Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_88-2_2_64723_WMCy4R.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 24.74 T-atoms per nm^3
Material density = 2.469 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6241 Angstrom
T1  -- O1  = 1.6254 Angstrom
T1  -- O2  = 1.6108 Angstrom
T1  -- O3  = 1.6153 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.012139  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006839  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6241 Angstrom
T2  -- O4  = 1.6260 Angstrom
T2  -- O2  = 1.6109 Angstrom
T2  -- O3  = 1.6171 Angstrom
      mean = 1.6195 Angstrom
        t1 = 0.012574  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007082  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6108 A <--> 1.6260 A
          Mean   = 1.6192 A
          StdDev = 0.0061 A

       t1 Range  = 0.0121 <-- 0.0124 --> 0.0126
       t2 Range  = 0.0068 <-- 0.0070 --> 0.0071

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.531 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.630 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.046 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.411 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.721 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 106.445 deg; O2  -- O3  = 3 A
       106.445 deg <-- 109.464 deg --> 111.046 deg

O4  -- T2  -- O4  = 109.434 deg; O4  -- O4  = 3 A
O4  -- T2  -- O2  = 109.411 deg; O4  -- O2  = 3 A
O4  -- T2  -- O3  = 111.125 deg; O4  -- O3  = 3 A
O4  -- T2  -- O2  = 109.509 deg; O4  -- O2  = 3 A
O4  -- T2  -- O3  = 110.892 deg; O4  -- O3  = 3 A
O2  -- T2  -- O3  = 106.412 deg; O2  -- O3  = 3 A
       106.412 deg <-- 109.464 deg --> 111.125 deg

        O-T-O SUMMARY
          Range  = 106.4123 deg <--> 111.1249 deg
          Mean   = 109.4639 deg
          StdDev = 1.5136 deg

        O--O SUMMARY
          Range  = 2.5840 A <--> 2.6732 A
          Mean   = 2.6438 A
          StdDev = 0.0290 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  83.494 deg; T1  -- T1  = 4.0751 A
T1  - O1  - T1  - O2  - T2  = 138.464 deg; T1  -- T2  = 5.6819 A
T1  - O1  - T1  - O3  - T2  = 113.987 deg; T1  -- T2  = 5.1728 A
T1  - O1  - T1  - O2  - T2  =  94.595 deg; T1  -- T2  = 4.4658 A
T1  - O1  - T1  - O3  - T2  = 116.813 deg; T1  -- T2  = 5.2541 A
T2  - O2  - T1  - O3  - T2  = 103.875 deg; T2  -- T2  = 4.8226 A

T2  - O4  - T2  - O4  - T2  =  83.523 deg; T2  -- T2  = 4.0787 A
T2  - O4  - T2  - O2  - T1  =  94.360 deg; T2  -- T1  = 4.4587 A
T2  - O4  - T2  - O3  - T1  = 116.684 deg; T2  -- T1  = 5.2520 A
T2  - O4  - T2  - O2  - T1  = 138.592 deg; T2  -- T1  = 5.6860 A
T2  - O4  - T2  - O3  - T1  = 114.071 deg; T2  -- T1  = 5.1768 A
T1  - O2  - T2  - O3  - T1  = 103.803 deg; T1  -- T1  = 4.8202 A

        T-T-T SUMMARY
          Range  = 83.4937 deg <--> 138.5920 deg
          Mean   = 108.5216 deg
          StdDev = 17.5732 deg

        T--T SUMMARY
          Range  = 4.0751 A <--> 5.6860 A
          Mean   = 4.9120 A
          StdDev = 0.5320 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.688 deg ; T1  -- T1   3.0601 A

T1  -- O2  -- T2  = 138.895 deg ; T1  -- T2   3.0166 A

T1  -- O3  -- T2  = 148.120 deg ; T1  -- T2   3.1081 A

T2  -- O4  -- T2  = 140.817 deg ; T2  -- T2   3.0620 A


        T-O-T SUMMARY
          Range  = 138.8952° <--> 148.1197 deg
          Mean   = 142.1301 deg
          StdDev = 3.5686 deg

        T--T SUMMARY
          Range  = 3.0166 A <--> 3.1081 A
          Mean   = 3.0617 A
          StdDev = 0.0326 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1088.000
Average ring size = 5.6000