Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_596847_7WiZmX.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 21.52 T-atoms per nm^3
Material density = 2.148 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O3  = 1.6277 Angstrom
T1  -- O4  = 1.5578 Angstrom
T1  -- O2  = 1.6589 Angstrom
      mean = 1.6149 Angstrom
        t1 = 0.064917  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060738  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5970 Angstrom
T2  -- O4  = 1.5970 Angstrom
T2  -- O5  = 1.6229 Angstrom
T2  -- O5  = 1.6229 Angstrom
      mean = 1.6100 Angstrom
        t1 = 0.059634  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045951  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5578 A <--> 1.6589 A
          Mean   = 1.6133 A
          StdDev = 0.0311 A

       t1 Range  = 0.0596 <-- 0.0623 --> 0.0649
       t2 Range  = 0.0460 <-- 0.0533 --> 0.0607

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  =  98.801 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 100.784 deg; O1  -- O4  = 2 A
O1  -- T1  -- O2  = 125.245 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 120.260 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 110.221 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 102.765 deg; O4  -- O2  = 3 A
       98.801 deg <-- 109.679 deg --> 125.245 deg

O4  -- T2  -- O4  = 120.150 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 102.726 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 102.895 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 102.895 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 102.726 deg; O4  -- O5  = 3 A
O5  -- T2  -- O5  = 127.222 deg; O5  -- O5  = 3 A
       102.726 deg <-- 109.769 deg --> 127.222 deg

        O-T-O SUMMARY
          Range  = 98.8006 deg <--> 127.2218 deg
          Mean   = 108.5946 deg
          StdDev = 9.3019 deg

        O--O SUMMARY
          Range  = 2.4449 A <--> 2.9077 A
          Mean   = 2.6043 A
          StdDev = 0.1496 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T1  = 102.629 deg; T2  -- T1  = 4.9812 A
T2  - O1  - T1  - O4  - T1  = 101.514 deg; T2  -- T1  = 5.0092 A
T2  - O1  - T1  - O2  - T1  = 135.325 deg; T2  -- T1  = 5.5314 A
T1  - O3  - T1  - O4  - T1  = 125.272 deg; T1  -- T1  = 5.8140 A
T1  - O3  - T1  - O2  - T1  = 110.271 deg; T1  -- T1  = 4.9764 A
T1  - O4  - T1  - O2  - T1  =  83.555 deg; T1  -- T1  = 4.1096 A

T1  - O4  - T2  - O4  - T1  = 125.868 deg; T1  -- T1  = 5.6110 A
T1  - O4  - T2  - O5  - T2  = 101.270 deg; T1  -- T2  = 4.9451 A
T1  - O4  - T2  - O5  - T2  = 102.071 deg; T1  -- T2  = 4.9733 A
T1  - O4  - T2  - O5  - T2  = 102.071 deg; T1  -- T2  = 4.9733 A
T1  - O4  - T2  - O5  - T2  = 101.270 deg; T1  -- T2  = 4.9451 A
T2  - O5  - T2  - O5  - T2  = 127.211 deg; T2  -- T2  = 5.8140 A

        T-T-T SUMMARY
          Range  = 83.5554 deg <--> 135.3254 deg
          Mean   = 108.0609 deg
          StdDev = 14.1614 deg

        T--T SUMMARY
          Range  = 4.1096 A <--> 5.8140 A
          Mean   = 5.1032 A
          StdDev = 0.4708 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.836 deg ; T1  -- T1   3.2304 A

T1  -- O2  -- T1  = 176.103 deg ; T1  -- T1   3.3159 A

T1  -- O3  -- T1  = 120.634 deg ; T1  -- T1   2.8282 A

T1  -- O4  -- T2  = 174.022 deg ; T1  -- T2   3.1505 A

T2  -- O5  -- T2  = 177.811 deg ; T2  -- T2   3.2453 A


        T-O-T SUMMARY
          Range  = 120.6340° <--> 179.8362 deg
          Mean   = 164.3335 deg
          StdDev = 23.6080 deg

        T--T SUMMARY
          Range  = 2.8282 A <--> 3.3159 A
          Mean   = 3.1439 A
          StdDev = 0.1789 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 44 68 98 138 185 235 290 353 420 493 571 656 746
TD10 = 1098
Circuit symbol = 4.6_{2}.6.6.6.6_{2}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6.6.6_{2}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 40 66 100 138 184 236 292 354 420 494 572 656 746
TD10 = 1097
Circuit symbol = 6.6.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1097.667
Average ring size = 5.7778