Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_481181_3mOj9w.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 18.18 T-atoms per nm^3
Material density = 1.814 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6090 Angstrom
T1  -- O2  = 1.6190 Angstrom
T1  -- O3  = 1.6060 Angstrom
T1  -- O4  = 1.5848 Angstrom
      mean = 1.6047 Angstrom
        t1 = 0.044733  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031175  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6408 Angstrom
T2  -- O4  = 1.6477 Angstrom
T2  -- O5  = 1.6805 Angstrom
T2  -- O6  = 1.6770 Angstrom
      mean = 1.6615 Angstrom
        t1 = 0.050269  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033595  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5848 A <--> 1.6805 A
          Mean   = 1.6331 A
          StdDev = 0.0323 A

       t1 Range  = 0.0447 <-- 0.0475 --> 0.0503
       t2 Range  = 0.0312 <-- 0.0324 --> 0.0336

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.258 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.605 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  99.223 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 112.065 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.813 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 115.662 deg; O3  -- O4  = 3 A
       99.223 deg <-- 109.437 deg --> 119.258 deg

O3  -- T2  -- O4  = 108.507 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 103.640 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.955 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 110.231 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.607 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 121.444 deg; O5  -- O6  = 3 A
       103.640 deg <-- 109.397 deg --> 121.444 deg

        O-T-O SUMMARY
          Range  = 99.2227 deg <--> 121.4441 deg
          Mean   = 108.4232 deg
          StdDev = 5.7027 deg

        O--O SUMMARY
          Range  = 2.4327 A <--> 2.9286 A
          Mean   = 2.6445 A
          StdDev = 0.1083 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 124.939 deg; T1  -- T1  = 5.0568 A
T1  - O1  - T1  - O3  - T2  =  61.438 deg; T1  -- T2  = 2.8272 A
T1  - O1  - T1  - O4  - T2  =  58.053 deg; T1  -- T2  = 2.7314 A
T1  - O2  - T1  - O3  - T2  = 158.896 deg; T1  -- T2  = 5.5367 A
T1  - O2  - T1  - O4  - T2  =  87.281 deg; T1  -- T2  = 3.9532 A
T2  - O3  - T1  - O4  - T2  = 110.479 deg; T2  -- T2  = 4.5669 A

T1  - O3  - T2  - O4  - T1  =  60.508 deg; T1  -- T1  = 2.8018 A
T1  - O3  - T2  - O5  - T2  =  94.193 deg; T1  -- T2  = 4.4134 A
T1  - O3  - T2  - O6  - T2  = 106.187 deg; T1  -- T2  = 4.3915 A
T1  - O4  - T2  - O5  - T2  =  80.432 deg; T1  -- T2  = 3.9532 A
T1  - O4  - T2  - O6  - T2  = 104.776 deg; T1  -- T2  = 4.4266 A
T2  - O5  - T2  - O6  - T2  = 158.940 deg; T2  -- T2  = 5.9325 A

        T-T-T SUMMARY
          Range  = 58.0534 deg <--> 158.9402 deg
          Mean   = 96.7439 deg
          StdDev = 31.6487 deg

        T--T SUMMARY
          Range  = 2.7314 A <--> 5.9325 A
          Mean   = 4.0997 A
          StdDev = 0.9529 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.070 deg ; T1  -- T1   2.8018 A

T1  -- O2  -- T1  = 127.209 deg ; T1  -- T1   2.9005 A

T1  -- O3  -- T2  = 114.539 deg ; T1  -- T2   2.7314 A

T1  -- O4  -- T2  = 121.986 deg ; T1  -- T2   2.8272 A

T2  -- O5  -- T2  = 153.676 deg ; T2  -- T2   3.2727 A

T2  -- O6  -- T2  = 110.790 deg ; T2  -- T2   2.7606 A


        T-O-T SUMMARY
          Range  = 110.7896° <--> 153.6764 deg
          Mean   = 124.8783 deg
          StdDev = 13.9956 deg

        T--T SUMMARY
          Range  = 2.7314 A <--> 3.2727 A
          Mean   = 2.8824 A
          StdDev = 0.1835 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7314 Angstrom
T2  -- T1  = 2.7314 Angstrom
T2  -- T2  = 2.7606 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 7 11 19 30 48 74 94 121 152 195 224 264 312 380 414
TD10 = 561
Circuit symbol = 3.4.3.6.4.5
Weight = 6
Vertex symbol  = 3.4.3.14_{2}.6_{2}.*
Weight = 30

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 20 31 50 75 100 125 160 200 229 267 316 369 411
TD10 = 587
Circuit symbol = 3.8_{2}.4.6_{2}.5.6_{2}
Weight = 10
Vertex symbol  = 3.14_{3}.4.6_{2}.6_{2}.14
Weight = 49

<TD10> = 574.000
Average ring size = 5.8049