Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_565849_RD0Hi6.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 25.93 T-atoms per nm^3
Material density = 2.587 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5654 Angstrom
T1  -- O2  = 1.6637 Angstrom
T1  -- O3  = 1.6310 Angstrom
T1  -- O4  = 1.5116 Angstrom
      mean = 1.5929 Angstrom
        t1 = 0.078155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049354  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5676 Angstrom
T2  -- O4  = 1.5676 Angstrom
T2  -- O5  = 1.7543 Angstrom
T2  -- O5  = 1.7543 Angstrom
      mean = 1.6609 Angstrom
        t1 = 0.112252  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.068608  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5116 A <--> 1.7543 A
          Mean   = 1.6156 A
          StdDev = 0.0794 A

       t1 Range  = 0.0782 <-- 0.0952 --> 0.1123
       t2 Range  = 0.0494 <-- 0.0590 --> 0.0686

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 115.833 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.136 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  90.204 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 117.574 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.592 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.224 deg; O3  -- O4  = 3 A
       90.204 deg <-- 108.927 deg --> 117.574 deg

O4  -- T2  -- O4  = 104.605 deg; O4  -- O4  = 2 A
O4  -- T2  -- O5  = 106.211 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  =  97.271 deg; O4  -- O5  = 2 A
O4  -- T2  -- O5  =  97.271 deg; O4  -- O5  = 2 A
O4  -- T2  -- O5  = 106.211 deg; O4  -- O5  = 3 A
O5  -- T2  -- O5  = 141.248 deg; O5  -- O5  = 3 A
       97.271 deg <-- 108.803 deg --> 141.248 deg

        O-T-O SUMMARY
          Range  = 90.2038 deg <--> 141.2484 deg
          Mean   = 106.5485 deg
          StdDev = 10.9737 deg

        O--O SUMMARY
          Range  = 2.1800 A <--> 3.3099 A
          Mean   = 2.5911 A
          StdDev = 0.2253 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  78.471 deg; T1  -- T2  = 3.8604 A
T1  - O1  - T1  - O3  - T1  = 103.764 deg; T1  -- T1  = 4.8123 A
T1  - O1  - T1  - O4  - T1  = 128.618 deg; T1  -- T1  = 5.5236 A
T2  - O2  - T1  - O3  - T1  =  99.823 deg; T2  -- T1  = 4.4003 A
T2  - O2  - T1  - O4  - T1  =  94.055 deg; T2  -- T1  = 4.2204 A
T1  - O3  - T1  - O4  - T1  = 127.522 deg; T1  -- T1  = 5.1949 A

T1  - O4  - T2  - O4  - T1  = 140.900 deg; T1  -- T1  = 5.3976 A
T1  - O4  - T2  - O5  - T2  =  74.198 deg; T1  -- T2  = 3.8604 A
T1  - O4  - T2  - O5  - T2  = 119.733 deg; T1  -- T2  = 5.4983 A
T1  - O4  - T2  - O5  - T2  = 119.733 deg; T1  -- T2  = 5.4983 A
T1  - O4  - T2  - O5  - T2  =  74.198 deg; T1  -- T2  = 3.8604 A
T2  - O5  - T2  - O5  - T2  = 140.957 deg; T2  -- T2  = 6.5663 A

        T-T-T SUMMARY
          Range  = 74.1980 deg <--> 140.9566 deg
          Mean   = 109.0464 deg
          StdDev = 23.8529 deg

        T--T SUMMARY
          Range  = 3.8604 A <--> 6.5663 A
          Mean   = 4.8874 A
          StdDev = 0.7847 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.545 deg ; T1  -- T1   2.8876 A

T1  -- O2  -- T1  = 151.298 deg ; T1  -- T1   3.2235 A

T1  -- O3  -- T1  = 125.821 deg ; T1  -- T1   2.9041 A

T1  -- O4  -- T2  = 136.886 deg ; T1  -- T2   2.8639 A

T2  -- O5  -- T2  = 166.255 deg ; T2  -- T2   3.4834 A


        T-O-T SUMMARY
          Range  = 125.8213° <--> 166.2547 deg
          Mean   = 140.3727 deg
          StdDev = 12.6683 deg

        T--T SUMMARY
          Range  = 2.8639 A <--> 3.4834 A
          Mean   = 3.0268 A
          StdDev = 0.2144 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.1800 A
O1  -- O4  = 2.1800 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 26 48 79 117 162 219 284 363 445 540 637 746 856 980
TD10 = 1314
Circuit symbol = 4.7_{4}.6.6.6.7_{2}
Weight = 24
Vertex symbol  = 4.7_{4}.6.6.6.7_{2}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 23 46 80 114 166 216 281 350 435 526 624 728 848 968
TD10 = 1291
Circuit symbol = 4.4.6.6.6.7
Weight = 18
Vertex symbol  = 4.4.6.6.6.7
Weight = 18

<TD10> = 1306.333
Average ring size = 5.9672