Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_95_2_8486602_h9CrOE.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 24.68 T-atoms per nm^3
Material density = 2.462 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5998 Angstrom
T1  -- O2  = 1.5956 Angstrom
T1  -- O3  = 1.6632 Angstrom
T1  -- O4  = 1.6182 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.067795  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042840  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6740 Angstrom
T2  -- O5  = 1.6059 Angstrom
T2  -- O6  = 1.6042 Angstrom
T2  -- O3  = 1.6172 Angstrom
      mean = 1.6253 Angstrom
        t1 = 0.064196  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040373  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5956 A <--> 1.6740 A
          Mean   = 1.6223 A
          StdDev = 0.0281 A

       t1 Range  = 0.0642 <-- 0.0660 --> 0.0678
       t2 Range  = 0.0404 <-- 0.0416 --> 0.0428

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.944 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.994 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  98.285 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 107.064 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  98.542 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 127.182 deg; O3  -- O4  = 3 A
       98.285 deg <-- 109.668 deg --> 127.182 deg

O4  -- T2  -- O5  = 106.692 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 106.500 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 126.479 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 119.044 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  =  99.716 deg; O5  -- O3  = 2 A
O6  -- T2  -- O3  =  99.536 deg; O6  -- O3  = 2 A
       99.536 deg <-- 109.661 deg --> 126.479 deg

        O-T-O SUMMARY
          Range  = 98.2846 deg <--> 127.1821 deg
          Mean   = 108.7711 deg
          StdDev = 10.3509 deg

        O--O SUMMARY
          Range  = 2.4339 A <--> 2.9390 A
          Mean   = 2.6309 A
          StdDev = 0.1775 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 136.644 deg; T1  -- T1  = 5.6474 A
T1  - O1  - T1  - O3  - T2  =  74.421 deg; T1  -- T2  = 3.5867 A
T1  - O1  - T1  - O4  - T2  = 105.422 deg; T1  -- T2  = 4.7023 A
T1  - O2  - T1  - O3  - T2  =  80.886 deg; T1  -- T2  = 4.0227 A
T1  - O2  - T1  - O4  - T2  = 117.870 deg; T1  -- T2  = 5.2943 A
T2  - O3  - T1  - O4  - T2  = 127.598 deg; T2  -- T2  = 5.4126 A

T1  - O4  - T2  - O5  - T2  =  87.306 deg; T1  -- T2  = 4.0227 A
T1  - O4  - T2  - O6  - T1  = 127.598 deg; T1  -- T1  = 5.4126 A
T1  - O4  - T2  - O3  - T2  = 105.263 deg; T1  -- T2  = 4.7023 A
T2  - O5  - T2  - O6  - T1  =  97.642 deg; T2  -- T1  = 4.3704 A
T2  - O5  - T2  - O3  - T2  = 167.431 deg; T2  -- T2  = 5.6530 A
T1  - O6  - T2  - O3  - T2  =  74.894 deg; T1  -- T2  = 3.5867 A

        T-T-T SUMMARY
          Range  = 74.4210 deg <--> 167.4314 deg
          Mean   = 107.8028 deg
          StdDev = 27.5634 deg

        T--T SUMMARY
          Range  = 3.5867 A <--> 5.6530 A
          Mean   = 4.6732 A
          StdDev = 0.7531 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.280 deg ; T1  -- T1   2.9032 A

T1  -- O2  -- T1  = 167.803 deg ; T1  -- T1   3.1731 A

T1  -- O3  -- T2  = 132.862 deg ; T1  -- T2   3.0068 A

T1  -- O4  -- T2  = 133.565 deg ; T1  -- T2   3.0256 A

T2  -- O5  -- T2  = 128.284 deg ; T2  -- T2   2.8902 A

T2  -- O6  -- T2  = 121.324 deg ; T2  -- T2   2.7969 A


        T-O-T SUMMARY
          Range  = 121.3238° <--> 167.8032 deg
          Mean   = 135.6864 deg
          StdDev = 15.0701 deg

        T--T SUMMARY
          Range  = 2.7969 A <--> 3.1731 A
          Mean   = 2.9660 A
          StdDev = 0.1213 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7969 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

<TD10> = 918.000
Average ring size = 9.0110