Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_351034_e2Pzp3.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 21.76 T-atoms per nm^3
Material density = 2.171 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5932 Angstrom
T1  -- O2  = 1.6100 Angstrom
T1  -- O4  = 1.6366 Angstrom
T1  -- O3  = 1.6507 Angstrom
      mean = 1.6226 Angstrom
        t1 = 0.033889  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023186  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6547 Angstrom
T2  -- O5  = 1.6070 Angstrom
T2  -- O6  = 1.6090 Angstrom
T2  -- O4  = 1.6344 Angstrom
      mean = 1.6263 Angstrom
        t1 = 0.037428  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025417  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5932 A <--> 1.6547 A
          Mean   = 1.6244 A
          StdDev = 0.0212 A

       t1 Range  = 0.0339 <-- 0.0357 --> 0.0374
       t2 Range  = 0.0232 <-- 0.0243 --> 0.0254

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 102.486 deg; O1  -- O2  = 2 A
O1  -- T1  -- O4  = 107.463 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 106.939 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 111.449 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 115.717 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 111.916 deg; O4  -- O3  = 3 A
       102.486 deg <-- 109.329 deg --> 115.717 deg

O3  -- T2  -- O5  = 115.588 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 111.732 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 106.850 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  =  99.690 deg; O5  -- O6  = 2 A
O5  -- T2  -- O4  = 110.170 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 112.900 deg; O6  -- O4  = 3 A
       99.690 deg <-- 109.488 deg --> 115.588 deg

        O-T-O SUMMARY
          Range  = 99.6900 deg <--> 115.7174 deg
          Mean   = 110.1648 deg
          StdDev = 4.1451 deg

        O--O SUMMARY
          Range  = 2.4580 A <--> 2.7610 A
          Mean   = 2.6655 A
          StdDev = 0.0788 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 119.798 deg; T1  -- T2  = 5.2702 A
T1  - O1  - T1  - O4  - T1  = 131.000 deg; T1  -- T1  = 5.2827 A
T1  - O1  - T1  - O3  - T2  = 144.154 deg; T1  -- T2  = 5.7587 A
T2  - O2  - T1  - O4  - T1  =  62.248 deg; T2  -- T1  = 2.9246 A
T2  - O2  - T1  - O3  - T2  =  96.047 deg; T2  -- T2  = 4.3774 A
T1  - O4  - T1  - O3  - T2  =  63.734 deg; T1  -- T2  = 2.9635 A

T2  - O3  - T2  - O5  - T1  = 125.453 deg; T2  -- T1  = 5.4566 A
T2  - O3  - T2  - O6  - T2  = 102.958 deg; T2  -- T2  = 4.8196 A
T2  - O3  - T2  - O4  - T1  = 128.203 deg; T2  -- T1  = 5.5570 A
T1  - O5  - T2  - O6  - T2  = 130.573 deg; T1  -- T2  = 5.3310 A
T1  - O5  - T2  - O4  - T1  =  54.018 deg; T1  -- T1  = 2.6742 A
T2  - O6  - T2  - O4  - T1  = 105.138 deg; T2  -- T1  = 4.6910 A

        T-T-T SUMMARY
          Range  = 54.0183 deg <--> 144.1537 deg
          Mean   = 103.4670 deg
          StdDev = 29.9187 deg

        T--T SUMMARY
          Range  = 2.6742 A <--> 5.7587 A
          Mean   = 4.5278 A
          StdDev = 1.0982 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.127 deg ; T1  -- T1   2.6742 A

T1  -- O2  -- T1  = 152.472 deg ; T1  -- T1   3.1275 A

T1  -- O3  -- T2  = 127.423 deg ; T1  -- T2   2.9635 A

T1  -- O4  -- T2  = 126.787 deg ; T1  -- T2   2.9246 A

T2  -- O5  -- T2  = 176.655 deg ; T2  -- T2   3.2127 A

T2  -- O6  -- T2  = 132.358 deg ; T2  -- T2   2.9439 A


        T-O-T SUMMARY
          Range  = 114.1265° <--> 176.6549 deg
          Mean   = 138.3036 deg
          StdDev = 20.6932 deg

        T--T SUMMARY
          Range  = 2.6742 A <--> 3.2127 A
          Mean   = 2.9744 A
          StdDev = 0.1711 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6742 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 19 36 67 101 136 193 243 286 355 431 495 574 664 757
TD10 = 1094
Circuit symbol = 3.6.3.8.4.7
Weight = 8
Vertex symbol  = 3.6.3.10.10_{2}.11_{2}
Weight = 27

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 34 68 100 138 189 239 292 360 415 503 574 658 761
TD10 = 1092
Circuit symbol = 3.6.6.10_{2}.7.10_{4}
Weight = 23
Vertex symbol  = 3.6.6.10_{2}.10.10_{3}
Weight = 29

<TD10> = 1093.000
Average ring size = 6.5845