Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_10527392_2J5Qz0.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 24.59 T-atoms per nm^3
Material density = 2.454 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6882 Angstrom
T1  -- O2  = 1.6654 Angstrom
T1  -- O3  = 1.7109 Angstrom
T1  -- O4  = 1.5470 Angstrom
      mean = 1.6529 Angstrom
        t1 = 0.089847  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.101460  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6202 Angstrom
T2  -- O3  = 1.6202 Angstrom
T2  -- O4  = 1.5927 Angstrom
T2  -- O4  = 1.5927 Angstrom
      mean = 1.6065 Angstrom
        t1 = 0.065711  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.041920  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5470 A <--> 1.7109 A
          Mean   = 1.6374 A
          StdDev = 0.0572 A

       t1 Range  = 0.0657 <-- 0.0778 --> 0.0898
       t2 Range  = 0.0419 <-- 0.0717 --> 0.1015

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.727 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 126.139 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  95.642 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 115.770 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 102.346 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.667 deg; O3  -- O4  = 2 A
       95.642 deg <-- 108.215 deg --> 126.139 deg

O3  -- T2  -- O3  = 130.973 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 107.585 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  =  98.715 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  =  98.715 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 107.585 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 113.722 deg; O4  -- O4  = 3 A
       98.715 deg <-- 109.549 deg --> 130.973 deg

        O-T-O SUMMARY
          Range  = 95.6419 deg <--> 130.9733 deg
          Mean   = 108.7585 deg
          StdDev = 11.1512 deg

        O--O SUMMARY
          Range  = 2.3993 A <--> 3.0306 A
          Mean   = 2.6359 A
          StdDev = 0.2102 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 112.800 deg; T1  -- T1  = 5.2940 A
T1  - O1  - T1  - O3  - T2  =  82.740 deg; T1  -- T2  = 4.0379 A
T1  - O1  - T1  - O4  - T2  = 144.913 deg; T1  -- T2  = 6.0229 A
T1  - O2  - T1  - O3  - T2  =  56.666 deg; T1  -- T2  = 2.7712 A
T1  - O2  - T1  - O4  - T2  = 102.146 deg; T1  -- T2  = 4.7094 A
T2  - O3  - T1  - O4  - T2  = 115.718 deg; T2  -- T2  = 4.8951 A

T1  - O3  - T2  - O3  - T1  =  66.668 deg; T1  -- T1  = 3.0456 A
T1  - O3  - T2  - O4  - T1  = 115.718 deg; T1  -- T1  = 4.8951 A
T1  - O3  - T2  - O4  - T1  = 101.696 deg; T1  -- T1  = 4.4841 A
T1  - O3  - T2  - O4  - T1  = 101.696 deg; T1  -- T1  = 4.4841 A
T1  - O3  - T2  - O4  - T1  = 115.718 deg; T1  -- T1  = 4.8951 A
T1  - O4  - T2  - O4  - T1  = 135.207 deg; T1  -- T1  = 5.5622 A

        T-T-T SUMMARY
          Range  = 56.6662 deg <--> 144.9134 deg
          Mean   = 103.9379 deg
          StdDev = 25.1565 deg

        T--T SUMMARY
          Range  = 2.7712 A <--> 6.0229 A
          Mean   = 4.5608 A
          StdDev = 0.9163 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.877 deg ; T1  -- T1   3.3079 A

T1  -- O2  -- T1  = 132.227 deg ; T1  -- T1   3.0456 A

T1  -- O3  -- T2  = 129.089 deg ; T1  -- T2   3.0080 A

T1  -- O4  -- T2  = 123.913 deg ; T1  -- T2   2.7712 A


        T-O-T SUMMARY
          Range  = 123.9126° <--> 156.8772 deg
          Mean   = 135.5266 deg
          StdDev = 12.8821 deg

        T--T SUMMARY
          Range  = 2.7712 A <--> 3.3079 A
          Mean   = 3.0332 A
          StdDev = 0.1934 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7712 Angstrom
T2  -- T1  = 2.7712 Angstrom
T2  -- T1  = 2.7712 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 24 45 67 102 133 184 224 285 337 408 470 555 631 726
TD10 = 1079
Circuit symbol = 3.6.6.7.7.7
Weight = 19
Vertex symbol  = 3.6.6.7.7.8
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 42 68 94 134 172 228 278 342 402 476 544 630 712
TD10 = 1055
Circuit symbol = 3.7.6.6.7_{2}.7_{2}
Weight = 23
Vertex symbol  = 3.7.6.6.7.7
Weight = 23

<TD10> = 1071.000
Average ring size = 5.5385