Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_559411_Mc9uNl.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 25.92 T-atoms per nm^3
Material density = 2.586 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6635 Angstrom
T1  -- O3  = 1.6311 Angstrom
T1  -- O4  = 1.5115 Angstrom
T1  -- O1  = 1.5653 Angstrom
      mean = 1.5929 Angstrom
        t1 = 0.078150  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050122  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.7544 Angstrom
T2  -- O5  = 1.7544 Angstrom
T2  -- O4  = 1.5676 Angstrom
T2  -- O4  = 1.5676 Angstrom
      mean = 1.6610 Angstrom
        t1 = 0.112275  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.081362  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5115 A <--> 1.7544 A
          Mean   = 1.6156 A
          StdDev = 0.0794 A

       t1 Range  = 0.0781 <-- 0.0952 --> 0.1123
       t2 Range  = 0.0501 <-- 0.0657 --> 0.0814

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 117.584 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.587 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  = 115.817 deg; O2  -- O1  = 3 A
O3  -- T1  -- O4  = 111.223 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  = 107.145 deg; O3  -- O1  = 3 A
O4  -- T1  -- O1  =  90.205 deg; O4  -- O1  = 2 A
       90.205 deg <-- 108.927 deg --> 117.584 deg

O5  -- T2  -- O5  = 141.247 deg; O5  -- O5  = 3 A
O5  -- T2  -- O4  =  97.281 deg; O5  -- O4  = 2 A
O5  -- T2  -- O4  = 106.205 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  = 106.205 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  =  97.281 deg; O5  -- O4  = 2 A
O4  -- T2  -- O4  = 104.594 deg; O4  -- O4  = 2 A
       97.281 deg <-- 108.802 deg --> 141.247 deg

        O-T-O SUMMARY
          Range  = 90.2053 deg <--> 141.2468 deg
          Mean   = 106.5478 deg
          StdDev = 10.9714 deg

        O--O SUMMARY
          Range  = 2.1799 A <--> 3.3101 A
          Mean   = 2.5911 A
          StdDev = 0.2253 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T1  = 128.630 deg; T1  -- T1  = 5.5241 A
T1  - O2  - T1  - O4  - T1  = 103.764 deg; T1  -- T1  = 4.8128 A
T1  - O2  - T1  - O1  - T2  =  78.474 deg; T1  -- T2  = 3.8603 A
T1  - O3  - T1  - O4  - T1  = 127.509 deg; T1  -- T1  = 5.1954 A
T1  - O3  - T1  - O1  - T2  =  94.063 deg; T1  -- T2  = 4.2207 A
T1  - O4  - T1  - O1  - T2  =  99.836 deg; T1  -- T2  = 4.4009 A

T2  - O5  - T2  - O5  - T1  =  74.196 deg; T2  -- T1  = 3.8603 A
T2  - O5  - T2  - O4  - T1  = 119.736 deg; T2  -- T1  = 5.4984 A
T2  - O5  - T2  - O4  - T2  = 140.955 deg; T2  -- T2  = 6.5667 A
T1  - O5  - T2  - O4  - T1  = 140.900 deg; T1  -- T1  = 5.3971 A
T1  - O5  - T2  - O4  - T2  = 119.736 deg; T1  -- T2  = 5.4984 A
T1  - O4  - T2  - O4  - T2  =  74.196 deg; T1  -- T2  = 3.8603 A

        T-T-T SUMMARY
          Range  = 74.1959 deg <--> 140.9548 deg
          Mean   = 111.4313 deg
          StdDev = 22.9875 deg

        T--T SUMMARY
          Range  = 3.8603 A <--> 6.5667 A
          Mean   = 4.9963 A
          StdDev = 0.8137 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.607 deg ; T1  -- T1   2.8882 A

T1  -- O2  -- T1  = 151.340 deg ; T1  -- T1   3.2235 A

T1  -- O3  -- T1  = 125.828 deg ; T1  -- T1   2.9043 A

T1  -- O4  -- T2  = 136.866 deg ; T1  -- T2   2.8636 A

T2  -- O5  -- T2  = 166.251 deg ; T2  -- T2   3.4836 A


        T-O-T SUMMARY
          Range  = 125.8285° <--> 166.2505 deg
          Mean   = 140.3925 deg
          StdDev = 12.6684 deg

        T--T SUMMARY
          Range  = 2.8636 A <--> 3.4836 A
          Mean   = 3.0270 A
          StdDev = 0.2143 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.1799 A
O1  -- O4  = 2.1799 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 26 48 79 117 162 219 284 363 445 540 637 746 856 980
TD10 = 1314
Circuit symbol = 4.7_{4}.6.6.6.7_{2}
Weight = 24
Vertex symbol  = 4.7_{4}.6.6.6.7_{2}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 23 46 80 114 166 216 281 350 435 526 624 728 848 968
TD10 = 1291
Circuit symbol = 4.4.6.6.6.7
Weight = 18
Vertex symbol  = 4.4.6.6.6.7
Weight = 18

<TD10> = 1306.333
Average ring size = 5.9672