Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_557509_EzCRwm.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 23.92 T-atoms per nm^3
Material density = 2.387 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6434 Angstrom
T1  -- O3  = 1.6126 Angstrom
T1  -- O4  = 1.5888 Angstrom
T1  -- O2  = 1.5289 Angstrom
      mean = 1.5934 Angstrom
        t1 = 0.070692  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.055744  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6965 Angstrom
T2  -- O5  = 1.6965 Angstrom
T2  -- O4  = 1.6147 Angstrom
T2  -- O4  = 1.6147 Angstrom
      mean = 1.6556 Angstrom
        t1 = 0.076615  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.067503  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5289 A <--> 1.6965 A
          Mean   = 1.6141 A
          StdDev = 0.0512 A

       t1 Range  = 0.0707 <-- 0.0737 --> 0.0766
       t2 Range  = 0.0557 <-- 0.0616 --> 0.0675

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 114.802 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 114.958 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 112.091 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 118.207 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  =  96.244 deg; O3  -- O2  = 2 A
O4  -- T1  -- O2  =  96.911 deg; O4  -- O2  = 2 A
       96.244 deg <-- 108.869 deg --> 118.207 deg

O5  -- T2  -- O5  = 121.728 deg; O5  -- O5  = 3 A
O5  -- T2  -- O4  =  96.941 deg; O5  -- O4  = 2 A
O5  -- T2  -- O4  = 117.718 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  = 117.718 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  =  96.941 deg; O5  -- O4  = 2 A
O4  -- T2  -- O4  = 106.007 deg; O4  -- O4  = 3 A
       96.941 deg <-- 109.509 deg --> 121.728 deg

        O-T-O SUMMARY
          Range  = 96.2441 deg <--> 121.7278 deg
          Mean   = 108.7835 deg
          StdDev = 9.5256 deg

        O--O SUMMARY
          Range  = 2.3337 A <--> 2.9636 A
          Mean   = 2.6352 A
          StdDev = 0.1866 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  =  87.033 deg; T1  -- T1  = 4.2755 A
T1  - O1  - T1  - O4  - T1  = 112.008 deg; T1  -- T1  = 5.2553 A
T1  - O1  - T1  - O2  - T2  = 129.254 deg; T1  -- T2  = 5.8052 A
T1  - O3  - T1  - O4  - T1  = 103.766 deg; T1  -- T1  = 4.6986 A
T1  - O3  - T1  - O2  - T2  = 133.079 deg; T1  -- T2  = 5.5587 A
T1  - O4  - T1  - O2  - T2  =  89.883 deg; T1  -- T2  = 4.3789 A

T2  - O5  - T2  - O5  - T1  =  93.090 deg; T2  -- T1  = 4.5348 A
T2  - O5  - T2  - O4  - T1  = 136.463 deg; T2  -- T1  = 5.8014 A
T2  - O5  - T2  - O4  - T2  = 115.686 deg; T2  -- T2  = 5.2553 A
T1  - O5  - T2  - O4  - T1  =  85.949 deg; T1  -- T1  = 4.2851 A
T1  - O5  - T2  - O4  - T2  = 136.463 deg; T1  -- T2  = 5.8014 A
T1  - O4  - T2  - O4  - T2  =  93.090 deg; T1  -- T2  = 4.5348 A

        T-T-T SUMMARY
          Range  = 85.9493 deg <--> 136.4630 deg
          Mean   = 109.4536 deg
          StdDev = 19.0340 deg

        T--T SUMMARY
          Range  = 4.2755 A <--> 5.8052 A
          Mean   = 5.0098 A
          StdDev = 0.5908 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.538 deg ; T1  -- T1   3.2816 A

T1  -- O2  -- T1  = 175.452 deg ; T1  -- T1   3.0553 A

T1  -- O3  -- T1  = 129.400 deg ; T1  -- T1   2.9158 A

T1  -- O4  -- T2  = 157.710 deg ; T1  -- T2   3.1430 A

T2  -- O5  -- T2  = 132.349 deg ; T2  -- T2   3.1038 A


        T-O-T SUMMARY
          Range  = 129.3998° <--> 175.4522 deg
          Mean   = 156.0611 deg
          StdDev = 19.4350 deg

        T--T SUMMARY
          Range  = 2.9158 A <--> 3.2816 A
          Mean   = 3.0995 A
          StdDev = 0.1263 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 27 47 80 111 151 206 269 330 394 475 567 661 751 853
TD10 = 1237
Circuit symbol = 4.6.6.6.6.7_{5}
Weight = 24
Vertex symbol  = 4.6.6.6.6.7_{5}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 27 46 78 112 166 204 260 332 410 488 557 652 760 868
TD10 = 1242
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 1238.667
Average ring size = 6.0968