Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_350458_FbMOmB.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 24.74 T-atoms per nm^3
Material density = 2.469 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5975 Angstrom
T1  -- O2  = 1.6407 Angstrom
T1  -- O3  = 1.6595 Angstrom
T1  -- O4  = 1.6338 Angstrom
      mean = 1.6329 Angstrom
        t1 = 0.051694  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037600  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.5664 Angstrom
T2  -- O6  = 1.5844 Angstrom
T2  -- O4  = 1.6480 Angstrom
T2  -- O3  = 1.6374 Angstrom
      mean = 1.6090 Angstrom
        t1 = 0.051924  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039948  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5664 A <--> 1.6595 A
          Mean   = 1.6210 A
          StdDev = 0.0316 A

       t1 Range  = 0.0517 <-- 0.0518 --> 0.0519
       t2 Range  = 0.0376 <-- 0.0388 --> 0.0399

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.596 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.126 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  96.101 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 106.692 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 116.818 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 114.364 deg; O3  -- O4  = 3 A
       96.101 deg <-- 109.450 deg --> 116.818 deg

O5  -- T2  -- O6  = 111.646 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 103.691 deg; O5  -- O4  = 3 A
O5  -- T2  -- O3  = 102.761 deg; O5  -- O3  = 3 A
O6  -- T2  -- O4  = 107.853 deg; O6  -- O4  = 3 A
O6  -- T2  -- O3  = 105.657 deg; O6  -- O3  = 3 A
O4  -- T2  -- O3  = 125.001 deg; O4  -- O3  = 3 A
       102.761 deg <-- 109.435 deg --> 125.001 deg

        O-T-O SUMMARY
          Range  = 96.1011 deg <--> 125.0005 deg
          Mean   = 109.4259 deg
          StdDev = 7.6330 deg

        O--O SUMMARY
          Range  = 2.4033 A <--> 2.9142 A
          Mean   = 2.6448 A
          StdDev = 0.1417 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 122.429 deg; T1  -- T2  = 5.6115 A
T1  - O1  - T1  - O3  - T1  = 112.421 deg; T1  -- T1  = 5.3329 A
T1  - O1  - T1  - O4  - T2  = 135.901 deg; T1  -- T2  = 5.9103 A
T2  - O2  - T1  - O3  - T1  = 106.662 deg; T2  -- T1  = 5.0219 A
T2  - O2  - T1  - O4  - T2  =  92.959 deg; T2  -- T2  = 4.5111 A
T1  - O3  - T1  - O4  - T2  =  76.064 deg; T1  -- T2  = 3.8416 A

T2  - O5  - T2  - O6  - T1  = 132.323 deg; T2  -- T1  = 5.6105 A
T2  - O5  - T2  - O4  - T2  =  95.286 deg; T2  -- T2  = 4.5111 A
T2  - O5  - T2  - O3  - T1  =  85.891 deg; T2  -- T1  = 4.1970 A
T1  - O6  - T2  - O4  - T2  =  85.787 deg; T1  -- T2  = 4.1970 A
T1  - O6  - T2  - O3  - T1  = 139.273 deg; T1  -- T1  = 5.8324 A
T2  - O4  - T2  - O3  - T1  = 106.971 deg; T2  -- T1  = 4.9767 A

        T-T-T SUMMARY
          Range  = 76.0645 deg <--> 139.2732 deg
          Mean   = 105.8720 deg
          StdDev = 20.3264 deg

        T--T SUMMARY
          Range  = 3.8416 A <--> 5.9103 A
          Mean   = 4.9039 A
          StdDev = 0.6771 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.221 deg ; T1  -- T1   3.1374 A

T1  -- O2  -- T1  = 175.291 deg ; T1  -- T1   3.2787 A

T1  -- O3  -- T2  = 142.660 deg ; T1  -- T2   3.1235 A

T1  -- O4  -- T2  = 141.432 deg ; T1  -- T2   3.0977 A

T2  -- O5  -- T2  = 151.459 deg ; T2  -- T2   3.0361 A

T2  -- O6  -- T2  = 151.101 deg ; T2  -- T2   3.0685 A


        T-O-T SUMMARY
          Range  = 141.4324° <--> 175.2912 deg
          Mean   = 153.3608 deg
          StdDev = 11.3885 deg

        T--T SUMMARY
          Range  = 3.0361 A <--> 3.2787 A
          Mean   = 3.1236 A
          StdDev = 0.0774 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 41 73 115 155 200 253 307 370 443 519 605 698 790
TD10 = 1183
Circuit symbol = 4.6_{3}.6.8_{2}.6_{2}.10_{10}
Weight = 30
Vertex symbol  = 4.6_{3}.6.8_{2}.6_{2}.10_{4}
Weight = 30

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 20 43 73 107 152 197 245 309 375 442 520 601 687 787
TD10 = 1160
Circuit symbol = 4.4.4.8_{4}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8_{2}.6.10_{6}
Weight = 30

<TD10> = 1171.500
Average ring size = 6.8182