Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_521385_wu4Xkb.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 15.16 T-atoms per nm^3
Material density = 1.513 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6242 Angstrom
T1  -- O2  = 1.6221 Angstrom
T1  -- O3  = 1.6274 Angstrom
T1  -- O4  = 1.6104 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.007777  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004163  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6275 Angstrom
T2  -- O4  = 1.6106 Angstrom
T2  -- O5  = 1.6242 Angstrom
T2  -- O6  = 1.6220 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007786  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004130  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6104 A <--> 1.6275 A
          Mean   = 1.6210 A
          StdDev = 0.0064 A

       t1 Range  = 0.0078 <-- 0.0078 --> 0.0078
       t2 Range  = 0.0041 <-- 0.0041 --> 0.0042

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.696 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.878 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.270 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.498 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.402 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.080 deg; O3  -- O4  = 3 A
       109.080 deg <-- 109.471 deg --> 109.878 deg

O3  -- T2  -- O4  = 109.087 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.874 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.489 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.270 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.402 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.702 deg; O5  -- O6  = 3 A
       109.087 deg <-- 109.471 deg --> 109.874 deg

        O-T-O SUMMARY
          Range  = 109.0800 deg <--> 109.8781 deg
          Mean   = 109.4500 deg
          StdDev = 0.2649 deg

        O--O SUMMARY
          Range  = 2.6373 A <--> 2.6616 A
          Mean   = 2.6465 A
          StdDev = 0.0099 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 133.240 deg; T1  -- T2  = 5.5012 A
T1  - O1  - T1  - O3  - T2  =  90.000 deg; T1  -- T2  = 4.3958 A
T1  - O1  - T1  - O4  - T1  = 134.610 deg; T1  -- T1  = 5.5366 A
T2  - O2  - T1  - O3  - T2  =  89.996 deg; T2  -- T2  = 4.3803 A
T2  - O2  - T1  - O4  - T1  =  92.110 deg; T2  -- T1  = 4.3048 A
T2  - O3  - T1  - O4  - T1  =  87.890 deg; T2  -- T1  = 4.3047 A

T1  - O3  - T2  - O4  - T1  =  90.004 deg; T1  -- T1  = 4.3806 A
T1  - O3  - T2  - O5  - T2  = 133.240 deg; T1  -- T2  = 5.5012 A
T1  - O3  - T2  - O6  - T2  =  92.106 deg; T1  -- T2  = 4.3047 A
T1  - O4  - T2  - O5  - T2  =  90.000 deg; T1  -- T2  = 4.3958 A
T1  - O4  - T2  - O6  - T2  =  87.894 deg; T1  -- T2  = 4.3048 A
T2  - O5  - T2  - O6  - T2  = 134.614 deg; T2  -- T2  = 5.5367 A

        T-T-T SUMMARY
          Range  = 87.8902 deg <--> 134.6140 deg
          Mean   = 101.9798 deg
          StdDev = 19.6634 deg

        T--T SUMMARY
          Range  = 4.3047 A <--> 5.5367 A
          Mean   = 4.6662 A
          StdDev = 0.5250 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.630 deg ; T1  -- T1   3.0079 A

T1  -- O2  -- T1  = 134.654 deg ; T1  -- T1   2.9935 A

T1  -- O3  -- T2  = 133.037 deg ; T1  -- T2   2.9854 A

T1  -- O4  -- T2  = 168.797 deg ; T1  -- T2   3.2056 A

T2  -- O5  -- T2  = 135.630 deg ; T2  -- T2   3.0079 A

T2  -- O6  -- T2  = 134.663 deg ; T2  -- T2   2.9934 A


        T-O-T SUMMARY
          Range  = 133.0368° <--> 168.7968 deg
          Mean   = 140.4018 deg
          StdDev = 12.7949 deg

        T--T SUMMARY
          Range  = 2.9854 A <--> 3.2056 A
          Mean   = 3.0323 A
          StdDev = 0.0783 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

<TD10> = 556.000
Average ring size = 5.6000