Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91a_1_66_clfl9B.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9770 Angstrom
T1  -- O3  = 1.8769 Angstrom
T1  -- O1  = 1.9111 Angstrom
T1  -- O1  = 1.8855 Angstrom
T1  -- O1  = 2.0141 Angstrom
T1  -- O2  = 1.6222 Angstrom
      mean = 1.8811 Angstrom

        T-O SUMMARY
          Range  = 1.6222 A <--> 2.0141 A
          Mean   = 1.8811 A
          StdDev = 0.1271 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 139.899 deg; O1  -- O3  = 4 A
O1  -- T1  -- O1  = 120.849 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  77.412 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  =  70.877 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  59.641 deg; O1  -- O2  = 2 A
O3  -- T1  -- O1  =  90.692 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 138.944 deg; O3  -- O1  = 4 A
O3  -- T1  -- O1  =  93.771 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  =  80.572 deg; O3  -- O2  = 2 A
O1  -- T1  -- O1  =  75.115 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  =  79.677 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 136.487 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 120.223 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 135.299 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  58.749 deg; O1  -- O2  = 2 A
       58.749 deg <-- 98.547 deg --> 139.899 deg

        O-T-O SUMMARY
          Range  = 58.7493 deg <--> 139.8994 deg
          Mean   = 99.1671 deg
          StdDev = 29.5528 deg

        O--O SUMMARY
          Range  = 1.8161 A <--> 3.6205 A
          Mean   = 2.7794 A
          StdDev = 0.5949 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  59.989 deg ; T1  -- T1   1.9325 A
T1  -- O1  -- T1  = 103.702 deg ; T1  -- T1   3.0579 A
T1  -- O1  -- T1  =  94.505 deg ; T1  -- T1   2.9310 A
T1  -- O1  -- T1  =  60.614 deg ; T1  -- T1   1.9160 A
T1  -- O1  -- T1  = 103.232 deg ; T1  -- T1   3.0579 A
T1  -- O1  -- T1  =  58.919 deg ; T1  -- T1   1.9325 A

T1  -- O2  -- T1  = 129.223 deg ; T1  -- T1   2.9310 A

T1  -- O3  -- T1  = 165.624 deg ; T1  -- T1   3.7243 A


        T-O-T SUMMARY
          Range  = 58.9193° <--> 165.6238 deg
          Mean   = 96.9759 deg
          StdDev = 35.6018 deg

        T--T SUMMARY
          Range  = 1.9160 A <--> 3.7243 A
          Mean   = 2.6854 A
          StdDev = 0.6378 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.8161 A
O2  -- O3  = 2.2708 A
O2  -- O3  = 2.2708 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 6 bridging O-atoms
  T1  -- T1  = 1.9160 Angstrom
  T1  -- T1  = 3.0579 Angstrom
  T1  -- T1  = 1.9325 Angstrom
  T1  -- T1  = 3.0579 Angstrom
  T1  -- T1  = 2.9310 Angstrom