Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_355979_Vg936X.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.08 T-atoms per nm^3
Material density = 1.904 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6299 Angstrom
T1  -- O2  = 1.6685 Angstrom
T1  -- O3  = 1.5980 Angstrom
T1  -- O4  = 1.6096 Angstrom
      mean = 1.6265 Angstrom
        t1 = 0.040843  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040603  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5807 Angstrom
T2  -- O4  = 1.6104 Angstrom
T2  -- O5  = 1.6166 Angstrom
T2  -- O6  = 1.6216 Angstrom
      mean = 1.6073 Angstrom
        t1 = 0.015781  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018175  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5807 A <--> 1.6685 A
          Mean   = 1.6169 A
          StdDev = 0.0241 A

       t1 Range  = 0.0158 <-- 0.0283 --> 0.0408
       t2 Range  = 0.0182 <-- 0.0294 --> 0.0406

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 120.459 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 102.587 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.556 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.233 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.076 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.945 deg; O3  -- O4  = 3 A
       102.587 deg <-- 109.476 deg --> 120.459 deg

O3  -- T2  -- O4  = 107.510 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 106.453 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.867 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 110.886 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 111.029 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.976 deg; O5  -- O6  = 3 A
       106.453 deg <-- 109.453 deg --> 111.029 deg

        O-T-O SUMMARY
          Range  = 102.5871 deg <--> 120.4585 deg
          Mean   = 108.9418 deg
          StdDev = 3.6537 deg

        O--O SUMMARY
          Range  = 2.5190 A <--> 2.8632 A
          Mean   = 2.6281 A
          StdDev = 0.0688 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 108.721 deg; T2  -- T1  = 5.0450 A
T2  - O1  - T1  - O3  - T1  =  93.255 deg; T2  -- T1  = 4.1971 A
T2  - O1  - T1  - O4  - T2  =  92.336 deg; T2  -- T2  = 4.4560 A
T1  - O2  - T1  - O3  - T1  = 153.098 deg; T1  -- T1  = 5.9018 A
T1  - O2  - T1  - O4  - T2  = 108.051 deg; T1  -- T2  = 5.2336 A
T1  - O3  - T1  - O4  - T2  =  85.686 deg; T1  -- T2  = 4.1143 A

T1  - O3  - T2  - O4  - T2  =  92.092 deg; T1  -- T2  = 4.1143 A
T1  - O3  - T2  - O5  - T2  = 147.241 deg; T1  -- T2  = 5.6421 A
T1  - O3  - T2  - O6  - T1  =  87.656 deg; T1  -- T1  = 4.2783 A
T2  - O4  - T2  - O5  - T2  = 120.225 deg; T2  -- T2  = 4.9284 A
T2  - O4  - T2  - O6  - T1  =  88.903 deg; T2  -- T1  = 4.1971 A
T2  - O5  - T2  - O6  - T1  =  97.468 deg; T2  -- T1  = 4.6218 A

        T-T-T SUMMARY
          Range  = 85.6855 deg <--> 153.0978 deg
          Mean   = 106.5125 deg
          StdDev = 22.9222 deg

        T--T SUMMARY
          Range  = 4.1143 A <--> 5.9018 A
          Mean   = 4.7179 A
          StdDev = 0.6165 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 170.878 deg ; T1  -- T1   3.2495 A

T1  -- O2  -- T1  = 115.221 deg ; T1  -- T1   2.8179 A

T1  -- O3  -- T2  = 136.716 deg ; T1  -- T2   2.9546 A

T1  -- O4  -- T2  = 175.353 deg ; T1  -- T2   3.2174 A

T2  -- O5  -- T2  = 117.043 deg ; T2  -- T2   2.7575 A

T2  -- O6  -- T2  = 128.906 deg ; T2  -- T2   2.9262 A


        T-O-T SUMMARY
          Range  = 115.2213° <--> 175.3529 deg
          Mean   = 140.6862 deg
          StdDev = 24.1933 deg

        T--T SUMMARY
          Range  = 2.7575 A <--> 3.2495 A
          Mean   = 2.9872 A
          StdDev = 0.1872 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7575 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 33 51 72 100 132 168 211 259 310 365 427 492 561
TD10 = 799
Circuit symbol = 4.6.4.8.4.8
Weight = 11
Vertex symbol  = 4.6.4.10_{8}.4.10_{11}
Weight = 44

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 17 31 51 71 95 131 169 203 250 314 372 423 487 563
TD10 = 782
Circuit symbol = 4.6.4.6.4.8_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.10_{7}
Weight = 29

<TD10> = 790.500
Average ring size = 7.6087