Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_546352_1toL8Z.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.50 T-atoms per nm^3
Material density = 2.245 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5426 Angstrom
T1  -- O2  = 1.6090 Angstrom
T1  -- O3  = 1.6337 Angstrom
T1  -- O4  = 1.6103 Angstrom
      mean = 1.5989 Angstrom
        t1 = 0.099409  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.126548  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6409 Angstrom
T2  -- O5  = 1.7145 Angstrom
T2  -- O4  = 1.6409 Angstrom
T2  -- O5  = 1.7145 Angstrom
      mean = 1.6777 Angstrom
        t1 = 0.092356  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053568  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5426 A <--> 1.7145 A
          Mean   = 1.6252 A
          StdDev = 0.0513 A

       t1 Range  = 0.0924 <-- 0.0959 --> 0.0994
       t2 Range  = 0.0536 <-- 0.0901 --> 0.1265

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.728 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  84.584 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 100.737 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 115.765 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.282 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 130.189 deg; O3  -- O4  = 3 A
       84.584 deg <-- 109.214 deg --> 130.189 deg

O4  -- T2  -- O5  = 118.887 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 108.456 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  =  93.943 deg; O4  -- O5  = 2 A
O5  -- T2  -- O4  =  93.943 deg; O5  -- O4  = 2 A
O5  -- T2  -- O5  = 123.669 deg; O5  -- O5  = 3 A
O4  -- T2  -- O5  = 118.887 deg; O4  -- O5  = 3 A
       93.943 deg <-- 109.631 deg --> 123.669 deg

        O-T-O SUMMARY
          Range  = 84.5843 deg <--> 130.1892 deg
          Mean   = 109.1197 deg
          StdDev = 12.9817 deg

        O--O SUMMARY
          Range  = 2.1384 A <--> 3.0229 A
          Mean   = 2.6578 A
          StdDev = 0.2344 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 105.409 deg; T1  -- T2  = 4.8908 A
T1  - O1  - T1  - O3  - T1  = 121.889 deg; T1  -- T1  = 5.3875 A
T1  - O1  - T1  - O4  - T1  =  83.887 deg; T1  -- T1  = 3.9654 A
T2  - O2  - T1  - O3  - T1  =  59.804 deg; T2  -- T1  = 2.9271 A
T2  - O2  - T1  - O4  - T1  = 168.865 deg; T2  -- T1  = 5.5872 A
T1  - O3  - T1  - O4  - T1  = 110.222 deg; T1  -- T1  = 4.6212 A

T1  - O4  - T2  - O5  - T2  = 103.095 deg; T1  -- T2  = 4.7553 A
T1  - O4  - T2  - O4  - T1  =  60.393 deg; T1  -- T1  = 2.9445 A
T1  - O4  - T2  - O5  - T2  = 131.583 deg; T1  -- T2  = 5.5367 A
T2  - O5  - T2  - O4  - T1  = 131.583 deg; T2  -- T1  = 5.5367 A
T2  - O5  - T2  - O5  - T2  = 118.001 deg; T2  -- T2  = 5.3875 A
T1  - O4  - T2  - O5  - T2  = 103.095 deg; T1  -- T2  = 4.7553 A

        T-T-T SUMMARY
          Range  = 59.8037 deg <--> 168.8654 deg
          Mean   = 109.5276 deg
          StdDev = 30.1040 deg

        T--T SUMMARY
          Range  = 2.9271 A <--> 5.5872 A
          Mean   = 4.6999 A
          StdDev = 0.8907 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.263 deg ; T1  -- T1   2.9445 A

T1  -- O2  -- T1  = 176.885 deg ; T1  -- T1   3.2168 A

T1  -- O3  -- T1  = 110.614 deg ; T1  -- T1   2.6865 A

T1  -- O4  -- T2  = 128.397 deg ; T1  -- T2   2.9271 A

T2  -- O5  -- T2  = 132.837 deg ; T2  -- T2   3.1426 A


        T-O-T SUMMARY
          Range  = 110.6137° <--> 176.8849 deg
          Mean   = 139.4615 deg
          StdDev = 23.3079 deg

        T--T SUMMARY
          Range  = 2.6865 A <--> 3.2168 A
          Mean   = 2.9658 A
          StdDev = 0.1890 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.1384 A
O1  -- O3  = 2.1384 A
T1  -- T1  = 2.6865 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 21 42 66 97 131 177 225 271 331 401 471 527 618 720
TD10 = 1044
Circuit symbol = 3.4.8.8_{3}.8_{3}.8_{3}
Weight = 32
Vertex symbol  = 3.4.8.8_{3}.8_{3}.8_{3}
Weight = 32

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 24 42 65 100 136 176 218 286 337 388 460 560 628 694
TD10 = 1062
Circuit symbol = 3.8_{4}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 45
Vertex symbol  = 3.8_{4}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 45

<TD10> = 1050.000
Average ring size = 6.8333