Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_441396_L0SJIv.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 22.71 T-atoms per nm^3
Material density = 2.266 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6258 Angstrom
T1  -- O2  = 1.6577 Angstrom
T1  -- O3  = 1.6284 Angstrom
T1  -- O4  = 1.6408 Angstrom
      mean = 1.6382 Angstrom
        t1 = 0.051565  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063145  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6370 Angstrom
T2  -- O5  = 1.6333 Angstrom
T2  -- O6  = 1.6446 Angstrom
T2  -- O3  = 1.5787 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.051593  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034135  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5787 A <--> 1.6577 A
          Mean   = 1.6308 A
          StdDev = 0.0219 A

       t1 Range  = 0.0516 <-- 0.0516 --> 0.0516
       t2 Range  = 0.0341 <-- 0.0486 --> 0.0631

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 117.946 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  96.919 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 103.240 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.598 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.992 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 115.469 deg; O3  -- O4  = 3 A
       96.919 deg <-- 109.361 deg --> 117.946 deg

O4  -- T2  -- O5  = 115.569 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.913 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 104.025 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 119.223 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  =  98.400 deg; O5  -- O3  = 2 A
O6  -- T2  -- O3  = 107.510 deg; O6  -- O3  = 3 A
       98.400 deg <-- 109.107 deg --> 119.223 deg

        O-T-O SUMMARY
          Range  = 96.9185 deg <--> 119.2232 deg
          Mean   = 108.3836 deg
          StdDev = 6.7822 deg

        O--O SUMMARY
          Range  = 2.4317 A <--> 2.8275 A
          Mean   = 2.6398 A
          StdDev = 0.1292 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  60.301 deg; T2  -- T1  = 2.7929 A
T2  - O1  - T1  - O3  - T2  = 111.923 deg; T2  -- T2  = 4.6011 A
T2  - O1  - T1  - O4  - T1  = 127.266 deg; T2  -- T1  = 5.4117 A
T1  - O2  - T1  - O3  - T2  =  59.123 deg; T1  -- T2  = 2.7596 A
T1  - O2  - T1  - O4  - T1  = 149.404 deg; T1  -- T1  = 5.8616 A
T2  - O3  - T1  - O4  - T1  = 120.556 deg; T2  -- T1  = 5.2751 A

T1  - O4  - T2  - O5  - T2  = 106.619 deg; T1  -- T2  = 4.4108 A
T1  - O4  - T2  - O6  - T2  =  91.476 deg; T1  -- T2  = 4.2575 A
T1  - O4  - T2  - O3  - T1  =  60.576 deg; T1  -- T1  = 2.8005 A
T2  - O5  - T2  - O6  - T2  = 144.262 deg; T2  -- T2  = 5.6291 A
T2  - O5  - T2  - O3  - T1  = 122.803 deg; T2  -- T1  = 4.8588 A
T2  - O6  - T2  - O3  - T1  =  92.903 deg; T2  -- T1  = 4.3310 A

        T-T-T SUMMARY
          Range  = 59.1235 deg <--> 149.4036 deg
          Mean   = 104.0845 deg
          StdDev = 29.0731 deg

        T--T SUMMARY
          Range  = 2.7596 A <--> 5.8616 A
          Mean   = 4.4344 A
          StdDev = 1.0247 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 118.913 deg ; T1  -- T1   2.8005 A

T1  -- O2  -- T1  = 162.112 deg ; T1  -- T1   3.2750 A

T1  -- O3  -- T2  = 121.106 deg ; T1  -- T2   2.7929 A

T1  -- O4  -- T2  = 114.682 deg ; T1  -- T2   2.7596 A

T2  -- O5  -- T2  = 114.093 deg ; T2  -- T2   2.7410 A

T2  -- O6  -- T2  = 149.295 deg ; T2  -- T2   3.1717 A


        T-O-T SUMMARY
          Range  = 114.0929° <--> 162.1120 deg
          Mean   = 130.0336 deg
          StdDev = 18.7757 deg

        T--T SUMMARY
          Range  = 2.7410 A <--> 3.2750 A
          Mean   = 2.9235 A
          StdDev = 0.2162 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7596 Angstrom
T1  -- T2  = 2.7929 Angstrom
T2  -- T1  = 2.7596 Angstrom
T2  -- T2  = 2.7410 Angstrom
T2  -- T1  = 2.7929 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 20 37 57 92 129 168 217 278 331 396 466 546 627 713
TD10 = 1011
Circuit symbol = 3.8.3.8_{5}.4.9_{6}
Weight = 23
Vertex symbol  = 3.8.3.8_{5}.8_{2}.*
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 20 38 60 90 125 172 220 272 333 401 466 545 627 718
TD10 = 1011
Circuit symbol = 3.8_{2}.8.8_{4}.8_{2}.8_{3}
Weight = 29
Vertex symbol  = 3.8_{2}.8.8_{4}.8_{2}.8_{3}
Weight = 29

<TD10> = 1011.000
Average ring size = 6.5714