Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_521889_y75xJA.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 15.49 T-atoms per nm^3
Material density = 1.545 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6240 Angstrom
T1  -- O2  = 1.6239 Angstrom
T1  -- O4  = 1.6093 Angstrom
T1  -- O3  = 1.6224 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.007353  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002750  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6234 Angstrom
T2  -- O5  = 1.6228 Angstrom
T2  -- O6  = 1.6243 Angstrom
T2  -- O4  = 1.6128 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.007304  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001834  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6093 A <--> 1.6243 A
          Mean   = 1.6204 A
          StdDev = 0.0055 A

       t1 Range  = 0.0073 <-- 0.0073 --> 0.0074
       t2 Range  = 0.0018 <-- 0.0023 --> 0.0027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.043 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.520 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.621 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.173 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.469 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.996 deg; O4  -- O3  = 3 A
       108.996 deg <-- 109.470 deg --> 110.043 deg

O3  -- T2  -- O5  = 109.487 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.260 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.256 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 110.038 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.317 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.468 deg; O6  -- O4  = 3 A
       109.256 deg <-- 109.471 deg --> 110.038 deg

        O-T-O SUMMARY
          Range  = 108.9955 deg <--> 110.0430 deg
          Mean   = 109.4187 deg
          StdDev = 0.2616 deg

        O--O SUMMARY
          Range  = 2.6309 A <--> 2.6612 A
          Mean   = 2.6447 A
          StdDev = 0.0085 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.014 deg; T1  -- T2  = 4.4061 A
T1  - O1  - T1  - O4  - T2  = 130.594 deg; T1  -- T2  = 5.4697 A
T1  - O1  - T1  - O3  - T1  = 137.303 deg; T1  -- T1  = 5.5539 A
T2  - O2  - T1  - O4  - T2  =  89.858 deg; T2  -- T2  = 4.3966 A
T2  - O2  - T1  - O3  - T1  =  87.893 deg; T2  -- T1  = 4.2822 A
T2  - O4  - T1  - O3  - T1  =  92.055 deg; T2  -- T1  = 4.2878 A

T2  - O3  - T2  - O5  - T1  =  89.986 deg; T2  -- T1  = 4.4061 A
T2  - O3  - T2  - O6  - T2  = 137.503 deg; T2  -- T2  = 5.5562 A
T2  - O3  - T2  - O4  - T1  = 130.507 deg; T2  -- T1  = 5.4692 A
T1  - O5  - T2  - O6  - T2  =  88.093 deg; T1  -- T2  = 4.2878 A
T1  - O5  - T2  - O4  - T1  =  90.142 deg; T1  -- T1  = 4.4075 A
T2  - O6  - T2  - O4  - T1  =  91.959 deg; T2  -- T1  = 4.2822 A

        T-T-T SUMMARY
          Range  = 87.8932 deg <--> 137.5028 deg
          Mean   = 106.0775 deg
          StdDev = 21.2818 deg

        T--T SUMMARY
          Range  = 4.2822 A <--> 5.5562 A
          Mean   = 4.7689 A
          StdDev = 0.5661 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.130 deg ; T1  -- T1   3.0130 A

T1  -- O2  -- T1  = 130.556 deg ; T1  -- T1   2.9501 A

T1  -- O3  -- T2  = 135.841 deg ; T1  -- T2   3.0077 A

T1  -- O4  -- T2  = 172.010 deg ; T1  -- T2   3.2142 A

T2  -- O5  -- T2  = 136.489 deg ; T2  -- T2   3.0145 A

T2  -- O6  -- T2  = 130.227 deg ; T2  -- T2   2.9470 A


        T-O-T SUMMARY
          Range  = 130.2275° <--> 172.0101 deg
          Mean   = 140.2090 deg
          StdDev = 14.5308 deg

        T--T SUMMARY
          Range  = 2.9470 A <--> 3.2142 A
          Mean   = 3.0244 A
          StdDev = 0.0900 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

<TD10> = 556.000
Average ring size = 5.6000