Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_355527_OxCmnB.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 21.75 T-atoms per nm^3
Material density = 2.170 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6324 Angstrom
T1  -- O2  = 1.6366 Angstrom
T1  -- O3  = 1.5493 Angstrom
T1  -- O4  = 1.5920 Angstrom
      mean = 1.6026 Angstrom
        t1 = 0.047543  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044946  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6170 Angstrom
T2  -- O5  = 1.6335 Angstrom
T2  -- O6  = 1.6680 Angstrom
T2  -- O4  = 1.6681 Angstrom
      mean = 1.6466 Angstrom
        t1 = 0.051160  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029052  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5493 A <--> 1.6681 A
          Mean   = 1.6246 A
          StdDev = 0.0370 A

       t1 Range  = 0.0475 <-- 0.0494 --> 0.0512
       t2 Range  = 0.0291 <-- 0.0370 --> 0.0449

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 122.052 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 102.030 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 102.595 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.195 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.985 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.430 deg; O3  -- O4  = 3 A
       102.030 deg <-- 109.381 deg --> 122.052 deg

O3  -- T2  -- O5  =  97.031 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 109.003 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 110.795 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 118.754 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 112.051 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 108.597 deg; O6  -- O4  = 3 A
       97.031 deg <-- 109.372 deg --> 118.754 deg

        O-T-O SUMMARY
          Range  = 97.0308 deg <--> 122.0516 deg
          Mean   = 108.3739 deg
          StdDev = 5.8714 deg

        O--O SUMMARY
          Range  = 2.4351 A <--> 2.8598 A
          Mean   = 2.6294 A
          StdDev = 0.1184 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  58.935 deg; T2  -- T1  = 2.7342 A
T2  - O1  - T1  - O3  - T2  = 107.391 deg; T2  -- T2  = 4.3666 A
T2  - O1  - T1  - O4  - T1  = 125.316 deg; T2  -- T1  = 5.2691 A
T1  - O2  - T1  - O3  - T2  =  57.234 deg; T1  -- T2  = 2.6841 A
T1  - O2  - T1  - O4  - T1  = 151.111 deg; T1  -- T1  = 5.9133 A
T2  - O3  - T1  - O4  - T1  = 127.234 deg; T2  -- T1  = 5.3573 A

T1  - O3  - T2  - O5  - T2  = 126.220 deg; T1  -- T2  = 4.9264 A
T1  - O3  - T2  - O6  - T1  =  63.832 deg; T1  -- T1  = 2.8648 A
T1  - O3  - T2  - O4  - T2  =  94.898 deg; T1  -- T2  = 4.4228 A
T2  - O5  - T2  - O6  - T1  = 108.075 deg; T2  -- T1  = 4.5113 A
T2  - O5  - T2  - O4  - T2  = 138.399 deg; T2  -- T2  = 5.7350 A
T1  - O6  - T2  - O4  - T2  =  94.681 deg; T1  -- T2  = 4.4490 A

        T-T-T SUMMARY
          Range  = 57.2336 deg <--> 151.1108 deg
          Mean   = 106.3473 deg
          StdDev = 29.9875 deg

        T--T SUMMARY
          Range  = 2.6841 A <--> 5.9133 A
          Mean   = 4.5101 A
          StdDev = 1.0727 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 122.689 deg ; T1  -- T1   2.8648 A

T1  -- O2  -- T1  = 163.832 deg ; T1  -- T1   3.2407 A

T1  -- O3  -- T2  = 115.911 deg ; T1  -- T2   2.6841 A

T1  -- O4  -- T2  = 113.985 deg ; T1  -- T2   2.7342 A

T2  -- O5  -- T2  = 120.684 deg ; T2  -- T2   2.8389 A

T2  -- O6  -- T2  = 161.694 deg ; T2  -- T2   3.2935 A


        T-O-T SUMMARY
          Range  = 113.9846° <--> 163.8323 deg
          Mean   = 133.1325 deg
          StdDev = 21.2673 deg

        T--T SUMMARY
          Range  = 2.6841 A <--> 3.2935 A
          Mean   = 2.9427 A
          StdDev = 0.2390 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.6841 Angstrom
T1  -- T2  = 2.7342 Angstrom
T2  -- T1  = 2.6841 Angstrom
T2  -- T1  = 2.7342 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 20 37 57 92 129 168 217 278 331 396 466 546 627 713
TD10 = 1011
Circuit symbol = 3.8.3.8_{5}.4.9_{6}
Weight = 23
Vertex symbol  = 3.8.3.8_{5}.8_{2}.*
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 20 38 60 90 125 172 220 272 333 401 466 545 627 718
TD10 = 1011
Circuit symbol = 3.8_{2}.8.8_{4}.8_{2}.8_{3}
Weight = 29
Vertex symbol  = 3.8_{2}.8.8_{4}.8_{2}.8_{3}
Weight = 29

<TD10> = 1011.000
Average ring size = 6.5714