Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_91_2_10388839_9OiKD6.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.51 T-atoms per nm^3
Material density = 2.346 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6167 Angstrom
T1  -- O3  = 1.6432 Angstrom
T1  -- O4  = 1.5833 Angstrom
T1  -- O2  = 1.6734 Angstrom
      mean = 1.6291 Angstrom
        t1 = 0.036656  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036855  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6130 Angstrom
T2  -- O4  = 1.6055 Angstrom
T2  -- O3  = 1.6130 Angstrom
T2  -- O4  = 1.6055 Angstrom
      mean = 1.6093 Angstrom
        t1 = 0.028746  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019208  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5833 A <--> 1.6734 A
          Mean   = 1.6225 A
          StdDev = 0.0291 A

       t1 Range  = 0.0287 <-- 0.0327 --> 0.0367
       t2 Range  = 0.0192 <-- 0.0280 --> 0.0369

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 106.026 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.682 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 114.916 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 107.789 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 114.212 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 108.601 deg; O4  -- O2  = 3 A
       104.682 deg <-- 109.371 deg --> 114.916 deg

O3  -- T2  -- O4  = 115.099 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 107.453 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 103.936 deg; O3  -- O4  = 3 A
O4  -- T2  -- O3  = 103.936 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 111.609 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  = 115.099 deg; O3  -- O4  = 3 A
       103.936 deg <-- 109.522 deg --> 115.099 deg

        O-T-O SUMMARY
          Range  = 103.9362 deg <--> 115.0988 deg
          Mean   = 109.2086 deg
          StdDev = 4.2778 deg

        O--O SUMMARY
          Range  = 2.5334 A <--> 2.7849 A
          Mean   = 2.6366 A
          StdDev = 0.0833 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 140.264 deg; T2  -- T2  = 5.6885 A
T2  - O1  - T1  - O4  - T1  = 101.668 deg; T2  -- T1  = 4.7441 A
T2  - O1  - T1  - O2  - T1  = 104.118 deg; T2  -- T1  = 4.8471 A
T2  - O3  - T1  - O4  - T1  =  95.292 deg; T2  -- T1  = 4.6811 A
T2  - O3  - T1  - O2  - T1  =  92.353 deg; T2  -- T1  = 4.5897 A
T1  - O4  - T1  - O2  - T1  = 128.520 deg; T1  -- T1  = 5.7895 A

T1  - O3  - T2  - O4  - T1  = 134.414 deg; T1  -- T1  = 5.5764 A
T1  - O3  - T2  - O3  - T1  =  99.158 deg; T1  -- T1  = 4.4371 A
T1  - O3  - T2  - O4  - T1  =  96.163 deg; T1  -- T1  = 4.5027 A
T1  - O4  - T2  - O3  - T1  =  96.163 deg; T1  -- T1  = 4.5027 A
T1  - O4  - T2  - O4  - T1  = 103.009 deg; T1  -- T1  = 4.9055 A
T1  - O3  - T2  - O4  - T1  = 134.414 deg; T1  -- T1  = 5.5764 A

        T-T-T SUMMARY
          Range  = 92.3525 deg <--> 140.2641 deg
          Mean   = 110.7371 deg
          StdDev = 17.8111 deg

        T--T SUMMARY
          Range  = 4.4371 A <--> 5.7895 A
          Mean   = 4.9928 A
          StdDev = 0.5074 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 172.854 deg ; T1  -- T1   3.2270 A

T1  -- O2  -- T1  = 145.960 deg ; T1  -- T1   3.2003 A

T1  -- O3  -- T2  = 127.003 deg ; T1  -- T2   2.9142 A

T1  -- O4  -- T2  = 158.690 deg ; T1  -- T2   3.1339 A


        T-O-T SUMMARY
          Range  = 127.0032° <--> 172.8539 deg
          Mean   = 151.1269 deg
          StdDev = 17.1364 deg

        T--T SUMMARY
          Range  = 2.9142 A <--> 3.2270 A
          Mean   = 3.1188 A
          StdDev = 0.1249 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 492 566 650 744
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 492 566 650 744
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

<TD10> = 1125.000
Average ring size = 6.0000