Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_88-2_2_83106_nu0Ey5.cif"

There are 20 T-atoms per unit cell
There are 40 O-atoms per unit cell

Framework density = 16.57 T-atoms per nm^3
Material density = 1.653 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6155 Angstrom
T1  -- O2  = 1.6217 Angstrom
T1  -- O3  = 1.6197 Angstrom
T1  -- O2  = 1.6218 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006042  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000693  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O3  = 1.6211 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007081  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001640  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6155 A <--> 1.6218 A
          Mean   = 1.6200 A
          StdDev = 0.0024 A

       t1 Range  = 0.0060 <-- 0.0066 --> 0.0071
       t2 Range  = 0.0007 <-- 0.0012 --> 0.0016

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.514 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.544 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.519 deg; O1  -- O2  = 3 A
O2  -- T1  -- O3  = 109.387 deg; O2  -- O3  = 3 A
O2  -- T1  -- O2  = 109.267 deg; O2  -- O2  = 3 A
O3  -- T1  -- O2  = 109.597 deg; O3  -- O2  = 3 A
       109.267 deg <-- 109.471 deg --> 109.597 deg

O3  -- T2  -- O3  = 109.300 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.815 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.300 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.300 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.815 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.300 deg; O3  -- O3  = 3 A
       109.300 deg <-- 109.471 deg --> 109.815 deg

        O-T-O SUMMARY
          Range  = 109.2670 deg <--> 109.8148 deg
          Mean   = 109.4713 deg
          StdDev = 0.1893 deg

        O--O SUMMARY
          Range  = 2.6427 A <--> 2.6529 A
          Mean   = 2.6461 A
          StdDev = 0.0033 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  92.148 deg; T1  -- T2  = 4.3491 A
T1  - O1  - T1  - O3  - T1  = 131.614 deg; T1  -- T1  = 5.6892 A
T1  - O1  - T1  - O2  - T1  =  75.048 deg; T1  -- T1  = 3.6609 A
T2  - O2  - T1  - O3  - T1  = 125.847 deg; T2  -- T1  = 5.5784 A
T2  - O2  - T1  - O2  - T1  =  92.148 deg; T2  -- T1  = 4.3491 A
T1  - O3  - T1  - O2  - T1  = 124.787 deg; T1  -- T1  = 5.5272 A

T1  - O3  - T2  - O3  - T1  = 129.483 deg; T1  -- T1  = 5.4865 A
T1  - O3  - T2  - O3  - T1  =  74.235 deg; T1  -- T1  = 3.6609 A
T1  - O3  - T2  - O3  - T1  = 129.483 deg; T1  -- T1  = 5.4865 A
T1  - O3  - T2  - O3  - T1  = 129.483 deg; T1  -- T1  = 5.4865 A
T1  - O3  - T2  - O3  - T1  =  74.235 deg; T1  -- T1  = 3.6609 A
T1  - O3  - T2  - O3  - T1  = 129.483 deg; T1  -- T1  = 5.4865 A

        T-T-T SUMMARY
          Range  = 74.2349 deg <--> 131.6136 deg
          Mean   = 108.9994 deg
          StdDev = 23.9731 deg

        T--T SUMMARY
          Range  = 3.6609 A <--> 5.6892 A
          Mean   = 4.8685 A
          StdDev = 0.8214 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2310 A

T1  -- O2  -- T1  = 135.798 deg ; T1  -- T1   3.0052 A

T1  -- O3  -- T2  = 138.769 deg ; T1  -- T2   3.0333 A


        T-O-T SUMMARY
          Range  = 135.7978° <--> 180.0000 deg
          Mean   = 151.5221 deg
          StdDev = 20.3869 deg

        T--T SUMMARY
          Range  = 3.0052 A <--> 3.2310 A
          Mean   = 3.0898 A
          StdDev = 0.1016 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 78 106 139 179 213 266 318 366 439 501 553
TD10 = 835
Circuit symbol = 4.8_{2}.4.8_{2}.4_{2}.8_{4}
Weight = 19
Vertex symbol  = 4.8_{2}.4.8_{2}.4_{2}.8_{4}
Weight = 19

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 18 36 56 66 116 140 154 232 264 294 392 432 478 588
TD10 = 831
Circuit symbol = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29
Vertex symbol  = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29

<TD10> = 834.200
Average ring size = 6.1818