Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_8546687_eUMvvg.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 20.68 T-atoms per nm^3
Material density = 2.064 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6008 Angstrom
T1  -- O2  = 1.6193 Angstrom
T1  -- O3  = 1.6347 Angstrom
T1  -- O4  = 1.5943 Angstrom
      mean = 1.6123 Angstrom
        t1 = 0.071377  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061392  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6301 Angstrom
T2  -- O4  = 1.6025 Angstrom
T2  -- O5  = 1.6119 Angstrom
T2  -- O2  = 1.6455 Angstrom
      mean = 1.6225 Angstrom
        t1 = 0.067658  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045829  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5943 A <--> 1.6455 A
          Mean   = 1.6174 A
          StdDev = 0.0171 A

       t1 Range  = 0.0677 <-- 0.0695 --> 0.0714
       t2 Range  = 0.0458 <-- 0.0536 --> 0.0614

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 104.092 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  98.589 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 125.482 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 128.255 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.040 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  99.171 deg; O3  -- O4  = 2 A
       98.589 deg <-- 109.938 deg --> 128.255 deg

O3  -- T2  -- O4  = 104.702 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 104.888 deg; O3  -- O5  = 3 A
O3  -- T2  -- O2  = 128.794 deg; O3  -- O2  = 3 A
O4  -- T2  -- O5  = 121.701 deg; O4  -- O5  = 3 A
O4  -- T2  -- O2  =  98.977 deg; O4  -- O2  = 2 A
O5  -- T2  -- O2  =  99.816 deg; O5  -- O2  = 2 A
       98.977 deg <-- 109.813 deg --> 128.794 deg

        O-T-O SUMMARY
          Range  = 98.5886 deg <--> 128.7944 deg
          Mean   = 109.8756 deg
          StdDev = 11.8241 deg

        O--O SUMMARY
          Range  = 2.4528 A <--> 2.9539 A
          Mean   = 2.6337 A
          StdDev = 0.1837 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.657 deg; T1  -- T2  = 4.3069 A
T1  - O1  - T1  - O3  - T2  = 159.022 deg; T1  -- T2  = 5.7616 A
T1  - O1  - T1  - O4  - T2  =  89.857 deg; T1  -- T2  = 4.3131 A
T2  - O2  - T1  - O3  - T2  =  82.736 deg; T2  -- T2  = 4.1409 A
T2  - O2  - T1  - O4  - T2  = 128.582 deg; T2  -- T2  = 5.8516 A
T2  - O3  - T1  - O4  - T2  = 110.170 deg; T2  -- T2  = 5.1334 A

T1  - O3  - T2  - O4  - T1  =  83.733 deg; T1  -- T1  = 4.1815 A
T1  - O3  - T2  - O5  - T1  = 128.582 deg; T1  -- T1  = 5.8516 A
T1  - O3  - T2  - O2  - T2  =  90.309 deg; T1  -- T2  = 4.3131 A
T1  - O4  - T2  - O5  - T1  = 109.151 deg; T1  -- T1  = 5.1014 A
T1  - O4  - T2  - O2  - T2  = 159.153 deg; T1  -- T2  = 5.7357 A
T1  - O5  - T2  - O2  - T2  =  90.177 deg; T1  -- T2  = 4.3069 A

        T-T-T SUMMARY
          Range  = 82.7360 deg <--> 159.1531 deg
          Mean   = 110.0941 deg
          StdDev = 26.8233 deg

        T--T SUMMARY
          Range  = 4.1409 A <--> 5.8516 A
          Mean   = 4.9165 A
          StdDev = 0.7006 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.616 deg ; T1  -- T1   2.8477 A

T1  -- O2  -- T2  = 167.845 deg ; T1  -- T2   3.2464 A

T1  -- O3  -- T2  = 168.404 deg ; T1  -- T2   3.2481 A

T1  -- O4  -- T2  = 140.813 deg ; T1  -- T2   3.0117 A

T2  -- O5  -- T2  = 122.045 deg ; T2  -- T2   2.8202 A


        T-O-T SUMMARY
          Range  = 122.0451° <--> 168.4038 deg
          Mean   = 144.9447 deg
          StdDev = 20.2032 deg

        T--T SUMMARY
          Range  = 2.8202 A <--> 3.2481 A
          Mean   = 3.0348 A
          StdDev = 0.1878 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

<TD10> = 918.000
Average ring size = 9.0110