Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_94_1_18_nIQNIP.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 32.13 T-atoms per nm^3
Material density = 3.205 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5482 Angstrom
T1  -- O2  = 1.6799 Angstrom
T1  -- O2  = 1.7180 Angstrom
T1  -- O3  = 1.6219 Angstrom
T1  -- O1  = 2.0949 Angstrom
      mean = 1.7326 Angstrom

        T-O SUMMARY
          Range  = 1.5482 A <--> 2.0949 A
          Mean   = 1.7326 A
          StdDev = 0.1924 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  59.745 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  =  80.959 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 134.092 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  81.031 deg; O1  -- O1  = 2 A
O2  -- T1  -- O2  = 132.596 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 102.157 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 135.514 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  =  86.046 deg; O2  -- O3  = 2 A
O2  -- T1  -- O1  =  48.791 deg; O2  -- O1  = 2 A
O3  -- T1  -- O1  = 120.945 deg; O3  -- O1  = 3 A
       48.791 deg <-- 98.188 deg --> 135.514 deg

        O-T-O SUMMARY
          Range  = 48.7912 deg <--> 135.5144 deg
          Mean   = 95.7463 deg
          StdDev = 30.8198 deg

        O--O SUMMARY
          Range  = 1.6118 A <--> 3.4974 A
          Mean   = 2.4809 A
          StdDev = 0.6470 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 113.087 deg ; T1  -- T1   3.0543 A
T1  -- O1  -- T1  = 118.892 deg ; T1  -- T1   2.6664 A
T1  -- O1  -- T1  = 113.087 deg ; T1  -- T1   3.0543 A
T1  -- O1  -- T1  = 113.087 deg ; T1  -- T1   3.0543 A
T1  -- O1  -- T1  =  79.047 deg ; T1  -- T1   2.6664 A
T1  -- O1  -- T1  = 113.087 deg ; T1  -- T1   3.0543 A

T1  -- O2  -- T1  = 128.022 deg ; T1  -- T1   3.0543 A

T1  -- O3  -- T1  = 162.192 deg ; T1  -- T1   3.2046 A


        T-O-T SUMMARY
          Range  = 79.0474° <--> 162.1916 deg
          Mean   = 117.5625 deg
          StdDev = 21.5774 deg

        T--T SUMMARY
          Range  = 2.6664 A <--> 3.2046 A
          Mean   = 2.9761 A
          StdDev = 0.1868 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.6118 A
O1  -- O2  = 2.1243 A
O1  -- O2  = 1.6118 A
O1  -- O2  = 2.1243 A
O2  -- O3  = 2.2799 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.0543 Angstrom
  T1  -- T1  = 3.2044 Angstrom
  T1  -- T1  = 3.2046 Angstrom
  T1  -- T1  = 3.0543 Angstrom
  T1  -- T1  = 2.6664 Angstrom
  T1  -- T1  = 3.0543 Angstrom
  T1  -- T1  = 3.0543 Angstrom