Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_8546708_TFL902.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 26.10 T-atoms per nm^3
Material density = 2.604 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6075 Angstrom
T1  -- O2  = 1.6721 Angstrom
T1  -- O3  = 1.6174 Angstrom
T1  -- O4  = 1.6081 Angstrom
      mean = 1.6263 Angstrom
        t1 = 0.066137  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.064482  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6723 Angstrom
T2  -- O4  = 1.6029 Angstrom
T2  -- O5  = 1.6062 Angstrom
T2  -- O2  = 1.6185 Angstrom
      mean = 1.6250 Angstrom
        t1 = 0.066269  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.041768  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6029 A <--> 1.6723 A
          Mean   = 1.6256 A
          StdDev = 0.0276 A

       t1 Range  = 0.0661 <-- 0.0662 --> 0.0663
       t2 Range  = 0.0418 <-- 0.0531 --> 0.0645

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.106 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  98.365 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 119.242 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 125.013 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.845 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.842 deg; O3  -- O4  = 2 A
       97.842 deg <-- 109.569 deg --> 125.013 deg

O3  -- T2  -- O4  = 108.248 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 108.858 deg; O3  -- O5  = 3 A
O3  -- T2  -- O2  = 125.104 deg; O3  -- O2  = 3 A
O4  -- T2  -- O5  = 119.045 deg; O4  -- O5  = 3 A
O4  -- T2  -- O2  =  98.373 deg; O4  -- O2  = 2 A
O5  -- T2  -- O2  =  97.741 deg; O5  -- O2  = 2 A
       97.741 deg <-- 109.562 deg --> 125.104 deg

        O-T-O SUMMARY
          Range  = 97.7411 deg <--> 125.1042 deg
          Mean   = 109.5654 deg
          StdDev = 10.0376 deg

        O--O SUMMARY
          Range  = 2.4289 A <--> 2.9205 A
          Mean   = 2.6469 A
          StdDev = 0.1741 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.705 deg ; T1  -- T1   2.9451 A

T1  -- O2  -- T2  = 127.627 deg ; T1  -- T2   2.9530 A

T1  -- O3  -- T2  = 127.537 deg ; T1  -- T2   2.9510 A

T1  -- O4  -- T2  = 138.036 deg ; T1  -- T2   2.9981 A

T2  -- O5  -- T2  = 132.662 deg ; T2  -- T2   2.9421 A


        T-O-T SUMMARY
          Range  = 127.5372° <--> 138.0355 deg
          Mean   = 131.7134 deg
          StdDev = 3.9482 deg

        T--T SUMMARY
          Range  = 2.9421 A <--> 2.9981 A
          Mean   = 2.9579 A
          StdDev = 0.0208 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.9451 Angstrom
  T1  -- T1  = 3.4775 Angstrom
  T1  -- T2  = 2.9510 Angstrom
  T1  -- T2  = 3.4874 Angstrom
  T1  -- T2  = 2.9530 Angstrom
  T1  -- T2  = 2.9981 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.9510 Angstrom
  T2  -- T1  = 3.4874 Angstrom
  T2  -- T1  = 2.9530 Angstrom
  T2  -- T1  = 2.9981 Angstrom
  T2  -- T2  = 2.9421 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

<TD10> = 918.000
Average ring size = 9.0110