Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_420906_KNAZfA.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 25.69 T-atoms per nm^3
Material density = 2.563 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5658 Angstrom
T1  -- O2  = 1.6260 Angstrom
T1  -- O3  = 1.6115 Angstrom
T1  -- O4  = 1.6170 Angstrom
      mean = 1.6051 Angstrom
        t1 = 0.065886  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.091868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6725 Angstrom
T2  -- O4  = 1.6116 Angstrom
T2  -- O5  = 1.6646 Angstrom
T2  -- O6  = 1.6748 Angstrom
      mean = 1.6559 Angstrom
        t1 = 0.063390  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038922  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5658 A <--> 1.6748 A
          Mean   = 1.6305 A
          StdDev = 0.0355 A

       t1 Range  = 0.0634 <-- 0.0646 --> 0.0659
       t2 Range  = 0.0389 <-- 0.0654 --> 0.0919

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 115.715 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  91.267 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 104.329 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.693 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.758 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 119.452 deg; O3  -- O4  = 3 A
       91.267 deg <-- 109.202 deg --> 119.452 deg

O3  -- T2  -- O4  =  94.959 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 111.907 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 121.108 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 115.729 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 106.855 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 106.313 deg; O5  -- O6  = 3 A
       94.959 deg <-- 109.478 deg --> 121.108 deg

        O-T-O SUMMARY
          Range  = 91.2673 deg <--> 121.1078 deg
          Mean   = 109.1883 deg
          StdDev = 9.0634 deg

        O--O SUMMARY
          Range  = 2.2716 A <--> 2.9149 A
          Mean   = 2.6505 A
          StdDev = 0.1758 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 131.350 deg; T1  -- T1  = 5.3865 A
T1  - O1  - T1  - O3  - T2  = 113.104 deg; T1  -- T2  = 5.0774 A
T1  - O1  - T1  - O4  - T2  =  87.597 deg; T1  -- T2  = 4.3266 A
T1  - O2  - T1  - O3  - T2  =  80.915 deg; T1  -- T2  = 3.6415 A
T1  - O2  - T1  - O4  - T2  =  85.362 deg; T1  -- T2  = 3.9237 A
T2  - O3  - T1  - O4  - T2  = 159.299 deg; T2  -- T2  = 5.8537 A

T1  - O3  - T2  - O4  - T2  = 120.869 deg; T1  -- T2  = 5.1574 A
T1  - O3  - T2  - O5  - T1  =  96.149 deg; T1  -- T1  = 4.4287 A
T1  - O3  - T2  - O6  - T2  = 112.714 deg; T1  -- T2  = 5.0589 A
T2  - O4  - T2  - O5  - T1  = 142.934 deg; T2  -- T1  = 5.7805 A
T2  - O4  - T2  - O6  - T2  =  77.513 deg; T2  -- T2  = 3.8953 A
T1  - O5  - T2  - O6  - T2  =  90.626 deg; T1  -- T2  = 4.4382 A

        T-T-T SUMMARY
          Range  = 77.5126 deg <--> 159.2993 deg
          Mean   = 107.9494 deg
          StdDev = 25.6957 deg

        T--T SUMMARY
          Range  = 3.6415 A <--> 5.8537 A
          Mean   = 4.7324 A
          StdDev = 0.7295 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.354 deg ; T1  -- T1   2.7169 A

T1  -- O2  -- T1  = 157.676 deg ; T1  -- T1   3.1906 A

T1  -- O3  -- T2  = 123.381 deg ; T1  -- T2   2.8914 A

T1  -- O4  -- T2  = 142.708 deg ; T1  -- T2   3.0591 A

T2  -- O5  -- T2  = 131.670 deg ; T2  -- T2   3.0375 A

T2  -- O6  -- T2  = 143.627 deg ; T2  -- T2   3.1823 A


        T-O-T SUMMARY
          Range  = 120.3541° <--> 157.6761 deg
          Mean   = 136.5694 deg
          StdDev = 12.9378 deg

        T--T SUMMARY
          Range  = 2.7169 A <--> 3.1906 A
          Mean   = 3.0130 A
          StdDev = 0.1669 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.2716 A
O1  -- O3  = 2.2716 A
T1  -- T1  = 2.7169 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 23 40 75 110 147 197 256 309 382 462 535 618 734 823
TD10 = 1174
Circuit symbol = 5.5_{2}.5.6.5.8_{4}
Weight = 17
Vertex symbol  = 5.5_{2}.5.6.5.10
Weight = 21

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 24 44 79 111 150 201 260 317 384 470 541 630 733 832
TD10 = 1203
Circuit symbol = 5.5_{2}.5.6.5.8_{3}
Weight = 16
Vertex symbol  = 5.5_{2}.5.6.5.10_{3}
Weight = 25

<TD10> = 1188.500
Average ring size = 5.8537