Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_10681262_D22C9f.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.84 T-atoms per nm^3
Material density = 2.279 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6113 Angstrom
T1  -- O1  = 1.6113 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O2  = 1.6212 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004094  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000975  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O3  = 1.6114 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O3  = 1.6114 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004094  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001229  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6113 A <--> 1.6212 A
          Mean   = 1.6163 A
          StdDev = 0.0050 A

       t1 Range  = 0.0041 <-- 0.0041 --> 0.0041
       t2 Range  = 0.0010 <-- 0.0011 --> 0.0012

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 110.322 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.332 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.314 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.314 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.332 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 109.208 deg; O2  -- O2  = 3 A
       109.208 deg <-- 109.470 deg --> 110.322 deg

O2  -- T2  -- O3  = 109.315 deg; O2  -- O3  = 3 A
O2  -- T2  -- O2  = 109.215 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 109.332 deg; O2  -- O3  = 3 A
O3  -- T2  -- O2  = 109.332 deg; O3  -- O2  = 3 A
O3  -- T2  -- O3  = 110.315 deg; O3  -- O3  = 3 A
O2  -- T2  -- O3  = 109.315 deg; O2  -- O3  = 3 A
       109.215 deg <-- 109.470 deg --> 110.315 deg

        O-T-O SUMMARY
          Range  = 109.2081 deg <--> 110.3216 deg
          Mean   = 109.3934 deg
          StdDev = 0.2973 deg

        O--O SUMMARY
          Range  = 2.6368 A <--> 2.6450 A
          Mean   = 2.6388 A
          StdDev = 0.0031 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O1  - T1  =  96.860 deg; T2  -- T1  = 4.6557 A
T2  - O1  - T1  - O2  - T1  = 134.258 deg; T2  -- T1  = 5.7322 A
T2  - O1  - T1  - O2  - T2  = 103.087 deg; T2  -- T2  = 4.7293 A
T1  - O1  - T1  - O2  - T1  =  97.840 deg; T1  -- T1  = 4.8260 A
T1  - O1  - T1  - O2  - T2  = 134.258 deg; T1  -- T2  = 5.7322 A
T1  - O2  - T1  - O2  - T2  =  96.860 deg; T1  -- T2  = 4.6557 A

T1  - O2  - T2  - O3  - T2  =  96.861 deg; T1  -- T2  = 4.6558 A
T1  - O2  - T2  - O2  - T1  = 103.087 deg; T1  -- T1  = 4.7293 A
T1  - O2  - T2  - O3  - T2  = 134.257 deg; T1  -- T2  = 5.7323 A
T2  - O3  - T2  - O2  - T1  = 134.257 deg; T2  -- T1  = 5.7323 A
T2  - O3  - T2  - O3  - T2  =  97.840 deg; T2  -- T2  = 4.8263 A
T1  - O2  - T2  - O3  - T2  =  96.861 deg; T1  -- T2  = 4.6558 A

        T-T-T SUMMARY
          Range  = 96.8601 deg <--> 134.2583 deg
          Mean   = 111.7253 deg
          StdDev = 17.2678 deg

        T--T SUMMARY
          Range  = 4.6557 A <--> 5.7323 A
          Mean   = 5.0838 A
          StdDev = 0.4959 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 166.770 deg ; T1  -- T1   3.2012 A

T1  -- O2  -- T2  = 137.279 deg ; T1  -- T2   3.0197 A

T2  -- O3  -- T2  = 166.776 deg ; T2  -- T2   3.2013 A


        T-O-T SUMMARY
          Range  = 137.2787° <--> 166.7763 deg
          Mean   = 156.9415 deg
          StdDev = 14.5219 deg

        T--T SUMMARY
          Range  = 3.0197 A <--> 3.2013 A
          Mean   = 3.1407 A
          StdDev = 0.0894 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 492 566 650 744
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 492 566 650 744
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

<TD10> = 1125.000
Average ring size = 6.0000