Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_8507550_W9GPoB.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 20.87 T-atoms per nm^3
Material density = 2.082 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6101 Angstrom
T1  -- O2  = 1.5970 Angstrom
T1  -- O3  = 1.6387 Angstrom
T1  -- O4  = 1.6262 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.066156  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046864  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6455 Angstrom
T2  -- O5  = 1.6052 Angstrom
T2  -- O6  = 1.5939 Angstrom
T2  -- O3  = 1.6196 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.068089  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.051162  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5939 A <--> 1.6455 A
          Mean   = 1.6171 A
          StdDev = 0.0178 A

       t1 Range  = 0.0662 <-- 0.0671 --> 0.0681
       t2 Range  = 0.0469 <-- 0.0490 --> 0.0512

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 121.850 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.235 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 101.762 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 101.841 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 101.612 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 128.826 deg; O3  -- O4  = 3 A
       101.612 deg <-- 109.854 deg --> 128.826 deg

O4  -- T2  -- O5  = 102.230 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 101.966 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 129.350 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 122.373 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 102.458 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 100.927 deg; O6  -- O3  = 2 A
       100.927 deg <-- 109.884 deg --> 129.350 deg

        O-T-O SUMMARY
          Range  = 100.9272 deg <--> 129.3496 deg
          Mean   = 108.7561 deg
          StdDev = 11.2372 deg

        O--O SUMMARY
          Range  = 2.4784 A <--> 2.9514 A
          Mean   = 2.6188 A
          StdDev = 0.1774 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 152.315 deg; T1  -- T1  = 5.7135 A
T1  - O1  - T1  - O3  - T2  =  85.772 deg; T1  -- T2  = 4.1422 A
T1  - O1  - T1  - O4  - T2  =  94.177 deg; T1  -- T2  = 4.4458 A
T1  - O2  - T1  - O3  - T2  =  82.099 deg; T1  -- T2  = 4.1386 A
T1  - O2  - T1  - O4  - T2  = 112.758 deg; T1  -- T2  = 5.2360 A
T2  - O3  - T1  - O4  - T2  = 129.186 deg; T2  -- T2  = 5.8468 A

T1  - O4  - T2  - O5  - T2  =  83.897 deg; T1  -- T2  = 4.1386 A
T1  - O4  - T2  - O6  - T1  = 129.186 deg; T1  -- T1  = 5.8468 A
T1  - O4  - T2  - O3  - T2  =  93.997 deg; T1  -- T2  = 4.4458 A
T2  - O5  - T2  - O6  - T1  = 107.252 deg; T2  -- T1  = 4.9712 A
T2  - O5  - T2  - O3  - T2  = 164.438 deg; T2  -- T2  = 5.7111 A
T1  - O6  - T2  - O3  - T2  =  86.054 deg; T1  -- T2  = 4.1422 A

        T-T-T SUMMARY
          Range  = 82.0986 deg <--> 164.4381 deg
          Mean   = 108.3043 deg
          StdDev = 26.6117 deg

        T--T SUMMARY
          Range  = 4.1386 A <--> 5.8468 A
          Mean   = 4.8578 A
          StdDev = 0.7175 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 122.851 deg ; T1  -- T1   2.8280 A

T1  -- O2  -- T1  = 146.201 deg ; T1  -- T1   3.0561 A

T1  -- O3  -- T2  = 165.022 deg ; T1  -- T2   3.2306 A

T1  -- O4  -- T2  = 164.595 deg ; T1  -- T2   3.2422 A

T2  -- O5  -- T2  = 123.220 deg ; T2  -- T2   2.8243 A

T2  -- O6  -- T2  = 134.508 deg ; T2  -- T2   2.9398 A


        T-O-T SUMMARY
          Range  = 122.8506° <--> 165.0224 deg
          Mean   = 142.7328 deg
          StdDev = 17.6515 deg

        T--T SUMMARY
          Range  = 2.8243 A <--> 3.2422 A
          Mean   = 3.0202 A
          StdDev = 0.1734 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 36 60 86 117 153 194 240 290 345 405 470 540 614
TD10 = 918
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{20}.10_{6}.10_{12}
Weight = 48

<TD10> = 918.000
Average ring size = 9.0110