Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_355562_j0PL2C.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 20.59 T-atoms per nm^3
Material density = 2.054 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6449 Angstrom
T1  -- O2  = 1.6387 Angstrom
T1  -- O3  = 1.5719 Angstrom
T1  -- O4  = 1.6332 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.034714  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021764  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6189 Angstrom
T2  -- O4  = 1.6413 Angstrom
T2  -- O5  = 1.5883 Angstrom
T2  -- O6  = 1.6137 Angstrom
      mean = 1.6155 Angstrom
        t1 = 0.027515  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024496  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5719 A <--> 1.6449 A
          Mean   = 1.6189 A
          StdDev = 0.0250 A

       t1 Range  = 0.0275 <-- 0.0311 --> 0.0347
       t2 Range  = 0.0218 <-- 0.0231 --> 0.0245

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.396 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.678 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.454 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 104.432 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 113.373 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 103.765 deg; O3  -- O4  = 3 A
       103.765 deg <-- 109.350 deg --> 113.373 deg

O3  -- T2  -- O4  = 114.347 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 106.148 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 106.650 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 105.766 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 114.119 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.483 deg; O5  -- O6  = 3 A
       105.766 deg <-- 109.419 deg --> 114.347 deg

        O-T-O SUMMARY
          Range  = 103.7651 deg <--> 114.3465 deg
          Mean   = 109.2428 deg
          StdDev = 3.8714 deg

        O--O SUMMARY
          Range  = 2.5219 A <--> 2.7396 A
          Mean   = 2.6386 A
          StdDev = 0.0830 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  75.633 deg; T2  -- T2  = 3.6281 A
T2  - O1  - T1  - O3  - T1  = 134.161 deg; T2  -- T1  = 5.4257 A
T2  - O1  - T1  - O4  - T1  =  84.832 deg; T2  -- T1  = 4.0326 A
T2  - O2  - T1  - O3  - T1  = 117.598 deg; T2  -- T1  = 5.4886 A
T2  - O2  - T1  - O4  - T1  = 112.978 deg; T2  -- T1  = 5.3975 A
T1  - O3  - T1  - O4  - T1  = 121.449 deg; T1  -- T1  = 5.6542 A

T1  - O3  - T2  - O4  - T1  =  73.954 deg; T1  -- T1  = 3.5607 A
T1  - O3  - T2  - O5  - T2  = 120.589 deg; T1  -- T2  = 5.1217 A
T1  - O3  - T2  - O6  - T2  = 128.362 deg; T1  -- T2  = 5.1710 A
T1  - O4  - T2  - O5  - T2  = 114.120 deg; T1  -- T2  = 5.3870 A
T1  - O4  - T2  - O6  - T2  = 126.713 deg; T1  -- T2  = 5.6061 A
T2  - O5  - T2  - O6  - T2  =  94.997 deg; T2  -- T2  = 4.6329 A

        T-T-T SUMMARY
          Range  = 73.9535 deg <--> 134.1609 deg
          Mean   = 110.9155 deg
          StdDev = 19.4874 deg

        T--T SUMMARY
          Range  = 3.5607 A <--> 5.6542 A
          Mean   = 4.9978 A
          StdDev = 0.7144 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 155.136 deg ; T1  -- T1   3.2127 A

T1  -- O2  -- T1  = 171.915 deg ; T1  -- T1   3.2693 A

T1  -- O3  -- T2  = 113.836 deg ; T1  -- T2   2.6737 A

T1  -- O4  -- T2  = 156.187 deg ; T1  -- T2   3.2041 A

T2  -- O5  -- T2  = 149.898 deg ; T2  -- T2   3.0677 A

T2  -- O6  -- T2  = 169.863 deg ; T2  -- T2   3.2148 A


        T-O-T SUMMARY
          Range  = 113.8359° <--> 171.9147 deg
          Mean   = 152.8058 deg
          StdDev = 19.2493 deg

        T--T SUMMARY
          Range  = 2.6737 A <--> 3.2693 A
          Mean   = 3.1070 A
          StdDev = 0.2043 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.6737 Angstrom
T2  -- T1  = 2.6737 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 25 45 69 100 143 189 235 285 349 419 499 563 649 739
TD10 = 1107
Circuit symbol = 4.6.6_{2}.8_{3}.6_{3}.8_{3}
Weight = 31
Vertex symbol  = 4.6.6_{2}.8_{2}.6_{3}.8_{2}
Weight = 31

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 44 68 102 141 176 223 293 353 413 481 559 648 743
TD10 = 1085
Circuit symbol = 4.5_{2}.5.6.5.8_{6}
Weight = 20
Vertex symbol  = 4.5_{2}.5.6.5.8
Weight = 17

<TD10> = 1096.000
Average ring size = 5.8221