Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_544570_AjMYUS.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 23.40 T-atoms per nm^3
Material density = 2.335 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6595 Angstrom
T1  -- O2  = 1.5402 Angstrom
T1  -- O3  = 1.6052 Angstrom
T1  -- O4  = 1.6507 Angstrom
      mean = 1.6139 Angstrom
        t1 = 0.101359  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076219  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6448 Angstrom
T2  -- O5  = 1.6585 Angstrom
T2  -- O4  = 1.6448 Angstrom
T2  -- O5  = 1.6585 Angstrom
      mean = 1.6516 Angstrom
        t1 = 0.038791  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018356  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5402 A <--> 1.6595 A
          Mean   = 1.6265 A
          StdDev = 0.0429 A

       t1 Range  = 0.0388 <-- 0.0701 --> 0.1014
       t2 Range  = 0.0184 <-- 0.0473 --> 0.0762

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.928 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.150 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 115.123 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  83.752 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  =  98.131 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 121.862 deg; O3  -- O4  = 3 A
       83.752 deg <-- 108.324 deg --> 121.862 deg

O4  -- T2  -- O5  = 110.989 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 109.513 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 104.091 deg; O4  -- O5  = 3 A
O5  -- T2  -- O4  = 104.091 deg; O5  -- O4  = 3 A
O5  -- T2  -- O5  = 117.159 deg; O5  -- O5  = 3 A
O4  -- T2  -- O5  = 110.989 deg; O4  -- O5  = 3 A
       104.091 deg <-- 109.472 deg --> 117.159 deg

        O-T-O SUMMARY
          Range  = 83.7517 deg <--> 121.8619 deg
          Mean   = 109.0783 deg
          StdDev = 8.8169 deg

        O--O SUMMARY
          Range  = 2.1002 A <--> 2.8459 A
          Mean   = 2.6591 A
          StdDev = 0.1757 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 103.073 deg; T2  -- T1  = 4.8238 A
T2  - O1  - T1  - O3  - T1  =  59.196 deg; T2  -- T1  = 2.8299 A
T2  - O1  - T1  - O4  - T1  = 167.300 deg; T2  -- T1  = 5.5389 A
T1  - O2  - T1  - O3  - T1  = 116.213 deg; T1  -- T1  = 5.2830 A
T1  - O2  - T1  - O4  - T1  =  85.035 deg; T1  -- T1  = 4.1185 A
T1  - O3  - T1  - O4  - T1  = 108.538 deg; T1  -- T1  = 4.5806 A

T1  - O4  - T2  - O5  - T2  =  96.689 deg; T1  -- T2  = 4.4786 A
T1  - O4  - T2  - O4  - T1  =  61.609 deg; T1  -- T1  = 2.8984 A
T1  - O4  - T2  - O5  - T2  = 145.526 deg; T1  -- T2  = 5.7190 A
T2  - O5  - T2  - O4  - T1  = 145.526 deg; T2  -- T1  = 5.7190 A
T2  - O5  - T2  - O5  - T2  = 113.580 deg; T2  -- T2  = 5.2830 A
T1  - O4  - T2  - O5  - T2  =  96.689 deg; T1  -- T2  = 4.4786 A

        T-T-T SUMMARY
          Range  = 59.1955 deg <--> 167.3000 deg
          Mean   = 110.2945 deg
          StdDev = 32.4564 deg

        T--T SUMMARY
          Range  = 2.8299 A <--> 5.7190 A
          Mean   = 4.6641 A
          StdDev = 0.9281 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 177.995 deg ; T1  -- T1   3.3185 A

T1  -- O2  -- T1  = 140.424 deg ; T1  -- T1   2.8984 A

T1  -- O3  -- T1  = 117.400 deg ; T1  -- T1   2.7432 A

T1  -- O4  -- T2  = 118.346 deg ; T1  -- T2   2.8299 A

T2  -- O5  -- T2  = 144.280 deg ; T2  -- T2   3.1572 A


        T-O-T SUMMARY
          Range  = 117.4000° <--> 177.9954 deg
          Mean   = 139.1791 deg
          StdDev = 23.3991 deg

        T--T SUMMARY
          Range  = 2.7432 A <--> 3.3185 A
          Mean   = 2.9708 A
          StdDev = 0.2202 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.1002 A
O2  -- O3  = 2.1002 A
T1  -- T1  = 2.7432 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 33 56 93 130 173 225 267 330 395 470 521 620 714
TD10 = 1009
Circuit symbol = 3.4.5.8.6.7
Weight = 8
Vertex symbol  = 3.4.5.10_{6}.10_{2}.13_{7}
Weight = 46

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 16 30 57 96 134 174 216 284 333 388 456 558 626 692
TD10 = 1022
Circuit symbol = 3.5.5.5.6.6
Weight = 11
Vertex symbol  = 3.5.5.5.13_{2}.13_{2}
Weight = 29

<TD10> = 1013.333
Average ring size = 8.0224