Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_600928_GyLTEy.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.18 T-atoms per nm^3
Material density = 2.213 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5885 Angstrom
T1  -- O2  = 1.6994 Angstrom
T1  -- O3  = 1.7138 Angstrom
T1  -- O4  = 1.5486 Angstrom
      mean = 1.6376 Angstrom
        t1 = 0.092923  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.065711  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6407 Angstrom
T2  -- O3  = 1.6407 Angstrom
T2  -- O4  = 1.5887 Angstrom
T2  -- O4  = 1.5887 Angstrom
      mean = 1.6147 Angstrom
        t1 = 0.065496  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061253  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5486 A <--> 1.7138 A
          Mean   = 1.6300 A
          StdDev = 0.0609 A

       t1 Range  = 0.0655 <-- 0.0792 --> 0.0929
       t2 Range  = 0.0613 <-- 0.0635 --> 0.0657

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 121.156 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  99.653 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  98.167 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 126.039 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  95.840 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 112.781 deg; O3  -- O4  = 3 A
       95.840 deg <-- 108.939 deg --> 126.039 deg

O3  -- T2  -- O3  = 128.325 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  =  98.136 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 110.493 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 110.493 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  =  98.136 deg; O3  -- O4  = 2 A
O4  -- T2  -- O4  = 111.335 deg; O4  -- O4  = 3 A
       98.136 deg <-- 109.486 deg --> 128.325 deg

        O-T-O SUMMARY
          Range  = 95.8398 deg <--> 128.3246 deg
          Mean   = 108.6934 deg
          StdDev = 10.9634 deg

        O--O SUMMARY
          Range  = 2.3707 A <--> 3.0418 A
          Mean   = 2.6317 A
          StdDev = 0.2108 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 101.897 deg; T2  -- T1  = 4.8233 A
T2  - O1  - T1  - O3  - T1  = 115.498 deg; T2  -- T1  = 5.2430 A
T2  - O1  - T1  - O4  - T2  =  89.720 deg; T2  -- T2  = 4.3310 A
T1  - O2  - T1  - O3  - T1  = 142.493 deg; T1  -- T1  = 5.9972 A
T1  - O2  - T1  - O4  - T2  =  92.098 deg; T1  -- T2  = 4.5172 A
T1  - O3  - T1  - O4  - T2  =  90.924 deg; T1  -- T2  = 4.4645 A

T1  - O3  - T2  - O3  - T1  = 122.380 deg; T1  -- T1  = 5.3798 A
T1  - O3  - T2  - O4  - T1  =  81.311 deg; T1  -- T1  = 4.0003 A
T1  - O3  - T2  - O4  - T1  = 137.770 deg; T1  -- T1  = 5.6676 A
T1  - O3  - T2  - O4  - T1  = 115.500 deg; T1  -- T1  = 5.2468 A
T1  - O3  - T2  - O4  - T1  =  81.311 deg; T1  -- T1  = 4.0003 A
T1  - O4  - T2  - O4  - T1  = 122.380 deg; T1  -- T1  = 5.3798 A

        T-T-T SUMMARY
          Range  = 81.3106 deg <--> 142.4928 deg
          Mean   = 108.0290 deg
          StdDev = 20.7487 deg

        T--T SUMMARY
          Range  = 4.0003 A <--> 5.9972 A
          Mean   = 4.9252 A
          StdDev = 0.6455 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.696 deg ; T1  -- T1   3.1722 A

T1  -- O2  -- T1  = 136.898 deg ; T1  -- T1   3.1613 A

T1  -- O3  -- T2  = 129.784 deg ; T1  -- T2   3.0377 A

T1  -- O4  -- T2  = 162.783 deg ; T1  -- T2   3.1019 A


        T-O-T SUMMARY
          Range  = 129.7844° <--> 173.6958 deg
          Mean   = 150.7902 deg
          StdDev = 18.1893 deg

        T--T SUMMARY
          Range  = 3.0377 A <--> 3.1722 A
          Mean   = 3.1183 A
          StdDev = 0.0541 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 41 66 96 134 178 227 285 345 408 480 562 648 733
TD10 = 1066
Circuit symbol = 4.8_{4}.6_{2}.6_{3}.6_{3}.8_{6}
Weight = 32
Vertex symbol  = 4.8_{3}.6_{2}.6_{3}.6_{3}.8_{4}
Weight = 32

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 40 64 92 128 178 226 272 340 416 486 550 628 736
TD10 = 1037
Circuit symbol = 4.4.6.6.6_{2}.8_{5}
Weight = 24
Vertex symbol  = 4.4.6.6.6_{2}.8_{3}
Weight = 24

<TD10> = 1056.333
Average ring size = 6.3484