = 3.6824 A
T1  - O4  - T2  - O5  - T2  =  72.824 deg; T1  -- T2  = 3.5921 A
T2  - O4  - T2  - O5  - T2  = 137.855 deg; T2  -- T2  = 5.4516 A

        T-T-T SUMMARY
          Range  = 72.8238 deg <--> 137.8547 deg
          Mean   = 95.7104 deg
          StdDev = 22.5159 deg

        T--T SUMMARY
          Range  = 3.5921 A <--> 5.5363 A
          Mean   = 4.5145 A
          StdDev = 0.7978 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 164.294 deg ; T1  -- T1   3.3064 A

T1  -- O2  -- T1  = 138.687 deg ; T1  -- T1   3.1014 A

T1  -- O3  -- T1  = 176.661 deg ; T1  -- T1   3.2347 A

T1  -- O4  -- T2  = 143.925 deg ; T1  -- T2   3.1242 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   2.9212 A


        T-O-T SUMMARY
          Range  = 138.6873° <--> 180.0000 deg
          Mean   = 158.5706 deg
          StdDev = 16.4407 deg

        T--T SUMMARY
          Range  = 2.9212 A <--> 3.3064 A
          Mean   = 3.1616 A
          StdDev = 0.1165 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O5  = 1.9649 A
O4  -- O5  = 1.9736 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 44 68 98 138 185 235 290 353 420 493 571 656 746
TD10 = 1098
Circuit symbol = 4.6_{2}.6.6.6.6_{2}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6.6.6_{2}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 40 66 100 138 184 236 292 354 420 494 572 656 746
TD10 = 1097
Circuit symbol = 6.6.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1097.667
Average ring size = 5.7778