Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_8340232_39pXoJ.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.57 T-atoms per nm^3
Material density = 1.753 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5932 Angstrom
T1  -- O2  = 1.6111 Angstrom
T1  -- O3  = 1.6200 Angstrom
T1  -- O4  = 1.6109 Angstrom
      mean = 1.6088 Angstrom
        t1 = 0.021928  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033624  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6291 Angstrom
T2  -- O5  = 1.6425 Angstrom
T2  -- O4  = 1.6115 Angstrom
T2  -- O6  = 1.6120 Angstrom
      mean = 1.6238 Angstrom
        t1 = 0.022641  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017159  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5932 A <--> 1.6425 A
          Mean   = 1.6163 A
          StdDev = 0.0138 A

       t1 Range  = 0.0219 <-- 0.0223 --> 0.0226
       t2 Range  = 0.0172 <-- 0.0254 --> 0.0336

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.240 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 102.031 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 111.983 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.846 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.669 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.647 deg; O3  -- O4  = 3 A
       102.031 deg <-- 109.403 deg --> 111.983 deg

O3  -- T2  -- O5  = 115.458 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 106.989 deg; O3  -- O4  = 3 A
O3  -- T2  -- O6  = 107.111 deg; O3  -- O6  = 3 A
O5  -- T2  -- O4  = 109.404 deg; O5  -- O4  = 3 A
O5  -- T2  -- O6  = 109.132 deg; O5  -- O6  = 3 A
O4  -- T2  -- O6  = 108.535 deg; O4  -- O6  = 3 A
       106.989 deg <-- 109.438 deg --> 115.458 deg

        O-T-O SUMMARY
          Range  = 102.0311 deg <--> 115.4581 deg
          Mean   = 109.3508 deg
          StdDev = 3.2742 deg

        O--O SUMMARY
          Range  = 2.4978 A <--> 2.7663 A
          Mean   = 2.6367 A
          StdDev = 0.0608 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 114.746 deg; T1  -- T1  = 5.2880 A
T1  - O1  - T1  - O3  - T2  =  90.065 deg; T1  -- T2  = 4.5007 A
T1  - O1  - T1  - O4  - T2  = 114.896 deg; T1  -- T2  = 5.2707 A
T1  - O2  - T1  - O3  - T2  = 129.716 deg; T1  -- T2  = 5.6802 A
T1  - O2  - T1  - O4  - T2  =  79.712 deg; T1  -- T2  = 3.9515 A
T2  - O3  - T1  - O4  - T2  = 130.200 deg; T2  -- T2  = 5.6679 A

T1  - O3  - T2  - O5  - T2  = 129.785 deg; T1  -- T2  = 5.6660 A
T1  - O3  - T2  - O4  - T1  = 129.996 deg; T1  -- T1  = 5.6632 A
T1  - O3  - T2  - O6  - T2  = 103.553 deg; T1  -- T2  = 5.0761 A
T2  - O5  - T2  - O4  - T1  =  79.987 deg; T2  -- T1  = 3.9515 A
T2  - O5  - T2  - O6  - T2  = 104.815 deg; T2  -- T2  = 5.0414 A
T1  - O4  - T2  - O6  - T2  = 104.985 deg; T1  -- T2  = 5.0406 A

        T-T-T SUMMARY
          Range  = 79.7121 deg <--> 130.1999 deg
          Mean   = 109.3341 deg
          StdDev = 18.9716 deg

        T--T SUMMARY
          Range  = 3.9515 A <--> 5.6802 A
          Mean   = 5.0575 A
          StdDev = 0.6308 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 174.439 deg ; T1  -- T1   3.1827 A

T1  -- O2  -- T1  = 147.803 deg ; T1  -- T1   3.0959 A

T1  -- O3  -- T2  = 156.092 deg ; T1  -- T2   3.1787 A

T1  -- O4  -- T2  = 144.607 deg ; T1  -- T2   3.0699 A

T2  -- O5  -- T2  = 175.213 deg ; T2  -- T2   3.2821 A

T2  -- O6  -- T2  = 145.422 deg ; T2  -- T2   3.0783 A


        T-O-T SUMMARY
          Range  = 144.6067° <--> 175.2132 deg
          Mean   = 157.2626 deg
          StdDev = 13.1017 deg

        T--T SUMMARY
          Range  = 3.0699 A <--> 3.2821 A
          Mean   = 3.1479 A
          StdDev = 0.0759 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

<TD10> = 1033.000
Average ring size = 5.8065