Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_421617_h1iVNk.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 21.91 T-atoms per nm^3
Material density = 2.186 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5927 Angstrom
T1  -- O2  = 1.6196 Angstrom
T1  -- O4  = 1.6392 Angstrom
T1  -- O3  = 1.6503 Angstrom
      mean = 1.6254 Angstrom
        t1 = 0.036040  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024549  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6533 Angstrom
T2  -- O5  = 1.5982 Angstrom
T2  -- O6  = 1.6091 Angstrom
T2  -- O4  = 1.6350 Angstrom
      mean = 1.6239 Angstrom
        t1 = 0.036574  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025876  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5927 A <--> 1.6533 A
          Mean   = 1.6247 A
          StdDev = 0.0218 A

       t1 Range  = 0.0360 <-- 0.0363 --> 0.0366
       t2 Range  = 0.0245 <-- 0.0252 --> 0.0259

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 102.089 deg; O1  -- O2  = 2 A
O1  -- T1  -- O4  = 107.409 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 106.569 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 112.684 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 116.282 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 110.861 deg; O4  -- O3  = 3 A
       102.089 deg <-- 109.316 deg --> 116.282 deg

O3  -- T2  -- O5  = 114.541 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 111.948 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 107.848 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  =  99.672 deg; O5  -- O6  = 2 A
O5  -- T2  -- O4  = 109.817 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 112.982 deg; O6  -- O4  = 3 A
       99.672 deg <-- 109.468 deg --> 114.541 deg

        O-T-O SUMMARY
          Range  = 99.6718 deg <--> 116.2819 deg
          Mean   = 110.1656 deg
          StdDev = 4.1480 deg

        O--O SUMMARY
          Range  = 2.4510 A <--> 2.7773 A
          Mean   = 2.6660 A
          StdDev = 0.0800 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 143.985 deg; T1  -- T2  = 5.7701 A
T1  - O1  - T1  - O4  - T1  = 129.819 deg; T1  -- T1  = 5.2909 A
T1  - O1  - T1  - O3  - T2  = 120.002 deg; T1  -- T2  = 5.2799 A
T2  - O2  - T1  - O4  - T1  =  63.242 deg; T2  -- T1  = 2.9535 A
T2  - O2  - T1  - O3  - T2  =  95.937 deg; T2  -- T2  = 4.3662 A
T1  - O4  - T1  - O3  - T2  =  62.156 deg; T1  -- T2  = 2.9247 A

T2  - O3  - T2  - O5  - T1  = 125.112 deg; T2  -- T1  = 5.4336 A
T2  - O3  - T2  - O6  - T1  = 128.029 deg; T2  -- T1  = 5.5291 A
T2  - O3  - T2  - O4  - T2  = 103.636 deg; T2  -- T2  = 4.8140 A
T1  - O5  - T2  - O6  - T1  =  54.602 deg; T1  -- T1  = 2.6962 A
T1  - O5  - T2  - O4  - T2  = 130.134 deg; T1  -- T2  = 5.3039 A
T1  - O6  - T2  - O4  - T2  = 104.759 deg; T1  -- T2  = 4.6556 A

        T-T-T SUMMARY
          Range  = 54.6019 deg <--> 143.9847 deg
          Mean   = 105.6472 deg
          StdDev = 27.2071 deg

        T--T SUMMARY
          Range  = 2.6962 A <--> 5.7701 A
          Mean   = 4.6168 A
          StdDev = 1.0078 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 115.655 deg ; T1  -- T1   2.6962 A

T1  -- O2  -- T1  = 151.890 deg ; T1  -- T1   3.1422 A

T1  -- O3  -- T2  = 126.765 deg ; T1  -- T2   2.9535 A

T1  -- O4  -- T2  = 126.572 deg ; T1  -- T2   2.9247 A

T2  -- O5  -- T2  = 179.450 deg ; T2  -- T2   3.1963 A

T2  -- O6  -- T2  = 130.639 deg ; T2  -- T2   2.9243 A


        T-O-T SUMMARY
          Range  = 115.6551° <--> 179.4498 deg
          Mean   = 138.4951 deg
          StdDev = 21.4029 deg

        T--T SUMMARY
          Range  = 2.6962 A <--> 3.1963 A
          Mean   = 2.9729 A
          StdDev = 0.1642 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6962 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 19 36 67 101 136 193 243 286 355 431 495 574 664 757
TD10 = 1094
Circuit symbol = 3.6.3.8.4.7
Weight = 8
Vertex symbol  = 3.6.3.10.10_{2}.11_{2}
Weight = 27

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 34 68 100 138 189 239 292 360 415 503 574 658 761
TD10 = 1092
Circuit symbol = 3.6.6.10_{2}.7.10_{4}
Weight = 23
Vertex symbol  = 3.6.6.10_{2}.10.10_{3}
Weight = 29

<TD10> = 1093.000
Average ring size = 6.5845