Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_93_2_1236768_VIFtIH.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.99 T-atoms per nm^3
Material density = 1.695 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5501 Angstrom
T1  -- O2  = 1.7075 Angstrom
T1  -- O3  = 1.5701 Angstrom
T1  -- O4  = 1.6169 Angstrom
      mean = 1.6111 Angstrom
        t1 = 0.091764  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.059012  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6904 Angstrom
T2  -- O5  = 1.6131 Angstrom
T2  -- O6  = 1.5430 Angstrom
T2  -- O7  = 1.7147 Angstrom
      mean = 1.6403 Angstrom
        t1 = 0.088679  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.093068  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5430 A <--> 1.7147 A
          Mean   = 1.6257 A
          StdDev = 0.0664 A

       t1 Range  = 0.0887 <-- 0.0902 --> 0.0918
       t2 Range  = 0.0590 <-- 0.0760 --> 0.0931

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.294 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.114 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  93.928 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 110.262 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 135.453 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  98.999 deg; O3  -- O4  = 2 A
       93.928 deg <-- 109.175 deg --> 135.453 deg

O4  -- T2  -- O5  = 110.180 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  =  92.806 deg; O4  -- O6  = 2 A
O4  -- T2  -- O7  = 130.802 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.269 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.672 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 100.924 deg; O6  -- O7  = 3 A
       92.806 deg <-- 108.942 deg --> 130.802 deg

        O-T-O SUMMARY
          Range  = 92.8060 deg <--> 135.4528 deg
          Mean   = 109.4929 deg
          StdDev = 14.2694 deg

        O--O SUMMARY
          Range  = 2.3153 A <--> 3.0961 A
          Mean   = 2.6441 A
          StdDev = 0.2725 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 103.693 deg; T2  -- T1  = 4.3675 A
T2  - O1  - T1  - O3  - T1  = 110.878 deg; T2  -- T1  = 4.6317 A
T2  - O1  - T1  - O4  - T1  = 162.299 deg; T2  -- T1  = 5.6265 A
T1  - O2  - T1  - O3  - T1  =  62.850 deg; T1  -- T1  = 2.7158 A
T1  - O2  - T1  - O4  - T1  =  59.922 deg; T1  -- T1  = 2.6412 A
T1  - O3  - T1  - O4  - T1  =  57.227 deg; T1  -- T1  = 2.5663 A

T1  - O4  - T2  - O5  - T2  =  94.205 deg; T1  -- T2  = 4.4231 A
T1  - O4  - T2  - O6  - T2  = 117.518 deg; T1  -- T2  = 5.1620 A
T1  - O4  - T2  - O7  - T2  = 127.077 deg; T1  -- T2  = 5.5549 A
T2  - O5  - T2  - O6  - T2  =  82.333 deg; T2  -- T2  = 4.0272 A
T2  - O5  - T2  - O7  - T2  = 111.423 deg; T2  -- T2  = 5.1932 A
T2  - O6  - T2  - O7  - T2  = 111.423 deg; T2  -- T2  = 5.1932 A

        T-T-T SUMMARY
          Range  = 57.2275 deg <--> 162.2987 deg
          Mean   = 101.0610 deg
          StdDev = 32.5843 deg

        T--T SUMMARY
          Range  = 2.5663 A <--> 5.6265 A
          Mean   = 4.3376 A
          StdDev = 1.1620 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 116.842 deg ; T1  -- T1   2.6412 A

T1  -- O2  -- T1  = 105.359 deg ; T1  -- T1   2.7158 A

T1  -- O3  -- T1  = 109.625 deg ; T1  -- T1   2.5663 A

T1  -- O4  -- T2  = 128.443 deg ; T1  -- T2   2.9783 A

T2  -- O5  -- T2  = 177.611 deg ; T2  -- T2   3.2255 A

T2  -- O6  -- T2  = 164.820 deg ; T2  -- T2   3.0590 A

T2  -- O7  -- T2  = 126.248 deg ; T2  -- T2   3.0590 A


        T-O-T SUMMARY
          Range  = 105.3594° <--> 177.6106 deg
          Mean   = 132.7070 deg
          StdDev = 25.9786 deg

        T--T SUMMARY
          Range  = 2.5663 A <--> 3.2255 A
          Mean   = 2.8922 A
          StdDev = 0.2334 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.5663 Angstrom
T1  -- T1  = 2.6412 Angstrom
T1  -- T1  = 2.7158 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 6 15 30 44 52 96 120 152 185 224 253 347 358 444 451
TD10 = 705
Circuit symbol = 3.6_{2}.3.7_{2}.3.7_{2}
Weight = 10
Vertex symbol  = 3.6_{2}.3.8.3.16_{2}
Weight = 38

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 19 27 45 70 101 127 152 183 234 284 338 373 421 483
TD10 = 740
Circuit symbol = 4.8.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.8.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 722.500
Average ring size = 5.4684