Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_95a_1_74_c25Gty.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6164 Angstrom
T1  -- O3  = 1.7736 Angstrom
T1  -- O1  = 2.0296 Angstrom
T1  -- O1  = 1.5409 Angstrom
T1  -- O1  = 1.8055 Angstrom
      mean = 1.7532 Angstrom

        T-O SUMMARY
          Range  = 1.5409 A <--> 2.0296 A
          Mean   = 1.7532 A
          StdDev = 0.1715 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  =  97.604 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 119.993 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  =  52.840 deg; O2  -- O1  = 1 A
O2  -- T1  -- O1  =  48.147 deg; O2  -- O1  = 1 A
O3  -- T1  -- O1  = 124.234 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  =  99.222 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 112.317 deg; O3  -- O1  = 3 A
O1  -- T1  -- O1  =  77.468 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  = 123.409 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  96.646 deg; O1  -- O1  = 3 A
       48.147 deg <-- 95.188 deg --> 124.234 deg

        O-T-O SUMMARY
          Range  = 48.1470 deg <--> 124.2342 deg
          Mean   = 95.0609 deg
          StdDev = 27.1100 deg

        O--O SUMMARY
          Range  = 1.4065 A <--> 3.3786 A
          Mean   = 2.5547 A
          StdDev = 0.7007 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  74.448 deg ; T1  -- T1   2.1947 A
T1  -- O1  -- T1  =  58.789 deg ; T1  -- T1   1.6586 A
T1  -- O1  -- T1  = 106.021 deg ; T1  -- T1   3.0663 A

T1  -- O2  -- T1  =  61.735 deg ; T1  -- T1   1.6586 A

T1  -- O3  -- T1  = 138.982 deg ; T1  -- T1   3.3224 A


        T-O-T SUMMARY
          Range  = 58.7894° <--> 138.9820 deg
          Mean   = 87.9951 deg
          StdDev = 30.8867 deg

        T--T SUMMARY
          Range  = 1.6586 A <--> 3.3224 A
          Mean   = 2.3801 A
          StdDev = 0.7066 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.2664 A
O1  -- O2  = 1.4065 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.1947 Angstrom
  T1  -- T1  = 3.3224 Angstrom
  T1  -- T1  = 3.0663 Angstrom
  T1  -- T1  = 1.6586 Angstrom
  T1  -- T1  = 3.0663 Angstrom
  T1  -- T1  = 3.0467 Angstrom