Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_420909_rL1i7E.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.80 T-atoms per nm^3
Material density = 1.975 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5469 Angstrom
T1  -- O2  = 1.5652 Angstrom
T1  -- O3  = 1.6296 Angstrom
T1  -- O4  = 1.6336 Angstrom
      mean = 1.5938 Angstrom
        t1 = 0.076277  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.088430  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6877 Angstrom
T2  -- O4  = 1.6604 Angstrom
T2  -- O5  = 1.6270 Angstrom
T2  -- O6  = 1.7186 Angstrom
      mean = 1.6734 Angstrom
        t1 = 0.065288  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032927  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5469 A <--> 1.7186 A
          Mean   = 1.6336 A
          StdDev = 0.0540 A

       t1 Range  = 0.0653 <-- 0.0708 --> 0.0763
       t2 Range  = 0.0329 <-- 0.0607 --> 0.0884

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.384 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  91.994 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 108.903 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.704 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 103.495 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 129.590 deg; O3  -- O4  = 3 A
       91.994 deg <-- 109.345 deg --> 129.590 deg

O3  -- T2  -- O4  = 102.843 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 110.210 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 116.753 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 102.840 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 120.332 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 102.921 deg; O5  -- O6  = 3 A
       102.840 deg <-- 109.316 deg --> 120.332 deg

        O-T-O SUMMARY
          Range  = 91.9939 deg <--> 129.5896 deg
          Mean   = 109.5287 deg
          StdDev = 9.7062 deg

        O--O SUMMARY
          Range  = 2.2856 A <--> 2.9525 A
          Mean   = 2.6636 A
          StdDev = 0.1920 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 129.042 deg; T1  -- T1  = 5.3638 A
T1  - O1  - T1  - O3  - T2  =  89.400 deg; T1  -- T2  = 4.1229 A
T1  - O1  - T1  - O4  - T2  =  76.829 deg; T1  -- T2  = 3.7549 A
T1  - O2  - T1  - O3  - T2  =  92.242 deg; T1  -- T2  = 3.9903 A
T1  - O2  - T1  - O4  - T2  =  98.260 deg; T1  -- T2  = 4.3298 A
T2  - O3  - T1  - O4  - T2  = 166.023 deg; T2  -- T2  = 5.5906 A

T1  - O3  - T2  - O4  - T1  = 135.604 deg; T1  -- T1  = 5.2154 A
T1  - O3  - T2  - O5  - T2  =  77.306 deg; T1  -- T2  = 3.7549 A
T1  - O3  - T2  - O6  - T2  = 105.983 deg; T1  -- T2  = 4.7173 A
T1  - O4  - T2  - O5  - T2  =  83.751 deg; T1  -- T2  = 4.1229 A
T1  - O4  - T2  - O6  - T2  = 110.974 deg; T1  -- T2  = 5.0182 A
T2  - O5  - T2  - O6  - T2  =  82.722 deg; T2  -- T2  = 4.2491 A

        T-T-T SUMMARY
          Range  = 76.8287 deg <--> 166.0232 deg
          Mean   = 103.8412 deg
          StdDev = 26.5039 deg

        T--T SUMMARY
          Range  = 3.7549 A <--> 5.5906 A
          Mean   = 4.4930 A
          StdDev = 0.6126 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.880 deg ; T1  -- T1   2.8139 A

T1  -- O2  -- T1  = 173.780 deg ; T1  -- T1   3.1259 A

T1  -- O3  -- T2  = 110.220 deg ; T1  -- T2   2.7212 A

T1  -- O4  -- T2  = 124.206 deg ; T1  -- T2   2.9112 A

T2  -- O5  -- T2  = 177.728 deg ; T2  -- T2   3.2534 A

T2  -- O6  -- T2  = 135.056 deg ; T2  -- T2   3.1762 A


        T-O-T SUMMARY
          Range  = 110.2203° <--> 177.7277 deg
          Mean   = 141.9784 deg
          StdDev = 25.2477 deg

        T--T SUMMARY
          Range  = 2.7212 A <--> 3.2534 A
          Mean   = 3.0003 A
          StdDev = 0.1974 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.2856 A
O1  -- O3  = 2.2856 A
T1  -- T2  = 2.7212 Angstrom
T2  -- T1  = 2.7212 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 16 27 46 76 102 124 161 212 242 285 343 409 454 510
TD10 = 779
Circuit symbol = 4.5_{3}.4.7.5.6
Weight = 10
Vertex symbol  = 4.5_{3}.4.13_{23}.5.13_{4}
Weight = 59

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 15 26 43 73 98 123 161 205 242 282 339 408 446 510
TD10 = 758
Circuit symbol = 4.5.4.5_{2}.4.6
Weight = 11
Vertex symbol  = 4.5.4.5_{2}.4.13_{13}
Weight = 47

<TD10> = 768.500
Average ring size = 9.0799