Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_554642_7uziyS.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 20.91 T-atoms per nm^3
Material density = 2.086 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6114 Angstrom
T1  -- O2  = 1.6293 Angstrom
T1  -- O3  = 1.6361 Angstrom
T1  -- O4  = 1.6509 Angstrom
      mean = 1.6319 Angstrom
        t1 = 0.024482  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020411  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6207 Angstrom
T2  -- O4  = 1.6305 Angstrom
T2  -- O3  = 1.6207 Angstrom
T2  -- O4  = 1.6305 Angstrom
      mean = 1.6256 Angstrom
        t1 = 0.038316  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023591  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6114 A <--> 1.6509 A
          Mean   = 1.6298 A
          StdDev = 0.0124 A

       t1 Range  = 0.0245 <-- 0.0314 --> 0.0383
       t2 Range  = 0.0204 <-- 0.0220 --> 0.0236

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.529 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.185 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 105.741 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.500 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 113.993 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.448 deg; O3  -- O4  = 3 A
       105.741 deg <-- 109.399 deg --> 113.993 deg

O3  -- T2  -- O4  = 104.730 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 110.490 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 117.515 deg; O3  -- O4  = 3 A
O4  -- T2  -- O3  = 117.515 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 102.162 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  = 104.730 deg; O3  -- O4  = 3 A
       102.162 deg <-- 109.524 deg --> 117.515 deg

        O-T-O SUMMARY
          Range  = 102.1624 deg <--> 117.5151 deg
          Mean   = 109.4588 deg
          StdDev = 4.9309 deg

        O--O SUMMARY
          Range  = 2.5372 A <--> 2.7797 A
          Mean   = 2.6577 A
          StdDev = 0.0816 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  60.770 deg; T2  -- T1  = 2.7887 A
T2  - O1  - T1  - O3  - T1  = 154.483 deg; T2  -- T1  = 5.6284 A
T2  - O1  - T1  - O4  - T2  =  81.746 deg; T2  -- T2  = 3.8353 A
T1  - O2  - T1  - O3  - T1  = 144.639 deg; T1  -- T1  = 5.4367 A
T1  - O2  - T1  - O4  - T2  = 115.472 deg; T1  -- T2  = 4.8970 A
T1  - O3  - T1  - O4  - T2  =  84.831 deg; T1  -- T2  = 4.0783 A

T1  - O3  - T2  - O4  - T1  =  86.789 deg; T1  -- T1  = 4.0256 A
T1  - O3  - T2  - O3  - T1  = 132.197 deg; T1  -- T1  = 5.6019 A
T1  - O3  - T2  - O4  - T1  = 139.744 deg; T1  -- T1  = 5.4957 A
T1  - O4  - T2  - O3  - T1  = 139.744 deg; T1  -- T1  = 5.4957 A
T1  - O4  - T2  - O4  - T1  =  58.461 deg; T1  -- T1  = 2.7236 A
T1  - O3  - T2  - O4  - T1  =  86.789 deg; T1  -- T1  = 4.0256 A

        T-T-T SUMMARY
          Range  = 58.4609 deg <--> 154.4829 deg
          Mean   = 109.1546 deg
          StdDev = 32.1742 deg

        T--T SUMMARY
          Range  = 2.7236 A <--> 5.6284 A
          Mean   = 4.5772 A
          StdDev = 0.9863 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 115.363 deg ; T1  -- T1   2.7236 A

T1  -- O2  -- T1  = 132.447 deg ; T1  -- T1   2.9820 A

T1  -- O3  -- T2  = 140.340 deg ; T1  -- T2   3.0637 A

T1  -- O4  -- T2  = 116.386 deg ; T1  -- T2   2.7887 A


        T-O-T SUMMARY
          Range  = 115.3627° <--> 140.3402 deg
          Mean   = 126.1342 deg
          StdDev = 10.7227 deg

        T--T SUMMARY
          Range  = 2.7236 A <--> 3.0637 A
          Mean   = 2.8895 A
          StdDev = 0.1395 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7887 Angstrom
T1  -- T1  = 2.7236 Angstrom
T2  -- T1  = 2.7887 Angstrom
T2  -- T1  = 2.7887 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 16 30 55 86 114 159 197 236 301 367 411 486 572 636
TD10 = 907
Circuit symbol = 3.6.4.9.5.8
Weight = 9
Vertex symbol  = 3.6.4.12_{20}.12_{4}.12_{6}
Weight = 61

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 17 30 52 88 114 156 189 250 304 344 416 518 545 618
TD10 = 909
Circuit symbol = 3.6.4.4.5.5
Weight = 10
Vertex symbol  = 3.6.4.4.12_{4}.12_{4}
Weight = 30

<TD10> = 907.667
Average ring size = 9.5510