Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_83_2_105_eyTbs5.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 20.63 T-atoms per nm^3
Material density = 2.058 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6207 Angstrom
T1  -- O2  = 1.6183 Angstrom
T1  -- O4  = 1.6215 Angstrom
T1  -- O3  = 1.6216 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.006629  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000975  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6181 Angstrom
T2  -- O3  = 1.6202 Angstrom
T2  -- O4  = 1.6216 Angstrom
T2  -- O5  = 1.6221 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.006727  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001095  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6181 A <--> 1.6221 A
          Mean   = 1.6205 A
          StdDev = 0.0014 A

       t1 Range  = 0.0066 <-- 0.0067 --> 0.0067
       t2 Range  = 0.0010 <-- 0.0010 --> 0.0011

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.233 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.590 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.405 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.439 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.632 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.527 deg; O4  -- O3  = 3 A
       109.233 deg <-- 109.471 deg --> 109.632 deg

O2  -- T2  -- O3  = 109.044 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.575 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.673 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.337 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.580 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.617 deg; O4  -- O5  = 3 A
       109.044 deg <-- 109.471 deg --> 109.673 deg

        O-T-O SUMMARY
          Range  = 109.0437 deg <--> 109.6726 deg
          Mean   = 109.4710 deg
          StdDev = 0.1813 deg

        O--O SUMMARY
          Range  = 2.6370 A <--> 2.6508 A
          Mean   = 2.6463 A
          StdDev = 0.0038 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 111.999 deg; T2  -- T2  = 5.0640 A
T2  - O1  - T1  - O4  - T2  = 123.545 deg; T2  -- T2  = 5.3830 A
T2  - O1  - T1  - O3  - T1  = 109.194 deg; T2  -- T1  = 4.9885 A
T2  - O2  - T1  - O4  - T2  =  91.437 deg; T2  -- T2  = 4.3342 A
T2  - O2  - T1  - O3  - T1  = 109.560 deg; T2  -- T1  = 4.9545 A
T2  - O4  - T1  - O3  - T1  = 109.551 deg; T2  -- T1  = 4.9553 A

T1  - O2  - T2  - O3  - T1  = 129.516 deg; T1  -- T1  = 5.5250 A
T1  - O2  - T2  - O4  - T2  = 109.194 deg; T1  -- T2  = 4.9885 A
T1  - O2  - T2  - O5  - T1  = 118.953 deg; T1  -- T1  = 5.2629 A
T1  - O3  - T2  - O4  - T2  = 109.560 deg; T1  -- T2  = 4.9545 A
T1  - O3  - T2  - O5  - T1  =  75.573 deg; T1  -- T1  = 3.7095 A
T2  - O4  - T2  - O5  - T1  = 109.551 deg; T2  -- T1  = 4.9553 A

        T-T-T SUMMARY
          Range  = 75.5731 deg <--> 129.5158 deg
          Mean   = 108.9693 deg
          StdDev = 13.5106 deg

        T--T SUMMARY
          Range  = 3.7095 A <--> 5.5250 A
          Mean   = 4.9229 A
          StdDev = 0.4626 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.228 deg ; T1  -- T1   3.0383 A

T1  -- O2  -- T2  = 144.432 deg ; T1  -- T2   3.0818 A

T1  -- O3  -- T2  = 138.126 deg ; T1  -- T2   3.0277 A

T1  -- O4  -- T2  = 137.872 deg ; T1  -- T2   3.0264 A

T2  -- O5  -- T2  = 138.963 deg ; T2  -- T2   3.0383 A


        T-O-T SUMMARY
          Range  = 137.8719° <--> 144.4318 deg
          Mean   = 139.7241 deg
          StdDev = 2.4378 deg

        T--T SUMMARY
          Range  = 3.0264 A <--> 3.0818 A
          Mean   = 3.0425 A
          StdDev = 0.0205 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391