Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_95a_1_173_r74skK.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8063 Angstrom
T1  -- O1  = 1.5630 Angstrom
T1  -- O2  = 1.8745 Angstrom
T1  -- O3  = 1.6116 Angstrom
      mean = 1.7139 Angstrom
        t1 = 0.271561  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.291801  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5630 A <--> 1.8745 A
          Mean   = 1.7139 A
          StdDev = 0.1321 A

       t1 Range  = 0.2716 <-- 0.2716 --> 0.2716
       t2 Range  = 0.2918 <-- 0.2918 --> 0.2918

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 123.525 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 139.299 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  61.396 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  =  70.763 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  67.011 deg; O1  -- O3  = 2 A
O2  -- T1  -- O3  = 134.356 deg; O2  -- O3  = 3 A
       61.396 deg <-- 99.392 deg --> 139.299 deg

        O-T-O SUMMARY
          Range  = 61.3959 deg <--> 139.2993 deg
          Mean   = 96.2131 deg
          StdDev = 33.5287 deg

        O--O SUMMARY
          Range  = 1.7529 A <--> 3.4511 A
          Mean   = 2.4621 A
          StdDev = 0.7131 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  81.324 deg; T1  -- T1  = 4.1319 A
T1  - O1  - T1  - O2  - T1  =  40.517 deg; T1  -- T1  = 2.1958 A
T1  - O1  - T1  - O3  - T1  =  70.549 deg; T1  -- T1  = 3.1870 A
T1  - O1  - T1  - O2  - T1  = 121.833 deg; T1  -- T1  = 5.5703 A
T1  - O1  - T1  - O3  - T1  =  68.935 deg; T1  -- T1  = 3.1540 A
T1  - O2  - T1  - O3  - T1  =  87.761 deg; T1  -- T1  = 3.7989 A

        T-T-T SUMMARY
          Range  = 40.5166 deg <--> 121.8327 deg
          Mean   = 77.6431 deg
          StdDev = 25.5979 deg

        T--T SUMMARY
          Range  = 2.1958 A <--> 5.5703 A
          Mean   = 3.6616 A
          StdDev = 1.1001 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.034 deg ; T1  -- T1   3.1870 A

T1  -- O2  -- T1  = 162.751 deg ; T1  -- T1   3.7066 A

T1  -- O3  -- T1  = 156.205 deg ; T1  -- T1   3.1540 A


        T-O-T SUMMARY
          Range  = 142.0344° <--> 162.7510 deg
          Mean   = 153.6635 deg
          StdDev = 8.8323 deg

        T--T SUMMARY
          Range  = 3.1540 A <--> 3.7066 A
          Mean   = 3.3492 A
          StdDev = 0.2585 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0065 A
O1  -- O3  = 1.7529 A
O1  -- O3  = 1.7529 A
T1  -- T1  = 2.1958 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 24 45 69 99 139 181 229 284 340 405 479 553 638 728
TD10 = 1085
Circuit symbol = 4.8_{5}.4.8_{7}.6.8_{8}
Weight = 34
Vertex symbol  = 4.8_{5}.4.8_{7}.8_{6}.8_{8}
Weight = 41

<TD10> = 1085.000
Average ring size = 7.4667