Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_98_2_195600_dOB6MK.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 18.27 T-atoms per nm^3
Material density = 1.823 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6130 Angstrom
T1  -- O2  = 1.6195 Angstrom
T1  -- O4  = 1.5834 Angstrom
T1  -- O3  = 1.6116 Angstrom
      mean = 1.6069 Angstrom
        t1 = 0.047086  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050259  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6321 Angstrom
T2  -- O4  = 1.6493 Angstrom
T2  -- O5  = 1.6838 Angstrom
T2  -- O6  = 1.6797 Angstrom
      mean = 1.6612 Angstrom
        t1 = 0.052283  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036921  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5834 A <--> 1.6838 A
          Mean   = 1.6341 A
          StdDev = 0.0328 A

       t1 Range  = 0.0471 <-- 0.0497 --> 0.0523
       t2 Range  = 0.0369 <-- 0.0436 --> 0.0503

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 120.389 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 100.150 deg; O1  -- O4  = 2 A
O1  -- T1  -- O3  = 103.527 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 104.233 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 112.375 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 116.164 deg; O4  -- O3  = 3 A
       100.150 deg <-- 109.473 deg --> 120.389 deg

O3  -- T2  -- O4  = 107.811 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 103.093 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.585 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 110.229 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.356 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 122.089 deg; O5  -- O6  = 3 A
       103.093 deg <-- 109.361 deg --> 122.089 deg

        O-T-O SUMMARY
          Range  = 100.1497 deg <--> 122.0891 deg
          Mean   = 108.3421 deg
          StdDev = 5.9910 deg

        O--O SUMMARY
          Range  = 2.4513 A <--> 2.9431 A
          Mean   = 2.6441 A
          StdDev = 0.1124 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 125.202 deg; T1  -- T1  = 5.0284 A
T1  - O1  - T1  - O4  - T2  =  87.347 deg; T1  -- T2  = 3.9219 A
T1  - O1  - T1  - O3  - T2  = 158.440 deg; T1  -- T2  = 5.5264 A
T1  - O2  - T1  - O4  - T2  =  58.926 deg; T1  -- T2  = 2.7782 A
T1  - O2  - T1  - O3  - T2  =  60.821 deg; T1  -- T2  = 2.8320 A
T2  - O4  - T1  - O3  - T2  = 110.676 deg; T2  -- T2  = 4.6146 A

T2  - O3  - T2  - O4  - T1  =  79.935 deg; T2  -- T1  = 3.9219 A
T2  - O3  - T2  - O5  - T2  = 160.805 deg; T2  -- T2  = 5.9578 A
T2  - O3  - T2  - O6  - T1  =  92.928 deg; T2  -- T1  = 4.3844 A
T1  - O4  - T2  - O5  - T2  = 105.280 deg; T1  -- T2  = 4.4678 A
T1  - O4  - T2  - O6  - T1  =  60.253 deg; T1  -- T1  = 2.8162 A
T2  - O5  - T2  - O6  - T1  = 105.750 deg; T2  -- T1  = 4.4388 A

        T-T-T SUMMARY
          Range  = 58.9262 deg <--> 160.8048 deg
          Mean   = 99.1716 deg
          StdDev = 34.4697 deg

        T--T SUMMARY
          Range  = 2.7782 A <--> 5.9578 A
          Mean   = 4.1777 A
          StdDev = 1.0234 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.608 deg ; T1  -- T1   2.8162 A

T1  -- O2  -- T1  = 123.075 deg ; T1  -- T1   2.8475 A

T1  -- O3  -- T2  = 117.847 deg ; T1  -- T2   2.7782 A

T1  -- O4  -- T2  = 122.324 deg ; T1  -- T2   2.8320 A

T2  -- O5  -- T2  = 149.999 deg ; T2  -- T2   3.2529 A

T2  -- O6  -- T2  = 112.239 deg ; T2  -- T2   2.7890 A


        T-O-T SUMMARY
          Range  = 112.2387° <--> 149.9990 deg
          Mean   = 124.5153 deg
          StdDev = 12.0345 deg

        T--T SUMMARY
          Range  = 2.7782 A <--> 3.2529 A
          Mean   = 2.8859 A
          StdDev = 0.1667 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7782 Angstrom
T2  -- T2  = 2.7890 Angstrom
T2  -- T1  = 2.7782 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 7 11 19 30 48 74 94 121 152 195 224 264 312 380 414
TD10 = 561
Circuit symbol = 3.4.3.6.4.5
Weight = 6
Vertex symbol  = 3.4.3.14_{2}.6_{2}.*
Weight = 30

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 20 31 50 75 100 125 160 200 229 267 316 369 411
TD10 = 587
Circuit symbol = 3.8_{2}.4.6_{2}.5.6_{2}
Weight = 10
Vertex symbol  = 3.14_{3}.4.6_{2}.6_{2}.14
Weight = 49

<TD10> = 574.000
Average ring size = 5.8049