Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_569270_Upb2at.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.27 T-atoms per nm^3
Material density = 1.922 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6234 Angstrom
T1  -- O2  = 1.6198 Angstrom
T1  -- O3  = 1.7180 Angstrom
T1  -- O4  = 1.6275 Angstrom
      mean = 1.6472 Angstrom
        t1 = 0.041305  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026340  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6362 Angstrom
T2  -- O3  = 1.6362 Angstrom
T2  -- O4  = 1.6188 Angstrom
T2  -- O4  = 1.6188 Angstrom
      mean = 1.6275 Angstrom
        t1 = 0.055846  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052048  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6188 A <--> 1.7180 A
          Mean   = 1.6406 A
          StdDev = 0.0353 A

       t1 Range  = 0.0413 <-- 0.0486 --> 0.0558
       t2 Range  = 0.0263 <-- 0.0392 --> 0.0520

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.650 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.804 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 100.209 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 112.154 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.735 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.690 deg; O3  -- O4  = 3 A
       100.209 deg <-- 109.374 deg --> 112.154 deg

O3  -- T2  -- O3  = 114.113 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 119.572 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 102.565 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 102.565 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 119.572 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  =  98.345 deg; O4  -- O4  = 2 A
       98.345 deg <-- 109.455 deg --> 119.572 deg

        O-T-O SUMMARY
          Range  = 98.3451 deg <--> 119.5720 deg
          Mean   = 109.3174 deg
          StdDev = 6.9144 deg

        O--O SUMMARY
          Range  = 2.4498 A <--> 2.8128 A
          Mean   = 2.6680 A
          StdDev = 0.1259 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  58.044 deg; T1  -- T2  = 2.7339 A
T1  - O1  - T1  - O3  - T2  =  69.228 deg; T1  -- T2  = 3.0127 A
T1  - O1  - T1  - O4  - T1  = 143.630 deg; T1  -- T1  = 5.2975 A
T2  - O2  - T1  - O3  - T2  =  86.011 deg; T2  -- T2  = 3.9249 A
T2  - O2  - T1  - O4  - T1  = 101.805 deg; T2  -- T1  = 4.6741 A
T2  - O3  - T1  - O4  - T1  = 144.506 deg; T2  -- T1  = 5.4712 A

T1  - O3  - T2  - O3  - T1  = 148.168 deg; T1  -- T1  = 5.7944 A
T1  - O3  - T2  - O4  - T1  = 157.297 deg; T1  -- T1  = 5.6344 A
T1  - O3  - T2  - O4  - T1  =  52.728 deg; T1  -- T1  = 2.5641 A
T1  - O3  - T2  - O4  - T1  =  52.728 deg; T1  -- T1  = 2.5641 A
T1  - O3  - T2  - O4  - T1  = 157.297 deg; T1  -- T1  = 5.6344 A
T1  - O4  - T2  - O4  - T1  = 109.403 deg; T1  -- T1  = 4.4625 A

        T-T-T SUMMARY
          Range  = 52.7281 deg <--> 157.2973 deg
          Mean   = 108.8541 deg
          StdDev = 40.1664 deg

        T--T SUMMARY
          Range  = 2.5641 A <--> 5.7944 A
          Mean   = 4.3827 A
          StdDev = 1.2299 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 104.322 deg ; T1  -- T1   2.5641 A

T1  -- O2  -- T1  = 136.595 deg ; T1  -- T1   3.0100 A

T1  -- O3  -- T2  = 127.826 deg ; T1  -- T2   3.0127 A

T1  -- O4  -- T2  = 114.734 deg ; T1  -- T2   2.7339 A


        T-O-T SUMMARY
          Range  = 104.3221° <--> 136.5950 deg
          Mean   = 120.8692 deg
          StdDev = 12.4175 deg

        T--T SUMMARY
          Range  = 2.5641 A <--> 3.0127 A
          Mean   = 2.8302 A
          StdDev = 0.1924 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.5641 Angstrom
T1  -- T2  = 2.7339 Angstrom
T2  -- T1  = 2.7339 Angstrom
T2  -- T1  = 2.7339 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 23 38 65 82 107 139 172 205 242 286 347 371 433
TD10 = 652
Circuit symbol = 3.6.3.8.4.7
Weight = 8
Vertex symbol  = 3.6.3.13_{12}.13_{3}.13_{6}
Weight = 65

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 6 15 20 38 64 81 106 130 180 195 238 298 320 389 432
TD10 = 645
Circuit symbol = 3.3.6.8.7.7
Weight = 8
Vertex symbol  = 3.3.6.13_{10}.13_{5}.13_{5}
Weight = 62

<TD10> = 649.667
Average ring size = 9.7672